Differentiated Fluorescence Centers in Europium Acetylacetonate Hydrate Doped Poly Methyl Methacrylate |
ZHANG Yang-yang1, ZHONG Hua2, CHEN Bao-jiu2, XIA Ying1, LIN Hai1* |
1. School of Textile and Material Engineering, Dalian Polytechnic University, Dalian 116034, China 2. Department of Physics, Dalian Maritime University, Dalian 116026, China |
|
|
Abstract Poly methyl methacrylate (PMMA) was doped with europium acetylacetonate hydrate. Judd-Ofelt parameters Ω2 (19.73×10-20 cm2) and Ω4 (2.19×10-20 cm2) indicate a high inversion asymmetry and strong covalent environment around Eu3+ in PMMA. The maximum stimulated emission cross-sections for the 5D0→7FJ(J=1, 2 and 4) transitions in EAH doped PMMA were calculated to be 0.38×10-21, 4.90×10-21 and 0.36×10-21 cm2, respectively. Efficient purplish-red and red fluorescence was obtained from europium acetylacetonate hydrate doped PMMA under 365 and 254 nm excitation respectively, indicating that it can be used as UV sensitive components for fiber optic sensors. Because of the suitable refractive index difference between doped sample and pure PMMA, it is expected to fabricate standard 9 μm/125 μm optical fiber which supports multi-mode transmission, providing basis of further development for medical fiber, flexible communication fiber and fiber optic sensor.
|
Received: 2013-07-29
Accepted: 2013-10-30
|
|
Corresponding Authors:
LIN Hai
E-mail: wjs@dlpu.edu.cn
|
|
[1] HE Bing, LOU Qi-hong, ZHOU Jun, et al(何 兵,楼祺洪,周 军,等). Acta Optica Sinica(光学学报),2006, 26(8):1279. [2] Guo L, Yan B, Liu J L, et al. Dalton Trans., 2011, 40: 632. [3] Bonzanini R, Girotto E M, Goncalves M C, et al. Polymer, 2005, 46: 253. [4] Parra D F, Mucciolo A, Brito H F, et al. J. Solid State Chem., 2003, 171: 412. [5] Molina C, Dahmouche K, Messaddep Y, et al. J. Lumin., 2003, 104: 93. [6] Liang H, Zhang Q J, Zheng Z Q, et al. Opt. Lett., 2004, 29(5): 447. [7] Li Y, Wei C, Wang X, et al. Photochem. Photobiol., 2011, 87: 618. [8] Wang W, Song H W, Bai X, et al. Phys. Chem. Chem. Phys., 2011, 13: 18023. [9] Li Z J, Zhang H W, Shen J S. J. Appl. Polym. Sci., doi: 10.1002/app.38223. [10] Zhang J L, Chen B W, Luo X, et al. Chinese Chem. Lett., 2012, 23:945. [11] Liu H G, Feng X S, Jang K W, et al. J. Lumin., 2007, 127: 307. [12] Zhang H X, Kam C H, Zhou Y, et al. Appl. Phys. Lett., 2000, 77: 609. [13] Yang Y S, Gong M J, Li Y Y, et al. J. Alloy. Compd.,1994, 207/208:112. [14] Huang L B, Cheng L H, Yu H Q, et al. Opt. Commun., 2012, 285: 1476. [15] TAO Dong-liang, LI Hui-zhen, CUI Yu-min, et al(陶栋梁,李慧珍,崔玉民,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2012, 32(9): 2473. [16] Dejneka M, Snitzer E, Riman R E. J. Lumin.,1995, 65:227. [17] Wang Y H, Li B, Zhang L M, et al. Chem. Phys. Chem., 2011, 12(2): 349. [18] Jiang H, Pan X J, Lei Z Y, et al. Chem. Phys. Lett., 2010, 500: 100. |
|
|
|