Effect of O2/Ar Ratio on Blue Photoluminescence Spectrum of Nanocrystalline ZnO Films
SONG Guo-li1，FANG Xiang-yun2，LIANG Hong1
1. Department of Physics, Harbin University, Harbin 150086, China 2. Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China
Abstract：Nanocrystalline ZnO films were deposited on quartz substrates by radio-frequency magnetron sputtering (RFMS) method. The authors discussed the effect caused by the change in the ratio of oxygen to argon and quartz substrates temperature on the qualities of thin films and blue photoluminescence spectrum of ZnO films. Relationship between XRD intensity and FWHM of nanocrystalline ZnO films at different ratio of O2/Ar in processing was given. Photoluminescence spectrum (PL), absorption spectra (ABS), photoluminescence excitation spectrum (PLE) and X-ray diffraction pattern (XRD) of nanocrystalline ZnO film with excitation wavelength 300 nm were measured at room temperature. XRD pattern indicates that nanocrystalline ZnO film has a hexagonal wurtzite structure and is polycrystalline. Blue visible emission bands (430-460 nm) were observed, and its central wavelength is 445 nm. The relationship between PL area of integration and PL intensity of maximum of nanocrystalline ZnO films at different ratio of O2/Ar in processing was given. The luminescence emission peak located at 450 nm corresponds to the transition from the shallow level of oxygen vacancy to valence band or the interstitial.
宋国利1，方香云2，梁 红1 . 氧氩比对纳米ZnO薄膜蓝光发射光谱的影响[J]. 光谱学与光谱分析, 2010, 30(03): 591-594.
SONG Guo-li1，FANG Xiang-yun2，LIANG Hong1 . Effect of O2/Ar Ratio on Blue Photoluminescence Spectrum of Nanocrystalline ZnO Films. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(03): 591-594.
[1] Tang Z K, Ping Yu, Wong G K L, et al. Nonlinear Optics, 1997, 18(2-4): 355. [2] Tang Z K, Wong G K L ,Yu P, et al. Appl. Phys. Lett., 1998, 72(25): 3270. [3] Bagnall D M, Chen Y F. Applied Physics Letters, 1997, 70(17): 2230. [4] Bagnall D M, Chen Y F, et al. Cryst. Growth, 1998, 184(2): 605. [5] Vanhensden K, Seager C H, Warren W L, et al. Appl. Phys. Lett., 1996, 68(3): 403. [6] Cao H, Zhao Y G, Ong H C, et al. Appl. Phys. Lett., 1998, 73(25): 3656. [7] Cho S, Ma J, Sun Y. Applied Physics Letters, 1999, 75(18): 2761. [8] Vanhensden K，Warren W L，Seager C H，et al. Appl. Phys., 1996, 79(10): 7983. [9] XIE Lun-jun, CHEN Guang-de, ZHU You-zhang, et al(谢伦军，陈光德，竹有章, 等). Chinese Journal of Luminescence(发光学报)，2006，27(2): 215. [10] SU Feng-lian, PENG Guan-liang, ZOU Jun, et al(苏凤莲，彭观良，邹 军, 等). Journal of Synthetic Crystals(人工晶体学报)，2005，34(1): 107. [11] FU Zhu-xi, LIN Bi-xia, ZHU Jie, et al(傅竹西，林碧霞，祝 杰, 等). Chinese Journal of Luminescence(发光学报)，2001，22(2): 119. [12] LIN Bi-xia, FU Zhu-xi, LIAO Gui-hong (林碧霞，傅竹西，廖桂红). Chinese Journal of Luminescence(发光学报)，2005，26(2): 225. [13] WANG Qing-pu, ZHANG De-heng, XUE Zhong-ying, et al(王卿璞，张德恒，薛忠营, 等). Chinese Journal of Luminescence(发光学报)，2003，24(1): 69. [14] SONG Guo-li, SUN Kai-xia(宋国利，孙凯霞). Acat Photonica Sinica(光子学报), 2006，35(3): 389. [15] XU Peng-shou, SUN Yu-ming, SHI Chao-shu, et al(徐彭寿, 孙玉明, 施朝淑，等). Science in China, A(中国科学, A)，2001, 31(4): 358. [16] LAN Zhen-li, ZHANG Xi-qing, YANG Guang-wu, et al (蓝镇立，张希清，杨广武, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2008，28(2): 253. [17] CHEN Jun, FENG Zhao-chi, YING Pin-liang, et al(陈 钧，冯兆池，应品良, 等). Chemical Journal of Chinese Universities(高等学校化学学报)，2004，25(11): 2074. [18] WANG Quan, ZHANG Qi-feng, SUN Hui, et al(王 全，张琦锋，孙 晖, 等). Chinese Journal of Chemical Physics(化学物理学报), 2007，20(11): 1667.