γ射线辐照处理竹材的X射线光谱研究
孙丰波1 , 费本华1 , 江泽慧1* , 于子绚1 , 田根林1 , 杨全文2
1. 国际竹藤网络中心,国家林业局竹藤科学与技术重点实验室,北京 100102 2. 国家林业局北京林业机械研究所,北京 100029
Study on Bamboo Treated with γ Rays by X-Ray Diffraction
SUN Feng-bo1 , FEI Ben-hua1 , JIANG Ze-hui1* , YU Zi-xuan1 , TIAN Gen-lin1 , YANG Quan-wen2
1. The International Center for Bamboo and Rattan, Beijing 100102, China 2. Beijing Forestry Machine Institute, State Forestry Administration, Beijing 100029, China
摘要 : 利用X射线衍射仪,对γ射线辐照处理前后的竹材进行X射线光谱分析,得出竹材结晶度和微纤丝角在辐照过程中的变化规律。随着辐照剂量的增加,竹材纤维素结晶度呈现先升高后降低的趋势,微纤丝角变化不明显,表明微纤丝角不是影响辐照过程中竹材物理、力学性能变化的主要因子。
关键词 :γ射线;竹材;辐照剂量;X射线光谱
Abstract :The microfibril angle and crystallinity of bamboo treated with γ rays were tested by X-ray diffraction (XRD). The result indicated that crystallinity in bamboo increased when irradiation dose was less than 100 kGy, while the irradiation dose was raised to about 100 kGy, crystallinity in bamboo reduced. But during the whole irradiation process, the influence on microfibril angle was not obvious, so it was not the dominant factors on variation in physical-mechanical properties of bamboo during the process of irradiation.
Key words :γ Rays;Bamboo;Irradiation dose;X-ray diffraction
收稿日期: 2010-08-10
修订日期: 2010-12-20
通讯作者:
江泽慧
E-mail: jiangzehui@icbr.ac.cn
引用本文:
孙丰波1 , 费本华1 , 江泽慧1* , 于子绚1 , 田根林1 , 杨全文2 . γ射线辐照处理竹材的X射线光谱研究[J]. 光谱学与光谱分析, 2011, 31(06): 1717-1719.
SUN Feng-bo1 , FEI Ben-hua1 , JIANG Ze-hui1* , YU Zi-xuan1 , TIAN Gen-lin1 , YANG Quan-wen2 . Study on Bamboo Treated with γ Rays by X-Ray Diffraction. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(06): 1717-1719.
链接本文:
https://www.gpxygpfx.com/CN/10.3964/j.issn.1000-0593(2011)06-1717-03
或
https://www.gpxygpfx.com/CN/Y2011/V31/I06/1717
[1] Burmester A. Materialpruf, 1966, 8: 205. [2] Goto T, Harada H, Saiki H. Bull Kyoto Univ. Forest, 1974, 46: 153. [3] Tsutomu Aoki, Misato Norimoto, Tadashi Yamada. Wood Research, 1977, 62: 19. [4] CAI Yu-lan, WANG Dong-wei. Journal of Cellulose Science and Technology, 2009, 17(1): 1. [5] LI Jian. Wood Science. Beijing: Higher Education Press. [6] JIANG Zehui. Bamboo and Rattan in the World. Shenyang: Liao Ning Science and Technology Publishing House, 2002. [7] JIANG Ze-hui, ZHOU Hui-yu, RUAN Xi-gen, et al. Scientia Silvae Sinicae, 2000, 36(3): 122. [8] YU Yan, WANG Ge, QIN Dao-chun, et al. Journal of Northeast Forestry University, 2007, 35(8): 28. [9] XU You-ming. Wood Science. Beijing: China Forestry Publishing House, 2006. [10] YANG Ge-sheng, WEI Meng-yuan, SHAO Hui-li, et al. J. Radiat. Res. Radiat. Process, 2007, 25(3): 141. [11] YANG Ge-sheng, SHAO Hui-li, HU Xue-chao. Journal of Functional Polymers, 2007, 19-20(2): 143.
[1]
李远静,陈彩云飞,李立平. γ射线辐照处理银灰色Akoya珍珠的谱学特征研究 [J]. 光谱学与光谱分析, 2023, 43(04): 1056-1062.
[2]
. 我国X射线光谱现场分析技术研究进展 [J]. 光谱学与光谱分析, 2021, 41(03): 704-713.
[3]
. X射线光谱数据处理平台的优化设计 [J]. 光谱学与光谱分析, 2021, 41(03): 763-767.
[4]
. X射线光谱中特征峰漂移校正算法的研究 [J]. 光谱学与光谱分析, 2020, 40(11): 3633-3638.
[5]
. 铜唑防腐剂处理竹材的同步辐射无损检测研究 [J]. 光谱学与光谱分析, 2018, 38(03): 901-904.
[6]
楚 杰;张军华*;马 莉;路海东* . XRD与NMR的热处理竹材结晶性能研究 [J]. 光谱学与光谱分析, 2017, 37(01): 256-261.
[7]
楚 杰;马 莉*;张军华*. 热处理竹材的化学成分傅里叶变换红外光谱分析 [J]. 光谱学与光谱分析, 2016, 36(11): 3557-3562.
[8]
安 鑫;杨淑敏;刘 嵘;韦鹏练;杨春明*;费本华* . 基于SR-WAXS技术的竹材纤维素晶胞模型研究 [J]. 光谱学与光谱分析, 2016, 36(11): 3704-3708.
[9]
彭冠云;江泽慧*;刘杏娥;余 雁;杨淑敏;邓 彪;肖体乔;王晓欢. 木材、竹材密度的CT技术检测 [J]. 光谱学与光谱分析, 2012, 32(07): 1935-1938.
[10]
罗彩香;夏海平*;虞 灿;张约品;徐 军 . γ射线辐照与O2 退火对Bi∶CdWO4 单晶体光谱性能的影响 [J]. 光谱学与光谱分析, 2012, 32(06): 1476-1479.
[11]
孙丰波;江泽慧;费本华*;陆 方;于子绚;常祥祯 . γ射线辐照处理竹材化学组分及结晶度变化研究 [J]. 光谱学与光谱分析, 2011, 31(07): 1922-1924.
[12]
汪佑宏;刘杏娥;江泽慧*;费本华;任海青 . 利用X射线衍射技术分析辐照处理对黄藤材晶体尺寸影响 [J]. 光谱学与光谱分析, 2010, 30(08): 2285-2288.
[13]
马 敏;王化祥;郝魁红 . 基于γ 射线的多相流检测系统 [J]. 光谱学与光谱分析, 2010, 30(07): 1998-2002.
[14]
孙丰波;余 雁;江泽慧*;任海青;王 戈;刘杏娥 . 竹材的纳米TiO2 改性及抗菌防霉性能研究 [J]. 光谱学与光谱分析, 2010, 30(04): 1056-1060.
[15]
王雅梅;王喜明*;刘君良. 应用ATR-FTIR研究铜唑类防腐剂在竹材中的固着机理 [J]. 光谱学与光谱分析, 2009, 29(10): 2651-2653.