Preparation of TBSI with NS-Acetic Anhydride Method and Its Spectral Analysis
HOU Shao-gang1, JIA Tai-xuan1*, ZHANG Huan-ping1, LI Hong-liang2, ZHAO Ling1, TIAN Da-yong1, WANG Ti1
1. College of Chemistry & Environmental Engineering, Anyang Institute of Technology, Anyang 455000, China 2. Hebi Uhoo Chemical Co., Hebi 458000, China
Abstract:In the study, N-t-butyl-2-benzothiazole sulfenimide (TBSI) was prepared by NS-acetic anhydride method with acetic anhydride as solvent. It was detected with FTIR, XRD, UV-Vis, TG-DTA. Micro-structure and essence disciplinarian of them were disclosed. Chemical bond types into TBSI molecule were revealed with FTIR. TBSI phase composition and structure were revealed with crystallographic data from XRD detecting such as cell parameters and crystal face index. The phase composition and qualitative identification of TBSI structure were completed. The absorption peaks were detected by UV-vis at 228.3, 281.3 and 298.3 nm, respectively caused by n→σ*, π→π*, n→π* electron transition. It could provide basic data with the enterprise of ZBPD product quality inspection. Two kinds of information were detected with TG-DTA as quality change and thermal effect. There were three absorption peaks of 46.5, 188.9, 368. 5 ℃ due to a few residual solvent volatilization in the sample, phase transition peak and decomposition peak. The decomposition temperature of TBSI was very high. It could provided reference with research on rubber vulcanizing properties with TBSI on rubber vulcanizing machine. This study could provide basis experimental data on the enterprises to designate the working standard tracing detection of TBSI industrialized production. Performance index of TBSI was judged. The project of TBSI industry standard could be declared by the enterprises, written a draft standard.
[1] Cynthia J H, Alfred Sullivanl B, Brian Host C, et al. Rubber Chemistry and Technology, 1994, 1: 76. [2] Datta R N, Hoog A J. Raw Materials and Applications,2001, 5: 256. [3] Li Q Y. Chinese J. Chem., 2006, 24(12): 1716. [4] Li Jing, Gao Fengli, Enbo Shangguan, et al. Electrochimica Acta, 2014, 136(1): 377. [5] LIU Ya-juan, TAN Hai-sheng, GU Jin-cui(刘亚娟, 谭海生, 谷金翠). Chinese Journal of Tropical Crops(热带作物学报), 2013, 34(11): 2278. [6] Weng Zhehui, Chen Zilu, Qin Suni, et al. Inorganica Chimica Acta, 2009, 362(10): 3624. [7] Abdul Latif A, Boon Seng O. Chemical Engineering Journal, 2010, 156(2): 257. [8] Lagarde J P, Lavialle D. US Patent 0144242, 2015. [9] Favrot J M, Simon N, Marechal J M. US Patent 8927643, 2015. [10] Miyazaki T, Nakamura M. P. US Patent 9023928, 2015. [11] Sichender, Adolf, Schlesmann, et al. EP Patent 0529449A1, 2014. [12] Cynthia J Hann, Alfred B. Rubber Chemistry and Technology, 1994, 67(1): 76. [13] Krejsa M R, Koenig J L. Rubber Chemistry and Technology, 1993, 66(1): 73. [14] Lederer D A, Zaper M. Rubber World (United States), 1992, 206(2): 114. [15] QIN Chuan-xiao(秦川校). Spectrum Resolution of Organic Compound(有机化合物的波谱解析). Shanghai: East China University of Technology Press(上海: 华东科技大学出版社), 2007. [16] Charles J Rostek, Horng-Jau Lin. Rubber Chemistry and Technology, 1996, 69(2): 180.