Temperature Dependence of Phase and Color Diagram for Ternary (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu Phosphors
GAO Ming-yuan1, LUO Lan1, 2*, GUO Rui1, WANG Yu1, ZHANG Peng-peng1
1. School of Materials Science and Engineering, Nanchang University, Nanchang 330031, China
2. Key Laboratory of Lightweight and High Strength Structural Materials of Jiangxi Province, Nanchang University, Nanchang 330031, China
Abstract：(Mg1-x-yBaxSry)1.95SiO4∶0.05Eu phosphor series samples were prepared by high-temperature solid-state method (at 1 150, 1 200 and 1 250 ℃). By XRD, PL and photograph records under UV lights, the composition- phase-emission light color relationship was established, and the ternary color diagram was then derived. The influence of fabricated temperatures, both on phase constitution and on emission color, was investigated too. Phase analysis showed that (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu powder would gradually change in phase constitution. Starting from Ba2SiO4 corner, the powder is a single phase till to the ones with the composition having maximum Mg2+ or Sr2+ solution. For Sr2SiO4 or Mg2SiO4 corner, there are two phases in the powder. Phase constitution is gradually complicated as Mg2+, Sr2+, Ba2+ contents are almost the same to each other. Furthermore, the higher the fabricated temperature, the larger Ba2SiO4-single-phase region is. At 1 150, 1 200, and 1 250 ℃ the solid solubility of Mg2+(Sr2+) were 20at% (30at%), 30at% (35at%) and 35at% (40at%). For the mixed-phase region, the number of phase components for the same composition is reduced. PL spectral analysis shows that the green emission is strong and red emission is weaker for the same sample under the excitation comparing 365 nm with 254 nm. The emission color and intensity under ultraviolet excitation change also gradually. Ba2SiO4-phase powders are green phosphors, and its emission intensity increases as the Sr2+ and Mg2+ solution. For the mixture region, the powder changes from green to red phosphor as Ba2+ content decreases, and red phosphors’ brightness decreases gradually as Mg2+ content decreases. For example, (Mg1-ySry)1.95SiO4∶0.05Eu series changes from bright red to dark red phosphor as y increases. When the fabrication temperature is increased, the overall brightness of the phosphor in the Ba2SiO4 single-phase region is improved with the Mg2+, Sr2+ content increases in brightest phosphor composition. The increasing of fabrication temperature also makes the emission intensity of the phosphors in mixed phase region increase, and the green phosphor region becomes larger (under 254 nm excitation, the red-green transition point of (Mg1-xBax)1.95SiO4∶0.05Eu is x1 150 ℃=0.5, x1 200 ℃=0.4, x1 250℃=0.3, (Ba1-ySry)1.95SiO4∶0.05Eu is y1 150 ℃=0.6, y1 200 ℃=0.7, y1 250 ℃=0.8, (Bax(Mg0.2Sr0.8)1-x)1.95SiO4∶0.05Eu is x1 150 ℃=0.5, x1 200 ℃=0.4, x1 250 ℃=0.3. The work has a systematic search on the relationship among composition-structure (phase constitution)-fabrication (temperature)-property(luminescence) for (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu powder, and screened out a series of good phosphors, for examples as (Mg0.35Ba0.6Sr0.05)1.95SiO4∶0.05Eu/(Mg0.6Sr0.4)1.95SiO4∶0.05Eu. Single-phase green phosphor is brighter than mixed-phase green phosphor. The solubility increasing can improve Ba2SiO4 single-phase green phosphor intensity. The higher fabricated temperature, the larger single-phase green phosphor region, the larger mixed-phase green phosphor region, and higher luminescent intensity for (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu phosphors. (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu emission light color dependence of the composition and temperature would be applied to other phosphor series, and it can also give a guide for new luminescent material discovering.
高明远，罗 岚，郭 锐，汪 雨，张澎鹏. 制备温度对(Mg1-x-yBaxSry)1.95SiO4∶0.05Eu 荧光粉三元相图及色像图的影响研究[J]. 光谱学与光谱分析, 2021, 41(02): 460-466.
GAO Ming-yuan, LUO Lan, GUO Rui, WANG Yu, ZHANG Peng-peng. Temperature Dependence of Phase and Color Diagram for Ternary (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu Phosphors. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(02): 460-466.
[1] PAN Zheng-wei, HE Hong, SONG Xiu-feng, et al(潘政薇, 何 洪, 宋秀峰, 等). Journal of the Chinese Ceramic Society(硅酸盐学报), 2009, 37(9): 1590.
[2] Denault K A, Brgoch J, Gaultois M W, et al. Chem. Mater., 2014, 26(7): 2275.
[3] WANG Yu, LUO Lan, GUO Rui, et al(汪 雨, 罗 岚, 郭 锐, 等). Chinese Journal of Luminescence(发光学报), 2019, 40(9): 1086.
[4] Wang Yu, Luo Lan, Guo Rui, et al. Materials Research Express, 2019, 6(11): 116201.
[5] GAO Ming-yuan, LUO Lan, WANG Yu, et al(高明远, 罗 岚, 汪 雨, 等). Journal of the Chinese Ceramic Society(硅酸盐学报), 2020, 48(2): 204.
[6] Cruz R T D, Saulo R Braganca. Ceramics International, 2015, 41(3): 4775.
[7] Fei M, Tian Y F, Zhang Z, et al. Journal of Alloys and Compounds, 2017, 728, 231.
[8] Cao Hong, Liu Miao, Chen Hang. Physica B: Condensed Matter, 2019, 571, 243.
[9] JIANG Hong-yi, HU Dan, JI Tong-kun(姜洪义, 胡 丹, 姬同坤). Journal of the Chinese Ceramic Society(硅酸盐学报), 2010，(3): 446.
[10] CHEN Yong-jie, LI Lang-kai, XIAO Lin-jiu, et al(陈永杰, 李郎楷, 肖林久, 等). Journal of the Chinese Ceramic Society(硅酸盐学报), 2011，(6): 908.
[11] LI Xiang-qi, ZHANG Yi(李湘祁, 张 懿). Chinese Journal of Luminescence(发光学报), 2014, 35(6): 643.
[12] Ashbrook S E, Berry A J, Hibberson W O, et al. American Mineralogist, 2005, 90(11-12): 1861.
[13] Li J, Deng J C, Lu Q F, et al. Optoelectronics Letters, 2013, 9(4): 293.
[14] Park C H, Hong S T, Keszler D A. Journal of Solid State Chemistry, 2009, 182(3): 496.
[15] Nag A, Kutty T R N. Journal of Materials Chemistry, 2004, 14(10): 1598.
[16] Li X J, Hua Y J, Ma H P, et al. RSC Advances, 2015, 5(77): 62659.
[17] Fields J M, Dear P S, Brown J J. Journal of the American Ceramic Society，1972, 55(12): 585.