Study on the Fracture Mechanism by Multi-Spectrum Methods
HU Rui-feng1, HAN Jing-hua1, FENG Guo-ying1*, HAN Wei2, ZHU Qi-hua2, WANG Zhu-ping1, GU Qiong-qiong1
1. College of Electronics ＆ Information Engineering, Sichuan University, Chengdu 610064, China
2. Laser Fusion Research Center, China Academy of Engineering Physics, Mianyang 621900, China
Abstract：Fused silica glass is a kind of indispensable material in high-energy laser system, and the damage of it has been one of the bottlenecks restricting the energy of system. In this paper, laser pulse shock wave was used to break down the fused glass samples, then the cause of the morphology of fractures on fused silica glass surface as well as internal phase transition were investigated experimentally and theoretically by multi-spectrum detecting of the samples before and after fracture, and the relationship between fracture morphologies and phase transition structure was explained from macro to micro. The fracture of the fused silica was induced by laser plasma shock wave, and during the shock wave, the tip of hoop stress produced from the inside glass would promote the crack propagation outward. We found that the whole fracture region could be divided into hackle zone, mist zone and mirror zone by morphology differences produced by the tip of hoop stress. The transmittance spectra and energy dispersive spectrometer were used to detect the samples before and after fracture. The results showed that the decrease of the transmittance and band gap of the glass were induced by the cracks, and the oxygen free or absent appeared in the fracture zone. Using the Raman spectrum to detect the different morphological areas of samples before and after broken, we found that the Si—O—Si band of fused glass breakage and recombination could reduce the relative content of three- and four-number rings structures corresponding to the stishovite and coesite of hackle zone, mist zone and mirror zone at the macro level. This kind of changes destroyed the mesh topology severely and induced the material fracture zone transforming to a higher density phase. From the micro level, the non-bridging oxygen hole center and E’center led to the decrease of the optical band gaps as well as transmittance which seriously affected the performance of glass.
胡锐峰，韩敬华，冯国英，韩 伟，朱启华，王竹萍，古琼琼. 使用多光谱手段研究熔石英断裂机理[J]. 光谱学与光谱分析, 2017, 37(11): 3327-3331.
HU Rui-feng, HAN Jing-hua, FENG Guo-ying, HAN Wei, ZHU Qi-hua, WANG Zhu-ping, GU Qiong-qiong. Study on the Fracture Mechanism by Multi-Spectrum Methods. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(11): 3327-3331.
[1] YU Zhen-kun, HE Hong-bo , QI Hong-ji, et al(余振坤，贺洪波，齐红基，等). Chinese Physics Letters(中国物理快报), 2013, 30(6): 067801.
[2] HE Xiang, WANG Gang, ZHAO Heng, et al(何 祥，王 刚，赵 恒，等). Chinese Physics B(中国物理B), 2016, 25(4): 048104.
[3] Liang Lv, Ma Ping, Huang Jinyong, et al. Applied Optics, 2016, 55(9): 2252.
[4] ZUO Yan-lei, WEI Xiao-feng, ZHOU Kai-nan, et al(左言磊，魏晓峰，周凯南，等). Chinese Physics B(中国物理B), 2016, 25(3): 256.
[5] Ocana J L, Morales M, Molpeceres C, et al. Applied Surface Science, 2004, 238(1-4): 242.
[6] ZHOU Qiang, QIU Rong, JIANG Yong, et al(周 强，邱 荣，蒋 勇，等). Chinese Optics Letters, 2016, 14(5): 051402.
[7] Raman R N, Demos S G, Shen N, et al. Optics Express, 2016, 24(3): 2634.
[8] Zhen J S, Yang Q, Yan Y H, et al. Radiation Effects and Defects in Solids, 2016, 171(3-4): 340.
[9] Lawn B. Fracture of brittle solids. Cambridge University Press, 1993. 25.
[10] Kajihara K, Hirano M, Skuja L, et al. Physical Review B Condensed Matter, 2008, 78(9): 1884.
[11] Cheng S, Schiefelbein S, Moore L, et al. Journal of Non-Crystalline Solids, 2006, 352(28): 3140.
[12] LU Peng-fei, WU Li-yuan, YANG Yang, et al(芦鹏飞，伍利源, 杨 阳，等). Chinese Physics B(中国物理B), 2016, 25(8): 086801.
[13] Shimada Y, Okuno M, Syono Y, et al. Physics & Chemistry of Minerals, 2002, 29(4): 233.
[14] Arndt J, Stffler D. The Science of Nature, 1968, 55(5): 226.
[15] Alfredo Pasquarello R C. Physical Review Letters, 1998, 80(23): 5145.