Mid-Infrared Emission Properties of Ho3+/Tm3+-Codoped Ge-Ga-S-CsI Glasses |
ZHU Jun, DAI Shi-xun*, WU Li-gang, ZHANG Wei, SHEN Xiang, WANG Xun-si, XU Tie-feng, NIE Qiu-hua |
College of Information Science and Engineering, Ningbo University, Ningbo 315211, China |
|
|
Abstract A serial of chalcogenide glasses based on 78GeS2-12Ga2S3-10CsI (in molar%) system doped with the different radios of Ho3+/Tm3+ ions were synthesized by melt-quenching method. Their absorption spectra and mid-infrared fluorescence under 808 nm laser excitation were measured. According to Judd-Ofelt theory, the intensity parameters Ωi(i=2, 4, 6), spontaneous transition probabilities Arad and radiative lifetomes τr for Ho3+ ion were calculated. Absorption cross-sections σa, emission cross-sections σe and gain coefficient G(λ) corresponding to the emission of Ho3+ ions at 2.0 μm were obtained. By changing the Tm3+ concentration, the energy transfer regime of Tm3+ and Ho3+ ions under 808 nm excitation was investigated. The results show that Ho3+/Tm3+-codoped Ge-Ga-S-CsI glasses would be a potential material for 2.0 μm emission.
|
Received: 2010-09-15
Accepted: 2010-12-30
|
|
Corresponding Authors:
DAI Shi-xun
E-mail: daishixun@nbu1.edu.cn
|
|
[1] Song J H, Heo J, Park S H. Appl. Phys., 2003, 93(12): 9441. [2] Peng B, Izumitani T. Op. Mater., 1995, 4(6): 797. [3] Yamauchi H, Murugan G S, Ohishib Y. J. Appl. Phys., 2004, 96(12): 7212. [4] Richards B, Jha A, Tsang Y, et al. Laser Phys. Lett., 2010, 7(3): 177. [5] Mazzera M, Baraldi A, Capelletti R, et al. Opt. Mater., 2009, 31(9): 1366. [6] Oprea I I, Hesse H, Betzler K. Opt. Mater., 2006, 28(3): 1136. [7] Peng B, Fan Z C, Qiu X M, et al. Adv. Mater., 2005, 17(7): 857. [8] Jackson S D. Opt. Lett., 2009, 34(15): 2327. [9] Ghishler C, Luthy W, Weber H P. IEEE J. Quantum Electron.,1995, 31(11): 1877. [10] ZHANG Peng-jun, DAI Shi-xun, LE Fang-da, et al(张鹏君,戴世勋,乐放达,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2010, 30(6): 1464. [11] Lee T H, Heo J. Phys. Rev. B: Condens. Matter,2006, 73(14): 144201.1. [12] Judd B R. Phys. Rev., 1962, 127(3): 750. [13] Ofelt G S. J. Chem. Phys., 1962, 37(3): 511. [14] Weber M J, Matsinger B H, Donlan V L, et al. J. Chem. Phys., 1972, 57(1): 562. [15] Rukmini E, Jayasankar C K. Opt. Mater., 1995, 4(4): 529. [16] Jacinto C, Vermelho M V D, Araujo M T, et al. Opt. Express, 2007, 15(15): 9232. [17] McCumber D E. Phys. Rev., 1964, 134(2A): A299. [18] Shin Y B, Lim H T, Choi Y G, et al. Am. Ceram. Soc., 2000, 83(4): 787.
|
[1] |
ZHANG Peng-jun1, DAI Shi-xun1, 2*, CAO Ying1, PENG Bo2, XU Tie-feng1, NIE Qiu-hua1, ZHANG Xiang-hua1, 3 . Energy Transfer and Mid-Infrared Luminescence Properties of Tm3+/Dy3+ Codoped Chalcohalide Glasses [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(09): 2321-2325. |
[2] |
ZHANG Peng-jun1, DAI Shi-xun1, 2*, LE Fang-da1, PENG Bo2, XU Tie-feng1, NIE Qiu-hua1, ZHANG Xiang-hua1, 3 . Mid-Infrared Emission and Multiphonon Relaxation in Tm3+-Doped Ge-Ga-Se Glasses[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(06): 1464-1468. |
|
|
|
|