Effect of the Cu+ Concentration on the Curve of Thermoluminescence of ZnS:Cu Electroluminescent Material |
LI Zhi-qiang, TIAN Shao-hua, SONG Wei-peng, WEI Zhi-ren, DOU Jun-hong, LI Juan |
Physics Science and Technology College, Hebei University, Baoding 071002, China |
|
|
Abstract In the paper, five ZnS∶Cu electroluminescent material specimens were prepared by adding 0.05%, 0.10%, 0.15%, 0.20% and 0.25% Cu+ to ZnS. From the sample’s thermoluminescence curve and luminance, the authors can see that with the variation of Cu+ concentration, the peak of thermoluminescence curve changed correspondingly. At first with the increase of Cu+ concentration, the peak of thermoluminescence curve rised gradually. When the Cu+ concentration was 0.05%, the peak of thermoluminescence curve was 124.15 which attainded max, when the Cu+ concentration was 0.25%, the peak of the curve of thermoluminesence forther decreased to 51. But the temperature corresponding to the peak of the curves of thermoluminesence didn’t change, which means that the depth of electron trap did not vary. The authors therefore conclude that excessive Cu+ results in a decline of luminance because the energy of trapped electrons turns into the transition without radiation, though the probability of trapping electrons increases and the life of photoelectrons shortens as the luminescence center increases. In this way, there is an optimal value for Cu+ concentration, which leads to the peak of the curves of thermoluminesence and the maximum of luminance.
|
Received: 2004-05-21
Accepted: 2004-08-16
|
|
Corresponding Authors:
LI Zhi-qiang
|
|
Cite this article: |
LI Zhi-qiang,TIAN Shao-hua,SONG Wei-peng, et al. Effect of the Cu+ Concentration on the Curve of Thermoluminescence of ZnS:Cu Electroluminescent Material [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(10): 1730-1732.
|
|
|
|
URL: |
https://www.gpxygpfx.com/EN/Y2005/V25/I10/1730 |
[1] ZHU Ning, MENG Xian-yu, SHI Pan(朱 宁,孟宪域,石 磐). Chinese Journal of Luminescence(发光学报), 2000, 21(2): 159. [2] XIONG Guang-nan, LOU Su-yun, LI Lan, et al(熊光楠,娄素云,李 岚, 等). Journal of Tianjin Institute of Technology(天津理工学院学报), 1998,14(3): 1. [3] LIU Bo, SHI Chao-shu, ZHANG Qing-li, et al(刘 波,施朝淑,张庆礼, 等). Chinese Journal of Luminescence(发光学报), 2002,23(4): 396. [4] Romeo N, et al. Thin. Solid. Films, 1999, 348: 49. [5] ZHAO Hui, et al(赵 辉, 等). Acta Physica Sinica(物理学报), 2000, 49(5): 954. [6] ZHAO Li-juan, et al(赵丽娟, 等). Acta Physica Sinica(物理学报), 1999, 48(7): 1381. [7] LOU Zhi-dong, et al(娄志东, 等). Chinese Science Bulletin(科学通报), 1998, 43(11): 1210. [8] Dimitrova V, et al. Thin Solid Films, 2000, 365: 134. [9] Mueller G O, et al. J. Lumin., 1997, 72-74: 1002. [10] DONG Guo-yi, LI Xiao-wei, WEI Zhi-ren, et al(董国义,李晓苇,韦志仁, 等). Acta Physica Sinica(物理学报), 2003, 52(3): 745. [11] WEI Zhi-ren, LI Zhi-qiang, DONG Guo-yi, et al(韦志仁,李志强,董国义,等). Chinese Journal of Luminescence(发光学报), 1997,18(4): 283. [12] MEI Zeng-xia, ZHANG Xi-qing, YAO Zhi-gang, HAN Jian-min, LI Jia-ze(梅增霞, 张希清, 姚志刚, 韩建民, 李家泽). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2001, 21(6): 766. [13] ZHONG Guo-zhu, Bryant F J(钟国柱, Bryant F J). Luminescence and Display Devices(发光与显示), 1983, (3): 9. [14] Onodera Chikara, Taguchi Tsunemasa. Japanese Journal of Applied Physics, 2000, 39(4): 1782. [15] Heine J R, Bawendi M G, Jensen K F, et al. Journal of Crystal Grownth, 1998, 195(1): 564. [16] Murase N, Kanematsu Y, Kawasaki Y, et al. J. Lumin., 2000, 87(9): 488. [17] Konishi M, Senna M, Isobe T. J. Lumin., 2000, 93(1): 1. [18] GUO Chang-xin, LI Bi-lin(郭常新,李碧琳). Chin. J. Lumin.(发光学报), 2001, 22(3): 223. [19] ZHANG Jian, GUO Yong(张 建,郭 勇). Bulletin of Academy of Military Medical Sciences(军事医学科学院院刊), 1994, 18(3): 172.
|
[1] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
[2] |
YANG Jian1, 2, ZHAO Su-ling1, 2*, SONG Dan-dan1, 2, XU Zheng1, 2, QIAO Bo1, 2, WANG Peng1, 2, WEI Peng1, 2. Highly Efficient Solution Processed Blue Thermally Activated Delayed Fluorescent Organic Light-Emitting Devices with a Mixed Hole Injection Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1028-1033. |
[3] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
[4] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
[5] |
HUANG Huan-huan, WANG Qian*, WU Li, LI Meng-xiao. The Luminescence Characteristics of Alumina Ceramic Powder by the Low Temperature Combustion Synthesis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(09): 2676-2680. |
[6] |
CHEN Yi-xiang, ZHAO Su-ling*, XU Zheng, ZHANG Cheng-wen, XU Xu-rong. The Establishment and the Application of the Electroluminescence Decay Measurement System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 1993-1996. |
[7] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
[8] |
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763. |
[9] |
YANG Zhao-kun, ZHAO Su-ling*, XU Zheng*, HUANG Qing-yu . The Inside Charge Behavior of Organic Light-Emitting Diodes Investigated with Transient Electroluminescent Measurements[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3134-3137. |
[10] |
SONG Ling-yun1, CAI Chun-feng1, LIU Bo-zhi1, HU Lian1, ZHANG Bing-po1, WU Jian-zhong2*, BI Gang2, WU Hui-zhen1*. Influence of Parameters of ZnS Film on the Organic/Inorganic Composite Luminescence Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(04): 898-902. |
[11] |
DAI Shuang, YU Tong-jun*, LI Xing-bin, YUAN Gang-cheng, LU Hui-min . The Electroluminescence Spectra of InGaN/GaN Blue LEDs During Aging Time [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 327-330. |
[12] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326. |
[13] |
YANG Yi-fan, ZHAO Su-ling*, GAO Song . Tunneling Electroluminescence of the ZnO Nanorods/MEH-PPV Heterojunction Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2895-2899. |
[14] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Properties of Phosphorescent Organic Light-Emitting Diodes with Different Doping Order on Light Emitting Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1763-1766. |
[15] |
MA Zhu1, YU Jun-sheng1*, JIANG Long-feng1, DONG Shou-cheng2, LI Zhen2*, HU Song3 . Spectra Characteristics and Electroluminescence Performance of Novel Fluorene Derivatives with Aggregation Fluorescence Enhancement[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(04): 935-939. |
|
|
|
|