Abstract：For Au-ceria catalysts prepared by deposition-precipitation method, the catalytic performance of water gas shift reaction was studied with different La loadings. In the complete doping range, ceria retains with its cubic fluorite structures. XRD, HRTEM and UV-Vis-DRS, studies showed that La doping can improve the activity of Au-ceria catalyst by stabilizing ceria and modifying its morphology. In addition, the test of catalyst stability evaluation also proved that a better stability performance of Au-ceria catalyst can be realized by appropriate La doping. The Au/ CL5.0 sample with 5 at% La doping showed the best performance in WGS reaction.
[1] Myers D J, Krebs J F, Carter J D, et al. Metal/Ceria Water-GasShift Catalysts for Automotive Polymer Electrolyte Fuel Cell Systems, Presentation at American Institute of Chemical Engineers. New Orleans: LA, 2002. [2] Kalhammer F R, Prokopius P R, Roan V P, et al. Status and Prospects of Fuel Cells as Automobile Engines, A Report of the Fuel Cell Technical Advisory Panel. California, 1998. [3] Myers D, Krebs J, Yu S, et al. Water-Gas Shift Catalysts, Reported in 2002 Annual National Laboratory R&D Meeting. Argonne National Laboratory, 2002. [4] ZHANG Feng-li, ZHENG Qi, LIN Xing-yi, et al(张凤利，郑 起, 林性贻，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2007，27(4)：781. [5] ZHAN Ying-ying, CAI Guo-hui, XIAO Yi-hong, et al(詹瑛瑛，蔡国辉，肖益鸿，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2004, 24(8): 914. [6] Ladd M F C，Pahlmer R A. Structure Determination by X-Ray Crystallography. Third Edition. New York：Plenum Press, 1994. 63. [7] Nowick A S. Diffusion in Crystalline Solids. G E Murch, A S Nowich, eds. 1984. 143. [8] Ozawa M, Kato O, Suzuki S. J. Mater. Sci. Lett.，1996, 15: 564. [9] Fu Q, Deng W, Saltsburg H, et al. Appl. Catal. B: Environ.，2005，56：57. [10] Patil S, Seal S, Guo Y, et al. Appl. Phys. Lett.，2006，88: 243110. [11] Sanchez M S, Gazquez J L. J. Catal.，1987，104：120. [12] Claude Binet, Ahmed Badri，Jean-Claude Lavalley. J. Phys. Chem., 1994, 98: 6392.