CeOx 与ZnO纳米复合粉体的制备及其发光性能
郭书霞,张兴堂,赵慧玲,李蕴才,黄亚彬,杜祖亮*
河南大学特种功能材料重点实验室,河南 开封 475001
Preparation and Luminescence of CeOx /ZnO Nanocomposite Powders
GUO Shu-xia, ZHANG Xing-tang, ZHAO Hui-ling, LI Yun-cai, HUANG Ya-bin,DU Zu-liang*
Key Laboratory of Special Functional Materials, Henan University, Kaifeng 475001, China
摘要 : 通过溶胶-凝胶法制备CeOx /ZnO纳米复合粉体,并对其结构和光致发光特性进行了研究。发现500 ℃烧结出的复合粉体在502 nm处的绿光发射同纯ZnO的相比有显著的增强;600 ℃烧结的样品在603 nm出现新的发光峰。通过XRD和XPS分析认为荧光增强的主要原因同粉体中铈主要以Ce3+ 形式存在有关,新的发光峰可能来源于ZnO/CeO2 界面处形成的新的能级跃迁。
关键词 :ZnO;复合粉体;发光
Abstract :CeOx /ZnO nanocomposite powders were prepared by sol-gel process. The powder samples were examined by XRD,TEM,XPS and photoluminescence (PL). PL enhancement of nanocomposite powder at 502 nm compared to pure ZnO was observed when Ce3+ were present in samples. New peak at 603 nm was observed when Ce4+ were present. PL enhancement of nanocomposite powder was correlated with more oxygen vacancies which were caused by Ce3+ . The new peak at 603 nm is attributed to new energy transition in the interface of CeO2 /ZnO.
Key words :ZnO;Nanocomposite;Luminescence
收稿日期: 2004-03-26
修订日期: 2004-06-28
通讯作者:
杜祖亮
引用本文:
郭书霞,张兴堂,赵慧玲,李蕴才,黄亚彬,杜祖亮* . CeOx 与ZnO纳米复合粉体的制备及其发光性能[J]. 光谱学与光谱分析, 2005, 25(06): 840-843.
GUO Shu-xia, ZHANG Xing-tang, ZHAO Hui-ling, LI Yun-cai, HUANG Ya-bin,DU Zu-liang* . Preparation and Luminescence of CeOx /ZnO Nanocomposite Powders . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(06): 840-843.
链接本文:
https://www.gpxygpfx.com/CN/Y2005/V25/I06/840
[1] Zhang S B, We S H. Alex Zunger. Phys. Rev. B, 2001, 63: 075205. [2] Vanheusden K, Warren W L, Seager C H,Voigt J A. J. Appl. Phys.,1996, 79: 7983. [3] Studenikin S A,Michael Cocivera. J. Appl. Phys.,2002, 91: 5060. [4] Kohan A F, Ceder G, Morgan D. Phys. Rev. B, 2000, 61: 15019. [5] Lü Shu-chen, SONG Guo-li, XIAO Zhi-yan,et al(吕书臣,宋国立,肖芝燕,等). Chin. J. Lumin.(发光学报), 2002, 23(3): 306. [6] Bixia Lin,Zhuxi Fu. Appl. Phys. Lett.,2001, 79: 943. [7] Garces N Y, Wang L, Bai L, Giles N C, Hallibuton L E. Appl. Phys. Lett.,2002, 81: 622. [8] Vladimir Z Mordkovich,Hideki Hayashi,et al. Adv. Funct. Mater.,2003, 13: 519. [9] LIN Hai, LIU Xing-ren(林 海,刘行仁). Journal of the Chinese Rare Earth Society(中国稀土学报), 1997, 15: 309. [10] XU Xiao-liang, XU Jun, XU Chuan-ming,et al(许晓亮, 徐 军, 徐传明,等). Chinese J. of Lumin.(发光学报), 2000, 23(3): 306. [11] CAI Chun-lin, YANG Shao-yan,et al(柴春林,杨少延,等). Chinese Science Bulletin(科学通报),2003, 48: 780. [12] Yong Xu,Martin Scoonen A A. American Mineralogist,2000, 85: 543. [13] Salvi A M, Decker F, Varsano F,Speranza G. Surf. Interface Anal.,2001, 31: 255. [14] XU Xiao-liang, XU Jun, XU Chuan-ming,et al(许小亮, 徐 军, 徐传明,等). Chinese J. of Lumin.(发光学报), 2003, 24: 171. [15] Zheng M J, Zhang L D, Li G H, Shen W Z. Chemical Physics Letter,2002, 363: 123. [16] Wu X L, Siu G G, Fu C L, Ong H C. Appl. Phys. Lett., 2001, 78: 2285(C). [17] ZHOU Li-qun, LIU Shi-zhong, SUN Ju-tang(周立群,柳士忠,孙聚堂). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2004,24(10):1217.
[1]
赖 妞,黄启强,张秦阳,张博文,王 娟,杨 杰,王 茺,杨 宇,王荣飞. CsPbX3 QDs@MOFs复合材料的研究综述 [J]. 光谱学与光谱分析, 2023, 43(11): 3321-3329.
[2]
丁 寒. 荧光性客体表面潜在手印的无背景显现研究 [J]. 光谱学与光谱分析, 2023, 43(11): 3427-3435.
[3]
覃丽梅,沈锡田. 抚顺煤精的光致发光光谱特征研究 [J]. 光谱学与光谱分析, 2023, 43(10): 3180-3185.
[4]
朱红伟,程佑法,陈淑祥,范春丽,李 婷,刘海彬,赵潇雪,山广褀,李建军. 一种疑似合成钻石的天然钻石光谱学特征 [J]. 光谱学与光谱分析, 2023, 43(06): 1690-1696.
[5]
严雪俊,周 扬,胡丹静,俞丹燕,余思逸,严 俊. 基于UV-Vis漫反射、Raman与PL光谱联用技术在黄色珍珠无损检测中的应用 [J]. 光谱学与光谱分析, 2023, 43(06): 1703-1710.
[6]
韩朝霞,杨志金,张志红,丁淑惠,张大伟,洪瑞金,陶春先,林 辉,禹德朝. 全彩色碳量子点的制备及其在WLED上的应用 [J]. 光谱学与光谱分析, 2023, 43(05): 1358-1366.
[7]
李 兆,王亚楠,徐祎朴,曹 静,王永锋,吴坤尧,邓 璐. 白光LED用YVO4 ∶Tm3+ 蓝色荧光粉的制备及发光性能 [J]. 光谱学与光谱分析, 2023, 43(02): 623-628.
[8]
翟艳珂,潘宜杏,向 浩,徐 黎,朱泽策,雷 咪. DSAZn与槲皮素的配位结合及对槲皮素的高灵敏度检测 [J]. 光谱学与光谱分析, 2023, 43(01): 122-128.
[9]
赵国强,仇猛淋,张金福,王庭顺,王广甫. 基于Voigt函数拟合的离子激发发光光谱分峰方法 [J]. 光谱学与光谱分析, 2022, 42(11): 3512-3518.
[10]
王 翀,王景华,李冬冬,佘江波. 掺Gd3+ 的LiYF4 ∶Yb3+ /Ho3+ 微米晶体制备以及在防伪中的应用研究 [J]. 光谱学与光谱分析, 2022, 42(11): 3581-3587.
[11]
廖逸民,闫胤洲,王 强,杨立学,潘永漫,邢 承,蒋毅坚. ZnO微米晶的激光制备装置及发光性能研究 [J]. 光谱学与光谱分析, 2022, 42(10): 3000-3005.
[12]
张礼刚,马丽红,赵谡玲,徐 征,杨海军,李晨璞,王 克,刘桂霞,柏永清,沈文梅. 反应温度对Na3 ScF6 ∶Yb/Er纳米晶的发光和形貌的影响 [J]. 光谱学与光谱分析, 2022, 42(10): 3068-3072.
[13]
张晓腾,刘 威,刘海峰,郑尊清,明镇洋,崔雁清,文铭升,尧命发. 不同环境氧浓度下聚甲氧基二甲醚(PODE)喷雾燃烧的羟基光谱分布及其反演重构研究 [J]. 光谱学与光谱分析, 2022, 42(08): 2587-2594.
[14]
胡欣妍,曹龙菲,李金华,李 霜. Eu3+ /Dy3+ 共掺Sr3 Y2 (BO3 )4 荧光粉的发光性质研究 [J]. 光谱学与光谱分析, 2022, 42(07): 2063-2068.
[15]
张雨潇,王 希,陈树果,刘召伟,胡连波. 黄海水体生物发光所致离水辐亮度变化及其与固有光学性质和深度的联系 [J]. 光谱学与光谱分析, 2022, 42(06): 1899-1906.