| Color-Tunable Nano-Material α-NaYF4：Yb, Er, Tm Prepared by Microemulsion-Hydrothermal Method |
| LONG Dan-dan1, ZHANG Qing-xia1, WANG Yu3, ZHANG Fan2, WANG Yan-fei2, ZHOU Xin2, QI Xiao-hua2, ZHANG Heng1, YAN Jing-hui1*, ZOU Ming-qiang2* |
1. School of Chemical and Environmental Engineering, Changchun University of Science and Technology, Changchun 130022, China
2. Chinese Academy of Inspection and Quarantine, Beijing 100123, China
3. China National Accreditation Service of Conformity Assessment, Beijing 100062, China |
|
|
|
|
Abstract NaYF4：Yb3+, Er3+, Tm3+ nanoparticles were prepared by microemulsion-hydrothermal method. Crystal phase, morphology and structure of the samples were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The luminescence properties were studied by up-conversional fluorescence spectroscopy. The XRD patterns of as-prepared samples were in agreement with the PDF #77-2042 of cubic NaYF4. SEM images of the particles showed that the samples were cotton-like spherical in shape and which were assembled by smaller nano-particles. The average size was 120 nm, while the shape was regular and the particle size was homogeneous. Under the excitation of 980 nm, the as-prepared particles could emit blue (438 and 486 nm), green (523 and 539 nm) and red (650 nm) light simultaneously. It can be seen from the color coordinates figure (CIE) that when doping concentration ratio of Tm3+ and Er3+ increased from 0 to 2, the whole emitting light color of samples movedto green region. While the ratio was 1：1, pseudo white light was obtained. As the ratio changed from 2 to 7, the luminous color was moved to red region.
|
|
Received: 2013-01-08
Accepted: 2013-04-08
|
|
|
|
Corresponding Authors:
YAN Jing-hui, ZOU Ming-qiang
E-mail: yanjinghui8888@yahoo.com.cn;mingqiangz@sina.com
|
|
[1] Tropper A C, Carter J N, Lader R D T. J. Opt. Soc. Am., 1994, B11: 886.
[2] JIA Ruo-kun, YANG Shan, LI Cui-xia, et al(贾若琨, 杨 珊, 李翠霞，等). Acta Chim. Sinica(化学学报), 2008, 66, 2439.
[3] Wright J C, Zalucha D J, Lauer H V, et al. Journal of Applied Physics, 1973, 44 (2): 781.
[4] Auzel F. Chem. Rev., 2004, 104(1): 139.
[5] Yi G S, Lu H C, Zhao S Y, et al. Nano Lett., 2004, 4 (11): 2191.
[6] van de Rijke F, Zijlmans H, Li S, et al. Biotechnol, 2001, 19(3): 273.
[7] Lim S F, Riehn R, Ryu W S, et al. Nano Lett., 2006, 6(2): 169.
[8] Wang L Y, Li Y D. Chem. Commun., 2006, 24: 2557.
[9] Downing E, Hesselink L, Ralston J, et al. Science, 1996, 273(5279): 1185.
[10] Sivakumar S, van Veggel F C J M, Raudsepp M. J. Am. Chem. Soc., 2005, 127(36): 12464.
[11] Yi G S, Lu HC, Zhao S Y, et al. Nano Lett., 2004, 4(11): 2191.
[12] SONG Qiu-sheng, GAO Kang, YAO Wei, et al(宋秋生, 高 康, 姚 伟，等). Acta Chim. Sinica(化学学报), 2012, 70: 2155.
[13] Park Y, Kim J H, Lee K T, et al. Adv. Mater, 2009, 21(44): 4467.
[14] Liu X M, Kong X G, Zhang Y L, et al. Chem. Comm., 2011, 47(43): 11957.
[15] Wang F, Liu X. J. Am. Chem. Soc., 2008, 130(17): 5642.
[16] Wang L, Li Y. Chem. Mater., 2007, 19(4): 727.
[17] Yang Z C, Huang S H, Lu S Z, et al. J. Non-Cryst. Solids, 2004, 343(3): 154.
[18] Tian Q, Tao K, Li W W, et al. J. Phys. Chem. C., 2011, 115(46): 22886.
[19] Boyer J C, Manseau M Q, Murray J I, et al. Langmuir, 2010, 26(2): 1157.
[20] Menyuk N, Dwight K, Pinaud F. Appl. Phys. Lett., 1972, 21(4): 159.
[21] Sommerdijk J L, Bril A. J. Lumin., 1974, 8(4): 341.
[22] Zijlmans H J M A, Bonnet J, Burton J, et al. Biochem., 1999, 267(1): 30.
[23] Feijo J A, Moreno N. Protoplasma, 2004, 223(1): 1.
[24] Waynant R W, Ilev I K, Gannot I Philos. Trans. R. Soc., 2001, 359(1780): 635.
[25] Menyuk N, Dwight K, Pinaud F, Appl. Phys. Lett., 1972, 21(4): 159.
[26] Kim J S, Park Y H, Choi J C, et al. Journal of the Electrochemical Society, 2005, 152(9): H135.
[27] Liang L F, Wu H, Hu H L, et al. Alloy. Compd., 2004, 368(1-2): 94.
[28] LI Yue, ZHAI Hai-qing, YANG Kui-sheng, et al(李 越, 翟海清, 杨魁胜，等). Chin. J. Lumi.n(发光学报), 2009, 30(2): 239.
[29] TIAN Xue-ying, LIU Juan, LI Xi-lin, et al(田雪英, 刘 娟, 李西林，等). Acta Optica Sinica(光学学报), 2011, 11(31): 1116004(1-4).
[30] CAO Liang-jun, TIAN Xue-ying, LIU Wei, et al(曹亮军, 田雪英, 刘 伟，等). J. Infrared Millim. Waves(红外与毫米波学报), 2011, 6(30): 518.
[31] YAN Jing-hui, SONG Li-hong, LI Zhong-tian, et al(闫景辉, 宋丽红, 李中田，等). Chinese Journal of Inorganic Chemistry(无机化学学报), 2007, 23(8): 1432.
[32] Wang M, Mi C C, Zhang Y X, et al. J. Phys. Chem. C, 2009, 113(44): 19021.
[33] Wang S, Deng R P, Guo H L, et al. Dalton Trans., 2010, 39(38): 9153. |
| [1] |
FU Zhen-xing1, LIU Bi-rui1, YANG Bing-xiong2 . Spectroscopic Properties of Energy Transfer Effect in Sm3+/Eu3+ Doped LaF3 Nanocrystals [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(08): 2686-2691. |
| [2] |
XU Jing1, YAN Jing-hui1, HAN Yu-ting1, QIAO Shu-liang3, YANG Bo1, LI Li2, LIU Cai-hong2, YAO Shuang1*, ZOU Ming-qiang2*. The Synthesis, Luminescence and Energy Transmission of NaLa(MoO4)2∶Eu3+/Tb3+/Tm3+ Materials[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(10): 2712-2717. |
| [3] |
LI Yu-bao, WEN Xiao-ling, XUE Jun-fa, OUYANG Jian-ming* . Components of Urinary Nanocrystals and Their Influence on Formation of Calcium Oxalate Stones [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(08): 2257-2262. |
| [4] |
ZHANG Qing-xia1, LONG Dan-dan1, ZHANG Fan2, QI Xiao-hua2, ZHANG Heng1, YAN Jing-hui1*, ZOU Ming-qiang2*. Influence of Bi3+ Doping on Properties of CaMoO4：Eu3+ Phosphors[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1758-1762. |
| [5] |
FU Zhen-xing1, 2, ZHENG Hai-rong1*, LIU Bi-rui2 . Spectroscopic Study on the Energy Transfer Effect in Sm3+/Eu3+ Codoped Tetragonal LaOF Nanocrystals System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(08): 2183-2186. |
| [6] |
HUANG Zhi-jie, LI Jun-jun, HE Jie-yu, OUYANG Jian-ming* . Study on Nano- and Microcrystallites in the Urines of Calcium Oxalate Stone Formers [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(07): 1913-1917. |
| [7] |
MENG Qing-yu1, 2，CHEN Bao-jiu3，Lü Shu-chen1，SUN Jiang-ting1，QU Xiu-rong1 . The Enhancement of 1.5 μm Near Infrared Luminescence in Er3+ and Yb3+ Codoped Y2O3 Nanocrystalline [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(05): 1224-1228. |
| [8] |
GUO Fu-quan1, 4, SUN Xiao-lao1,XIONG Fei1, GUO Bin2, LIANG Hao3, CHEN Biao4, ZHANG Qi-jin4 . Synthesis and Spectral Properties of Stilbene Derivatives as Two-Photon Absorption Materials [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(09): 2462-2466. |
| [9] |
MENG Qing-yu1,2,CHEN Bao-jiu3*,XU Wu4,ZHAO Xiao-xia2,YANG Yan-min2,DI Wei-hua2,WANG Xiao-jun2 . Study on Concentration Quenching and Energy Transfer in Ln3+ (Ln=Tb, Tm, Eu) in Y2O3 Nanocrystal Powders [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(01): 151-155. |
| [10] |
XU Hui,JIN Run-zhi,WU Chun-yang,YANG Yu*,QIAN Guo-dong. Two-Photon Up-Conversion Fluorescence of a Neodymium Organic Framework Nd(BTC)[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(08): 1734-1736. |
| [11] |
YUAN Qiu-li1,ZHAO Jin-tao1,NIE Qiu-lin1,2. Hydrothermal Synthesis and Luminescence of One-Dimensional Mn2+-Doped CdS Nanocrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(06): 1058-1061. |
| [12] |
SUN Ping, XIONG Bo, ZHANG Guo-qing, ZHU Bai-jin, DING Feng-lian. Spectral Analysis of ZnO Nanocrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(01): 143-146. |
| [13] |
SHI Qin-fen1, WANG Xiao-mei1*, JIANG Wan-li3, YANG Ping2, JIANG Xue-zhang1, WEN Di-jiang1,XU Gui-bao３ . Study on Two-Photon Induced Fluorescence of Newly Synthesized Chromophore BECVN and BMABN[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(12): 1925-1928. |
|
|
|
|