Abstract：We have investigated the performances of organic light-emitting diodes (OLED) with different spacer, the structure was fabricated as ITO/MoO3(40 nm)/NPB(40 nm)/TCTA(10 nm)/CBP∶GIr114%∶R-4B2%(30 nm)/spacer (3 nm)/ CBP∶GIr114%∶R-4B2%(30 nm)/BCP(10 nm)/Alq3(40 nm)/LiF(1 nm)/Al(100 nm), the spacers were CBP，TCTA，TPBI and BCP separately, GIr1 and R-4B were green and red phosphorescent dye respectively. The results showed that compared to the reference device utilized CBP as the spacer layer, TCTA，TPBI and BCP had higher current efficiency in excess of 59%，79% and 93%, the maximum current efficiency of 16.91 cd·A-1 was achieved with BCP as the spacer at voltage of 5 V, TPBI and BCP as the spacer layer obtained the higher current density and lower efficiency roll-off. We attributed to these results to the follow reasons, the first was that carriers and excitons were limited to a narrow recombination region because of TCTA with higher LUMO energy level and triplet energy, which improved the probability of carriers recombination, in addition, more serious quenching at higher current density. The second reason was that TPBI and BCP had the higher HOMO energy level and electron mobility, which broadened excitons recombination zone. In addition, the spacer layer caused the accumulation of electrons or holes and the formation of high space electric field, leading to carrier injection and transport more effectively. In particular, we obtained a better stability of phosphorescent organic light-emitting diodes since the way for the red and green co-doped with host material.
张 微，张方辉*，黄 晋 . 间隔层对红绿磷光有机电致发光器件发光性能的影响 [J]. 光谱学与光谱分析, 2014, 34(02): 322-326.
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326.
[1] Xiao Y, Yang J P, Cheng P P, et al. Appl. Phys. Lett., 2012, 100: 013308. [2] Goushi K, Adachi C. Appl. Phys. Lett., 2012, 101: 23306. [3] Chen Y H, Chen J S, Zhao Y B, et al. Appl. Phys. Lett., 2012, 100: 213301. [4] Zhao F C, Zhang Z Q, Dai Y F, et al. Organic Electronics, 2012, 13: 1049. [5] Liu J, Teng M Y, Zhang X P. Organic Electronics, 2012, 13: 2177. [6] WANG Xu-peng, MI Bao-xiu, GAO Zhi-qiang, et al(王旭鹏，密保秀，高志强，等). Acta Phys. Sin.(物理学报), 2011, 60: 00878. [7] Kalinowskia J, Fattori V, Cocchi M, et al. Coordination Chemistry Reviews, 2011, 255: 2401. [8] Zhang D D, Duan L, Zhang D Q, et al. Organic Electronics, 2013, 14: 260. [9] Shen C Y, Yang Y, Jin S Z, et al. International Journal for Light and Electron Optics, 2010, 121: 1487. [10] Choi J, Koh T, Lee S, et al. Appl. Phys. Lett., 2012, 100: 233303. [11] Lee S, Tang C W, Rothberg L J. Appl. Phys. Lett., 2012, 101: 043303. [12] Bhansali V, Jia H P, Oswald L W, et al. Appl. Phys. Lett., 2012, 100: 183305. [13] Zhao B, Su Z S, Li W L, et al. Appl. Phys. Lett., 2012, 101: 053310. [14] Wetzelaer G, Najaki A, Kist R, et al. Appl. Phys. Lett., 2013, 102: 053301. [15] Hu Y M, Chen X Q, Zhan Y Q, et al. Appl. Phys. Lett., 2012, 100: 163303. [16] Zhao F C, Zhang Z Q, Liu Y P, et al. Organic Electronics, 2012, 313: 1049. [17] GAO Li-yan, ZHAO Su-ling, XU Zheng, et al(高利岩，赵谡玲，徐 征，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2011, 31(9): 2328. [18] CHEN Su-jie, YU Jun-sheng, WEN Wen, et al(陈苏杰，余军胜，文 雯，等). Acta Phys. Sin.(物理学报), 2011, 60: 037202. [19] Hwang M C, Thangargju K, So K, et al. Synthetic Metals, 2012, 162: 391. [20] Acharya R, Cao X A. Appl. Phys. Lett., 2012, 101: 053306. [21] Gao C H, Zhou D Y, Gu W, et al. Organic Electronics, 2013, 14: 1177.