Measurement of Triglyceride Content of Resin in Masson Pulp by UV Spectral Method
SHI Hai-qiang1, 2,HE Bei-hai1
1. State Key Lab of Pulp and Paper Engineering, South China University of Technology, Guangzhou 510640, China 2. Faculty of Chemical Engineering and Materials, Dalian Institute of Light Industry, Dalian 116034, China
Abstract：Pitch deposit is one of the most troublesome problems for the paper mills in South China that use the masson pine as a raw material to make paper. The triglyceride has been identified as the main composition accounting for pitch problem. in order to set down effective pitch control scheme, the triglyceride content in papermaking process must be measured quantitatively. A method to measure the content of triglyceride in masson wood pulp was developed based on UV spectrophotometer in the present work. The UV spectrogram and characteristic peak location of standard glycerol trioleate as well as the effect of measuring time on absorbency were discussed. The results showed that at 412 nm the relation between absorbency and consistency of glycerol trioleate was linear and the pertinent coefficient reached 0.971 in the range of reagent dosage and consistency in this experiment. The absorbency decreased linearly with measuring time and the pertinent coefficient reached 0.990 2. The results of reproductive experiment showed that the recoveries were 98%-104% and the accuracy was 1.27%-4.03% for the samples in consistency 1.25-0.50 g·L-1. With this method, the content of triglyceride in hexane extractive of masson TMP and acid SP were measured respectively. The degradative effect of triglyceride before and after enzyme treatment for masson wood pulp was also evaluated. The results showed that the triglyceride content was relatively high, about 50% both in the total extractive of masson TMP and acid SP. After enzyme treatment, the content of triglyceride in masson TMP and acid SP was reduced by 46.31% and 35.55% respectively.
[1] CHEN Shi-guang(陈世光). Paper Science and Technology(造纸科学与技术)，2001，20(6)：78. [2] HUANG Min-li, GAN Yi(黄闽荔，甘 毅). China Pulp and Paper Industry(中华纸业)，2003，24(12)：26. [3] LI Sheng-shu(李胜树). China Pulp and Paper Industry(中华纸业)，2003，24(7)：32. [4] QIN Meng-hua, CHEN Jia-xiang, YU Jia-lan(秦梦华, 陈嘉翔, 余家鸾). Transactions of China Pulp and Paper(中国造纸学报), 1997，12(增刊)：29. [5] Ian D Suckling, Richard Mede. Appita J.，1990，43(1)：77. [6] Suvi Pietartnen, Stefan Willfor, Bjarne Holmbom. Appita J., 2004, 57(2): 146. [7] Bruce B Sithole. Appita J., 1992, 45(4): 260. [8] Kurt fischer. Tappi J., 1992, 75: 130. [9] Fujita Y. Tappi J., 1992, 75: 117. [10] Sundberg K, Pettersson C, Eckerman C, et al. Journal of Pulp and Paper Science, 1996, 22(7): 248. [11] XU Wen-lin, SHA Ou, QIAN Jun-hong, et al(许文林, 沙 鸥, 钱俊红, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2003，23(5)：933.