Abstract：For the system of Ce(NO3)2·6H2O and urea solution during homogeneous precipitation method, X-ray diffraction (XRD), infrared spectrum (IR) and especially X-ray photoelectron spectroscopy (XPS) were used to study and characterize the product structure, variety of cerium ion valence, compound surface character and kernel electronic configurations.The results of XRD and IR showed that calcination temperature had a great effect on the cerium ion valence.The products are orthorhombic Ce2O(CO3)2·H2O with valence Ⅲ by using homogeneous precipitation method directly.When heated from the temperature 200 ℃ to 250 ℃, the product of CeO(CO3)2·H2O with valence Ⅵ was finally changed into stable CeO2 with valence Ⅳ.XPS was used to study the surface character and kernel electronic configurations of the three different compounds through fine scanning of O(1s), Ce(3d) and Ce(4d) apices, and the results approved that the compounds with different valences are caused by the different valence electronic configurations of the products.
Key words：Calcination;Cerium ion valence;X-ray photoelectron spectroscopy
梅 燕，闫建平，聂祚仁. 焙烧条件对Ce离子价态影响的XPS研究[J]. 光谱学与光谱分析, 2010, 30(01): 270-273.
MEI Yan, YAN Jian-ping, NIE Zuo-ren. XPS Study on the Influence of Calcination Conditions to Cerium Ion Valence . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(01): 270-273.
[1] Jacques B, Oliveiero L, Renard B, et al.Catalysis Today, 2002, 75: 29. [2] Kaspar J, Fornasiero M, Graziani M.Catalysis Today, 1999, 50: 285. [3] Cambelli P, Gorbo P, Migliardin F.Catalysis Today, 2000, 59: 279. [4] Mori T, Drennan J, Wang Y R, et al.Journal of Thermal Analysis and Calorimetry, 2002, 70: 309. [5] Hoshino T, Kurata Y, Terasaki Y, et al.Journal of Non-Crystalline Solids, 2001, 283: 129. [6] CHEN Shou-chun(陈寿椿).Important Inorganic Chemistry Reaction(重要无机化学反应).Shanghai: Shanghai Science and Technology Press(上海: 上海科技出版公司), 1963. [7] DONG Xiang-ting, HONG Guang-yan, YU De-cai C(董相廷, 洪广言, 于得财).Journal of the Chinese Ceramic Society(硅酸盐学报), 1997, 25(3): 323. [8] YANG Nan-ru(杨南如).Testing Technique of Inorganic Nonmetal Materials(无机非金属材料测试方法).Wuhan: Wuhan University Press(武汉: 武汉工业大学出版社), 2000. [9] MEI Yan, NIE Zuo-ren, WANG Wei(梅 燕, 聂祚仁, 王 为).Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2007, 27(2): 254. [10] Francois L N, Lionel H, Koffi K, et al.J.Phys.Chem., 1998, 92: 2561. [11] Bielanski A, Haber J J.Oxygen in Catalysis.New York: Mareel Dekker, Inc., 1991. [12] Li L, Wei Q, Liu H, et al, Z.Phys.B., 1995, 96: 451. [13] Maiste A, Kikas A, Ruus R, et al.J.of Electron Spectroscopy and Related Phenomena, 1995, 76: 583. [14] Naik I K, Tien T Y.J.Phys.Chem.Solids, 1978, 38: 311. [15] Teterin Y A, Teterin A Y, Lebedev A M, et al.Journal of Electron Spectroscopy and Related Phenomena, 1998, 88: 275. [16] Fever P L, Magnan H, Vogel J, et al.Journal of Electron Spectroscopy and Related Phenomena, 1999, 101: 103, 787. [17] Praline G, Koel B E, Hance R L, et al.Journal of Electron Spectroscopy and Related Phenomena, 1980, 21: 17