光谱学与光谱分析
塑料光纤拉曼散射的研究
孙秀平，冯克成，张喜和，谭 勇，张凤东，王兆民
长春理工大学理学院，吉林 长春 130022
Study of Raman Scattering of Plastic Optical Fiber
SUN Xiu-ping,FENG Ke-cheng,ZHANG Xi-he,TAN Yong,ZHANG Feng-dong,WANG Zhao-min
Changchun University of Science and Technology, Changchun 130022, China
摘要 ： 给出了聚甲基丙烯酸甲脂(PMMA)塑料光纤(POF)的一级受激拉曼散射光谱，研究了一级斯托克斯光谱特点，测试了它的阈值，带宽，分析了拉曼光谱的形成机制，并将塑料光纤的拉曼光谱和石英光纤的拉曼光谱进行了比较。
关键词 ：塑料光纤;拉曼散射;斯托克斯光
Abstract ：The first order stimulated Raman scattering (SRS) spectrum of PMMA plastic optical fiber was given, and the characteristic of the first order Stokes spectrum was studied. The threshold and the spectrum width were measured. The formation mechanism of SRS was analyzed, and then the first order Stokes spectrum of plastic optical fiber and that of silica fiber were compared.
Key words ：Plastic optical fiber;Raman scattering;Stokes spectrum
收稿日期: 2004-10-18
修订日期: 2005-01-28
通讯作者:
孙秀平
引用本文:
孙秀平，冯克成，张喜和，谭 勇，张凤东，王兆民. 塑料光纤拉曼散射的研究[J]. 光谱学与光谱分析, 2005, 25(12): 2002-2004.
链接本文:
https://www.gpxygpfx.com/CN/Y2005/V25/I12/2002
[1] ZHANG Yong-qiang, et al(张永强, 等). Journal of Yanshan University(燕山大学学报), 2003, 27(1): 58.
[1]
赖春红，张芝峻，文 靖，曾 诚，张 琦. 表面增强拉曼散射信号长程探测研究进展
[2]
李佳佳，徐大鹏，王子雄，张 彤. 纳米材料的表面增强拉曼散射增强机理研究进展
[3]
潘科宇，朱明尧，王艺蒙，徐 阳，迟明波，吴一辉. 相敏检测调制深度对受激拉曼信号强度及信噪比影响研究
[4]
孙志明，李 辉，冯奕博，高钰航，裴佳欢，常 莉，罗云敬，邹明强，王 聪. 单位点表面电荷调控提升拉曼检测灵敏度
[5]
尹雄翼，石元博，王胜君，焦仙鹤，孔宪明. 基于ML-PCA-BP模型的多环芳烃拉曼光谱定量分析
[6]
孙 楠，谭红琳，张正东，任 翔，周 燕，刘建琪，蔡晓明，蔡金明. 碳纳米管掺杂聚丙烯腈/铜室温环化为石墨的拉曼光谱分析及形成机制研究
[7]
焦若男，刘 琨，孔繁艺，王 婷，韩 雪，李泳江，孙长森. 近海微塑料含量的相干反斯托克斯拉曼光谱成像研究
[8]
王子雄,徐大鹏*,张一帆,李佳佳. 表面增强拉曼散射检测分析物分子的研究进展
[9]
付兴虎,王振兴,李佳轩,马双玉,付广伟,金 娃,毕卫红,董艳华. 纳米银溶胶和微腔型光纤SERS基底的制备及其性能比较
[10]
. 高性能三维纳米结构SERS芯片设计、批量制备与痕量汞离子检测
[11]
. 小尺寸样品CARS图像信号分布实验研究
[12]
. 微腔型银修饰光纤SERS探针的制备及性能研究
[13]
. 基于超疏水高黏附结构的痕量农药分子现场检测SERS基底研究
[14]
. Na2 CO3 的高压拉曼光谱研究
[15]
. 纳米结构表面形貌成型机理及其对石墨烯拉曼光谱的影响