| 光谱学与光谱分析 |
|
|
|
|
|
| Preparation and Luminescent Properties of ZnMoO4∶Tb3+ |
| Namila1, 2, WANG Fu-ming1*, WANG Xi-gui2, Aolegen3 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
2. College of Chemistry and Environment Science, Inner Mongolia Normal University, Huhhot 010022, China
3. Inner Mongolia Ling Yi (Group) Information Technology Co., Ltd., Huhhot 010010, China |
|
|
|
|
Abstract Tb3+ doped ZnMoO4 materials were synthesized by combustion method. XRD results show that the samples completely formed single ZnMoO4 phase at 700 ℃ which belongs to Trigonal, while the incorporation of Tb3+ does not affect the basic structure of ZnMoO4. The TG-DTA results show that the samples fully formed ZnMoO4 phase due to the energy absorption at about 680 ℃. IR results show that there were no other organic peaks after burning at 700 ℃, indicating that citric acid has been completely decomposed and Tb3+ ions have been fully integrated into the lattice of ZnMoO4. SEM results show that the dispersion of particles gradually increases along with the improvement of the temperature.The best excitation wavelength was 488 nm when the monitoring wavelength was 544 nm, which corresponds to the 5D4→7F5 transition of Tb3+. Finally, a valuable green fluorescent powder of ZnMoO4∶Tb3+ has been obtained.
|
|
Received: 2012-03-30
Accepted: 2012-07-30
|
|
|
|
Corresponding Authors:
WANG Fu-ming
E-mail: wangfuming@metall.ustb.edu.cn
|
|
[1] Haque M M, Kim D K. Materials Letters, 2009, 63: 793.
[2] Mohitkar S A, Kalpana G, Vidyasagar K. Journal of Solid State Chemistry, 2011, 184(4): 735.
[3] Kang Fengwen, HU Yihua, WU Haoyi, et al. Journal of Rare Earths, 2011, 29(9): 837.
[4] YANG Yu-ling, LI Xue-ming, FENG Wen-lin, et al(杨玉玲，黎学明，冯文林, 等). Chinese Journal of Inorganic Chemistry(无机化学学报), 2011 27(2): 276.
[5] Enrico Cavalli, Philippe Boutinaud, Rachid Mahiou, et al. Inorganic Chemistry, 2010, 49: 4916.
[6] XU Cheng-ke, QIU Gui-ming, HUANG Chong(许成科，邱桂明，黄 翀). Optoelectronic Technology(光电子技术), 2010, 30(1): 37.
[7] QIU Gui-ming, XU Cheng-ke, YANG Ying-quan(邱桂明，许成科，杨英权). Optoelectronic Technology(光电子技术), 2011, 31(2): 125.
[8] Li Guangzhi, Wang Zhenling, Quan Zewei, et al. Crystal Growth and Design, 2007, 7(9 ): 1797.
[9] CHENG Li-hong, ZHONG Hai-yang, SUN Jia-shi, et al(程丽红，仲海洋，孙佳石, 等). Chinese Journal of Luminescence(发光学报), 2011, 32(12): 1238.
[10] Zhang Zhijun, Chen Haohong, Yang Xinxin, et al. Materials Science and Engineering B, 2007, 145: 34.
[11] GUAN Li, ZUO Jin-gai, LIU Chong, et al(关 丽，左金改，刘 冲, 等). Chinese Journal of Luminescence(发光学报), 2011, 32(8): 779.
[12] Ju Xiaoxia, Li Xueming, Li Wulin, et al. Materials Letters, 2011, 65: 2642.
[13] Hou Zhiyao, Chai Ruitao, Zhang Milin, et al. Langmuir, 2009, 25(20): 12340.
[14] Zhang Kong, Liu Qian, Su Xiaobin, et al. Acta Physico-Chimica Sinica, 2011, 27 (8): 2001.
[15] Lakshminarasimhan N, Varadaraju U V. Journal of Solid State Chemistry, 2008, 181: 2418.
[16] Lü Jian-tao, WANG Ke-jia, LIU Jin-song, et al(吕健滔，王可嘉，刘劲松, 等). Acta Optica Sinica(光学学报), 2012, 31(2): 0216006.
[17] LI Jun-fu, QIU Ke-hui, ZHAO Jie, et al(李钧甫，邱克辉，赵 洁, 等). Materials Review(材料导报), 2010, 24(1): 19.
[18] GAO Fei, LIANG Li-fang, GUO Chong-feng(高 飞，梁利芳，郭崇峰). Chinese Journal of Luminescence(发光学报), 2009, 30(5): 610.
[19] HUANG Pei-shuai, WEI Jian-she, ZHOU Li-ya(黄培帅，魏建设，周立亚). Technology & Development of Chemical Industry(化工技术与开发), 2009, 38(4): 1.
[20] ZHOU Li-ya, WANG Lei, WEI Jian-she, et al(周立亚，王 雷，魏建设, 等). Chemical Research and Application(化学研究与应用), 2008, 20(8): 952.
[21] LEI Zhi-yi, ZHU Liang, LI Feng(雷志轶，朱 亮，李 峰). Industrial Catalysis(工业催化), 2008, 16(10): 659.
[22] Tomaszewicz E, Dabrowska G, Kaczmarek S M, et al. Journal of Non-Crystalline Solids, 2010, 356: 2059.
[23] XIE Ye, WANG Hai-bo, ZHANG Rui-xi, et al(谢 晔，王海波，张瑞西, 等). New Chemical Materials(化工新型材料), 2011, 39(8): 78.
[24] SUN Jia-yue, DU Hai-yan, HU Wen-xiang(孙家跃，杜海燕，胡文祥). Solid Luminescent materials(固体发光材料). Beijing: Chemical Industry Press(北京: 化学工业出版社), 2003.
[25] YANG Ding-ming, WANG Qing-long, JI Hong-xin, et al(杨定明，王擎龙，吉红新, 等). Journal of Sichuan University·Engineering Science Edition(四川大学学报·工程科学版), 2012, 44(1): 173.
|
| [1] |
LIU Xiao-zhen1, ZHANG Cheng1, CHEN Jie2, SHEN Qin-wei1, GUO Ling-ling1, XIE Guang1 . Preparation of La2Zr2O7 Powder with Combustion Method and Its Spectral Properties [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(12): 4063-4066. |
| [2] |
FENG Ying, TONG Yi-ping*, LI Wen-wei . A Study on Synthesis of CaAl12O19∶xMn4+ Red Phosphor with Combustion Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3211-3214. |
| [3] |
WANG Xi-gui, BO Su-ling, NA Mi-la, QI Xia. Preparation and Luminescent Properties of CaMoO4∶Tb3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(01): 22-25. |
| [4] |
Namila1, 2,WANG Xi-gui2,ZHENG Xue-fang1*,AO Cui-hua2,KANG Yi-you2 . Preparation and Luminescence Properties of EuVO4[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(04): 887-890. |
| [5] |
SHA Ren, WANG Xi-gui, WU Hong-ying, LI Xia. Synthesis of CaLaAl3O7∶Eu3+ by Gel-Combustion Method and Its Luminescence Properties[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(12): 2781-2784. |
| [6] |
CHI Yu-xian1,NIU Shu-yun1*,JIN Jing1,YANG Guang-di2,YE Ling2. Crystal Structures and Luminescence Property of d10 Transition Metal Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(10): 2258-2262. |
| [7] |
ZHAI Yong-qing,YANG Guo-zhong,LIU Yu,LIU Hong-mei. Synthesis and Luminescent Properties of Novel Red Phosphor SrO·Y2O3∶Eu[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(03): 522-526. |
| [8] |
WANG Xi-gui1,LI Xia1,2. Preparation and Luminescence Properties of Tb3+ Ion and Na2WO4 Co-Doped SiO2 Materials[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(02): 260-264. |
| [9] |
CHEN Zhe,XIE Hong,YAN You-wei*. Influence of Eu2+ Content on the Spectral Characteristics of BaMgAl10O17∶Eu2+ Phosphors[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(04): 657-659. |
| [10] |
PENG Zhi-wei,WANG Ling-ling*,LIU Huang-qing, LI Hong-jian, ZOU Bing-suo, YANG Guang, ZHANG Jie . Preparation and Luminescence Properties of Nanocrystals Gd2O3∶Eu3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(03): 427-431. |
| [11] |
WANG Xi-gui1, WU Hong-ying1, ZHAO Si-qin1, WENG Shi-fu2, WU Jin-guang2 . Structure and Luminescence Properties of Eu3+ Complexes with Benzoic Acid and 1,10-Phenanthroline Incorporated in SiO2,SiO2-B2O3 and SiO2-B2O3-Na2O Matrices [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(05): 805-808. |
| [12] |
CHANG Jian-jun1, HUANG Shi-hua1，PENG Hong-shang1, MENG Chun-xia1, YOU Fang-tian1, Lü Shao-zhe2, SUN Ling-dong3. Spectrum and Synthesis of Rare Earth Activated Nanoparticle[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(02): 231-234. |
| [13] |
WANG Xi-gui1，WU Hong-ying1，WENG Shi-fu2，WU Jin-guang2 . Synthesis and Luminescence Properties of Europium(Ⅲ) Complexes with Camphoric Acid and 1,10-Phenanthroline [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(07): 799-802. |
| [14] |
WANG Xi-gui1，WU Hong-ying1，YAO Guang-qing2，WENG Shi-fu2，WU Jin-guang2 . Study on the Transition of Green，Yellow Fluorescence of Ternary Complexes of Tb-Benzoic Acid-1,10-Phenanthroline [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(06): 708-712. |
|
|
|
|