光谱学与光谱分析
|
合金钢的激光诱导击穿光谱实验条件优化
邵 妍,高 勋* ,杜 闯,赵振明,陈伟钰,郝作强,孙长凯,林景全
长春理工大学理学院, 吉林 长春 130022
The LIBS Experiment Condition Optimization of Alloy Steel
SHAO Yan, GAO Xun* , DU Chuang, ZHAO Zhen-ming, CHEN Wei-yu, HAO Zuo-qiang, SUN Chang-kai, LIN Jing-quan
School of Science, Changchun University of Science and Technology, Changchun 130022, China
摘要 : 利用1 064 nm波长Nd∶YAG脉冲激光诱导击穿合金钢产生激光等离子体光谱,采用高分辨率及门宽控制的ICCD探测LIBS信号光谱。选用铁元素原子谱线404.581,414.387,427.176和438.355 nm进行分析,研究了不同实验参数对LIBS光谱信号强度的影响结果。实验结果表明,激光脉冲能量、激光聚焦位置以及ICCD探测器的延时等实验参数对合金钢LIBS信号有较大影响。通过优化这些实验参数,获得高光谱强度和信背比的LIBS信号,确定了LIBS技术用于合金钢微量元素成分分析的最佳实验条件,从而开展合金钢样品成分分析。
关键词 :激光诱导击穿光谱;光谱强度;信背比;合金钢
Abstract :Laser induced plasma spectroscopy of alloy steel was produced by Nd∶YAG pulsed laser at 1 064 nm, and the spectral signal was detected by high resolution and width controlled ICCD. Several Fe atomic spectral lines such as 404.581, 414.387, 427.176 and 438.355 nm were chosen for analysis, and the effects of different experimental parameters on LIBS spectral signal intensity were investigated. It is shown that the experimental parameters such as pulse energy, laser focus location and laser delay time have great influence on the LIBS signal. LIBS signals with high spectral intensity and signal-background ratio (SBR) as well as the optimum experiment conditions were obtained by optimizing these experiment parameters so as to make composition analysis of the alloy steel.
Key words :LIBS;Spectral intensity;SBR;Alloy steel
收稿日期: 2012-06-29
修订日期: 2012-09-20
通讯作者:
高 勋
E-mail: lasercust@yahoo.com.cn
引用本文:
邵 妍,高 勋* ,杜 闯,赵振明,陈伟钰,郝作强,孙长凯,林景全 . 合金钢的激光诱导击穿光谱实验条件优化 [J]. 光谱学与光谱分析, 2013, 33(02): 531-534.
SHAO Yan, GAO Xun* , DU Chuang, ZHAO Zhen-ming, CHEN Wei-yu, HAO Zuo-qiang, SUN Chang-kai, LIN Jing-quan . The LIBS Experiment Condition Optimization of Alloy Steel . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(02): 531-534.
链接本文:
https://www.gpxygpfx.com/CN/10.3964/j.issn.1000-0593(2013)02-0531-04
或
https://www.gpxygpfx.com/CN/Y2013/V33/I02/531
[1] Sturm V, Schmitz H U, Reuter T, et al. Spectrochimica Acta Part B: Atomic Spectroscopy, 2008, 63(10): 1167. [2] Laszlo Peter, Volker Sturm, Reinard Noll. Applied Optics, 2003, 42(30): 6199. [3] SUN Lan-xiang, YU Hai-bin, XIN Yong, et al(孙兰香,于海斌,辛 勇,等). Chinese Journal of Lasers(中国激光), 2011, 38(9): 0915002. [4] SUN Lan-xiang, YU Hai-bin, CONG Zhi-bo, et al(孙兰香,于海斌,丛智博,等). Chinese Journal of Scientific Instrument(仪器仪表学报), 2011, 32(11): 2602. [5] Hiroyuki Kondo, Naoya Hamada, Kazuaki Wagatsuma. Spectrochimica Acta Part B: Atomic Spectroscopy, 2009, 64(9): 884. [6] Kondo Hiroyuki, Aimoto Michihiro, Yamamura Hideaki, et al. Metallurgical Analysis(冶金分析), 2009, 29(1):13. [7] Herbert Balzer, Stefan Holters, Volker Sturm, et al. Anal. Bioanal. Chem., 2006, 385(2): 234. [8] SUN Lan-xiang, YU Hai-bin, CONG Zhi-bo, et al(孙兰香,于海斌,丛智博,等). Acta Optica Sinica(光学学报), 2010, 30(9): 2757. [9] DONG Mei-rong, LU Ji-dong, LI Jun, et al(董美蓉,陆继东,李 军,等). Acta Optica Sinica(光学学报), 2011, 31(1): 0130002-1. [10] LIN Zhao-xiang, LI Jie, LU Ji-dong, et al(林兆祥, 李 捷, 陆继东, 等). Journal of Huazhong University of Science and Technology(Nature Science Edition)(华中科技大学学报·自然科学版), 2009, 37(4): 17. [11] Margetic V, Pakulev A, Stockhaus A, et al. Spectrochimica Acta Part B: Atomic Spectroscopy, 2000, 55(11): 1771.
[1]
刘 佳,郭飞飞,于 雷,崔飞鹏,赵 迎,韩 冰,沈学静,王海舟. 激光诱导击穿光谱技术对钕铁硼永磁材料中多元素的定量表征 [J]. 光谱学与光谱分析, 2024, 44(01): 141-147.
[2]
杨文锋,林德惠,曹 宇,钱自然,李绍龙,朱德华,李 果,张 赛. 基于PCA-SVM的飞机蒙皮激光分层除漆LIBS在线监测研究 [J]. 光谱学与光谱分析, 2023, 43(12): 3891-3898.
[3]
孙成玉,焦 龙,闫娜莹,闫春华,屈 乐,张晟瑞,马 羚. 激光诱导击穿光谱结合人工神经网络鉴别不同产地的丹参药材 [J]. 光谱学与光谱分析, 2023, 43(10): 3098-3104.
[4]
刘 曙,金 悦,苏 飘,闵 红,安雅睿,吴晓红. 变量重要性-反向传播人工神经网络辅助激光诱导击穿光谱测定铁矿石中硅、铝、钙和镁含量 [J]. 光谱学与光谱分析, 2023, 43(10): 3132-3142.
[5]
李长明,陈安民,高 勋,金明星. 不同样品温度下激光诱导等离子体的空间分辨光谱 [J]. 光谱学与光谱分析, 2023, 43(07): 2032-2036.
[6]
赵 洋,张 雷,程年恺,尹王保,侯佳佳,白成华. 二元激光等离子体的时空演化机制研究 [J]. 光谱学与光谱分析, 2023, 43(07): 2067-2073.
[7]
王 斌,郑少锋,甘久林,刘 曙,李伟才,杨中民,宋武元. 塑料标准样品结合偏最小二乘法在激光诱导击穿光谱法元素定量分析领域的研究 [J]. 光谱学与光谱分析, 2023, 43(07): 2124-2131.
[8]
胡梦颖,张鹏鹏,刘 彬,杜雪苗,张灵火,徐进力,白金峰. 高压制样-激光诱导击穿光谱技术测定土壤中的硅铝铁钾 [J]. 光谱学与光谱分析, 2023, 43(07): 2174-2180.
[9]
吴书佳,姚明印,曾剑辉,何 梁,付港荣,曾瑜琦,薛 龙,刘木华,黎 静. 猪饲料中Cu元素的空间限域LIBS检测 [J]. 光谱学与光谱分析, 2023, 43(06): 1770-1775.
[10]
袁 舒,吴 鼎,武华策,刘佳敏,吕 燕,海 然,李 聪,冯春雷,丁洪斌. 真空下激光烧蚀碳化钨铜多组分等离子体发射光谱的时空演化研究 [J]. 光谱学与光谱分析, 2023, 43(05): 1394-1400.
[11]
王 秋,李 斌,韩昭洋,占朝辉,廖 军,刘燕德. 基于LIBS结合傅里叶变换NIR技术的油茶炭疽病等级研究 [J]. 光谱学与光谱分析, 2023, 43(05): 1450-1458.
[12]
柴 树,彭海蒙,武文栋. 高温环境中基于声学信号的激光诱导击穿光谱校正方法 [J]. 光谱学与光谱分析, 2023, 43(05): 1401-1407.
[13]
宁倩倩,杨佳浩,刘晓琳,何玉韩,皇甫至超,余文静,王朝晖. 时间分辨飞秒激光诱导击穿光谱的设计与研究 [J]. 光谱学与光谱分析, 2023, 43(04): 1083-1087.
[14]
丁坤艳,何长涛,刘志刚,肖 婧,冯国英,周凯南,谢 娜,韩敬华. 基于综合光谱法的污染物颗粒诱导光学元件损伤研究 [J]. 光谱学与光谱分析, 2023, 43(04): 1234-1241.
[15]
苏云鹏,贺春景,李昂泽,徐可米,邱丽荣,崔 晗. 基于共焦LIBS技术结合机器学习的矿石分类识别方法 [J]. 光谱学与光谱分析, 2023, 43(03): 692-697.