Abstract：Cr3+:Al2(WO4)3 Crystal was grown from the Na2WO4 solvent system by using the TSSG method. The absorption spectrum shows that there are two strong absorption wideband peaks and one weak absorption peak belonging to Cr3+ ion in the crystal. The peak values of two strong absorption wideband peaks are at 422 and 595 nm, respectively. The values of two weak absorption peaks are at 684 and 663 nm, respectively. The fluorescence spectrum shows that one emission wideband peak ranging from 650 to 820 nm coexists with one stronger emission peak at 680 nm. The peak value of emission wideband is at 740 nm. The crystal field and Racah parameters were calculated, where Dq/B=2.420 indicates that it has an intermediary crystal field. The result shows that Cr3+:Al2(WO4)3 crystal is promising for tunable laser because it not only has the spectral characteristics required for tunable laser crystal but also has the good physicochemical properties.
涂朝阳，朱昭捷，李坚富，王 燕，游振宇，吴柏昌. Cr3+:Al2(WO4)3晶体的生长和光谱特性[J]. 光谱学与光谱分析, 2005, 25(06): 804-807.
TU Chao-yang, ZHU Zhao-jie, LI Jian-fu, WANG Yan, YOU Zhen-yu, WU Bai-chang . Study on the Growth and Spectral Characteristics of Cr3+:Al2(WO4)3 Crystal . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(06): 804-807.
[1] Craig D C, Stephenson N C. Acta Cryst., 1968, B24: 1250. [2] Tanabe Y, Sugano S. J. Japan Phys. Soc., 1954, 9(5): 753. [3] LUO Zun-du, HUANG Yi-dong(罗遵度，黄艺东). Spectrum Physics of Solid State Laser Materials(固体激光材料光谱物理学). Fuzhou: Science and Technology Publishing Company of Fujian Province(福州：福建科学技术出版社), 2003. 120. [4] Andrews L J, Lempicki A, McCollum B C，et al. Phys. Rev. B, 1986, 34: 2735. [5] Caird J A, Payne S A, Stave P R，et al. IEEE J. Quant. Elect., 1988, QE-24: 1077. [6] Huber G, Payne S A, Chase L L，et al. J. Lumin., 1988, 39: 259. [7] TU Chao-yang, ZHU Zhao-jie, LI Jian-fu, HUANG Miao-liang, WU Bai-chang(涂朝阳，朱昭捷，李坚富，黄妙良, 吴柏昌). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2003, 23(4): 669. [8] Kenyon P T，et al. IEEE J. Quantum Electronic, 1982, QE-18(8): 1189. [9] WU Cheng-jiu(邬承就). Journal of Synthetic Crystal(人工晶体学报), 1993, 22(4)：384.