Abstract：The photo-stability of both MDMO-PPV film and MEH-PPV film, as irradiated under different conditions, and in the presence and absence of oxygen and visible light luminance, were studied by UV-Vis spectra and fluorescence spectra respectively. The maximum absorbance of them was at 500 nm, while the maximum fluorescence intensity of them were at 580 and 589 nm, respectively. In the presence of both oxygen and light irradiation, the fluorescence intensity was decreased and the films were damaged. Photocatalysis oxidation technology using solid-state nanocrystalline TiO2-PVC film was introduced to increase the photo-stability and some meaningful clues were observed.
李晓娥1, 2, 阎宏涛1, Durrant James R2 . 共轭聚合物聚对苯撑乙烯膜的光稳定性研究[J]. 光谱学与光谱分析, 2005, 25(05): 743-746.
LI Xiao-e1, 2, YAN Hong-tao1, DURRANT James R2 . Studies on the Photo-Stability of Poly p-(Phenylene Vinylene). SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(05): 743-746.
[1] LIU Hai-peng, ZENG Fan-di, LIU Shi-jun(刘海鹏, 曾繁涤, 刘世俊). J. Wuhan Inst. Chem. Tech.(武汉化工学院学报), 2001, 23(4): 29. [2] Munters T, Martens T, Goris L et al. Thin Solid Films, 2002, 403-404: 247. [3] Friend R H, Gymer R W, Holmes A B et al. Nature, 1999, 397: 121. [4] Zheng Min, Bai Fenglian, Zhu Daoben. Polymers for Advanced Technologies, 1999, 10: 476. [5] Dehong Hu, Ji Yu, Paul F Barbara. J. Am. Chem. Soc., 1999, 121: 6936. [6] Thomas Huser, Ming Yan. Journal of Photochemistry and Photobiology A: Chemistry, 2001, 144: 43. [7] Atreya M, Li S, Kang E T et al. Polymer Degradation and Stability, 1999, 65: 287. [8] Hong Yee Low. Thin Solid Films, 2002, 413: 160. [9] Christoph J, Brabec N, Serdar Sariciftci, Jan C Hummelen. Advanced Functional Materials, 2001, 11(1): 15. [10] Topoglidis E, Lutz T, Willis R L et al. Faraday Discuss, 2000, 116: 35.