Spectroscopic Study on Film Formation Mechanism and Structure of Composite Silanes-V-Zr Passive Film
WANG Lei1, LIU Chang-sheng2, SHI Lei2, AN Cheng-qiang1
1. School of Environmental and Chemical Engineering, Shenyang Ligong University, Shenyang 110159, China 2. Key Laboratory for Anisotropy & Texture of Materials, Ministry of Education, Northeastern University, Shenyang 110004, China
Abstract：A composite silanes-V-Zr passive film was overlayed on hot-dip galvanized steel. Attenuated total reflection Fourier transformed infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectrometer (XPS) and radio frequency glow discharge optical emission spectrometry (rf-GD-OES) were used to characterize the molecular structure of the silanes-V-Zr passive film. The mechanism of film formation was discussed. The results show that the silane molecules are crosslinked as the main film former and inorganic inhibitor is even distributed in the film. The fitting peak of 100.7 eV in XPS single Si2p energy range spectra of the composite silanes-V-Zr passive film and the widening and strengthening of the Si—O infrared absorption peak at 1 100 cm-1 indicate that the silanes were adsorbed on the surface of zinc with chemical bond of Si—O—Zn, and the silane molecules were connected with each other by bond of Si—O—Si. Two characteristic absorption peaks of amide at 1 650 and 1 560 cm-1 appear in the infrared spectroscopy of the composite silanes-V-Zr passive film, and a characteristic absorption peak of epoxy groups at 910 cm-1 disappears in the infrared spectroscopy of the passive film. The results indicate that γ-APT can be prepared through nucleophilic ring-opening of ethylene oxide in γ-GPT molecule to form C—N covalent bonds. The rf-GD-OES results indicate that there is a oxygen enriched layer in 0.3 μm depth of the composite silanes-V-Zr passive film. Moreover, ZrF4, ZrO2 and some inorganic matter obtained by the reaction during the forming process of the composite silanes-V-Zr passive film are distributed evenly throughout the film. According to the film composition, the physical processes and chemical reactions during the film forming process were studied by using ATR-FTIR. Based on this, the film forming mechanism was proposed.
王 雷1，刘常升2，石 磊2，安成强1 . 光谱学研究硅烷钒锆复合钝化膜的结构和成膜机理 [J]. 光谱学与光谱分析, 2015, 35(02): 453-456.
WANG Lei1, LIU Chang-sheng2, SHI Lei2, AN Cheng-qiang1 . Spectroscopic Study on Film Formation Mechanism and Structure of Composite Silanes-V-Zr Passive Film. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(02): 453-456.
[1] Zhu D Q, van Ooij W J. Electrochimica Acta, 2004, 49(7): 1113. [2] Fedel M, Olivierb M, Poelmanc M et al. Progress in Organic Coatings, 2009, 66(3): 118. [3] Xiao W, Man R L, Miao C et al. Journal of Rare Earths, 2010, 28(3): 117. [4] Zhang J, Wu C Y. Progress in Organic Coatings, 2009, 66(3): 387 [5] Song D, Jing X Y, Wang J, et al. Journal of Alloys and Compounds, 2012, 510(1): 66. [6] Lu Xiangyu, Zuo Yu, Zhao Xuhui, et al. Corrosion Science, 2012, 60(7): 165. [7] Yue Yuanyuan, Liu Zhongxia, Wan Tingting, et al. Progress in Organic Coatings, 2013, 76(3): 835. [8] YU Xing(余 兴). Chinese Journal of Inorganic Analytical Chemistry(中国无机分析化学), 2011，1(1): 53. [9] ZHOU Chan, XU Jia-xi(周 婵，许家喜). Progress in Chemistry(化学进展), 2011，23(1): 165. [10] WANG Lei, LIU Chang-sheng, SHI Lei(王 雷，刘常升，石 磊). Journal of Northeastern University(Natural Science)(东北大学学报·自然科学版), 2011，32(7): 956.