Research on Preparation Process Optimization and Surface Enhanced Raman Spectroscopy (SERS) of Graphene-Silver Nanoparticle Composites
GONG Tian-cheng1,2, ZHU Yong1*, WANG Xin-yu1,3, WANG Ning1, ZHANG Jie1
1. Key Laboratory of Optoelectronic Technology & System, Education of Ministry, Chongqing University, Chongqing 400044, China
2. State Key Laboratory of Optical Technologies on Nano-Fabrication and Micro-Engineering, Institute of Optics and Electronics, Chinese Academy of Sciences, Chengdu 610209, China
3. Chongqing Engineering Research Center of Graphene Film Manufacturing, Chongqing 401329, China
Abstract:Based on general preparation process of surface-enhanced Raman scattering (SERS) substrate of graphene-silver nanoparticles composites, the coupling agent has been used to improve the uniformity of silver nanoparticles adsorbed on the target substrates; bilayer of polymethylmethacrylate (PMMA) has been used to transfer graphene in order to reduce the defects of graphene; annealing treatment has been used to reduce the Raman background noise and improve the contrast of Raman spectra. The experimental results indicate that using the optimized preparation process can improve the uniformity of SERS substrate. The contrast of graphene Raman signal at G and 2D peak increased by 54.9% and 64.3%, respectively. The goodness of fit (R2) on the relationship between Raman intensities of Rhodamine 6G (R6G, at 774 and 1 363 cm-1) and concentration achieved 0.997 5 and 0.986 7, respectively.
Key words:Raman spectra; Graphene; Silver nanoparticles; Composites; Prepar process
龚天诚,朱 永,王鑫羽,王 宁,张 洁. 石墨烯-银纳米颗粒复合结构制备工艺优化及表面增强拉曼光谱特性[J]. 光谱学与光谱分析, 2018, 38(11): 3321-3327.
GONG Tian-cheng, ZHU Yong, WANG Xin-yu, WANG Ning, ZHANG Jie. Research on Preparation Process Optimization and Surface Enhanced Raman Spectroscopy (SERS) of Graphene-Silver Nanoparticle Composites. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(11): 3321-3327.
[1] Nair R R, Blake P, Grigorenko A N, et al. Science, 2008, 320(5881): 1308.
[2] Geim A K, Novoselov K S. Nature Materials, 2007, 6(3): 183.
[3] Xie L, Ling X, Fang Y, et al. Journal of the American Chemical Society, 2009, 131(29): 9890.
[4] WU Juan-xia, XU Hua, ZHANG Jin(吴娟霞, 徐 华, 张 锦). Acta Chimica Sinica(化学学报), 2014, 72(3): 301.
[5] Moskovits M. Journal of Raman Spectroscopy, 2005, 36(6-7): 485.
[6] Xu H, Bjerneld E J, Kll M, et al. Physical Review Letters, 1999, 83(21): 4357.
[7] Kang L, Chu J, Zhao H, et al. Journal of Materials Chemistry C, 2015, 3(35): 9024.
[8] Li X, Li J, Zhou X, et al. Carbon, 2014, 66: 713.
[9] Gong T, Zhu Y, Zhang J, et al. Carbon, 2015, 87: 385.
[10] Gong T, Zhang J, Zhu Y, et al. Carbon, 2016, 102: 245.
[11] Zhang S G, Zhang X W, Liu X, et al. Applied Physics Letters, 2014, 104(12): 121109.
[12] Lu R, Konzelmann A, Xu F, et al. Carbon, 2015, 86: 78.
[13] Lee P C, Meisel D. Journal of Physical Chemistry, 1982, 86: 17(17): 3391.
[14] Rycenga M, Cobley C M, Zeng J, et al. Chemical Reviews, 2011, 111(6): 3669.
[15] Pinkhasova P, Yang L, Zhang Y, et al. Langmuir, 2012, 28(5): 2529.
[16] Li X, Cai W, An J, et al. Science, 2009, 324(5932): 1312.
[17] Li X, Zhu Y, Cai W, et al. Nano Letters, 2009, 9(12): 4359.
[18] Barin G B, Song Y, Gimenez I D F, et al. Carbon, 2015, 84: 82.
[19] Shen X S, Wang G Z, Hong X, et al. Physical Chemistry Chemical Physics, 2009, 11(34): 7450.
[20] Daniel M C, Astruc D. Chemical Reviews, 2004, 104(1): 293.
[21] Ding G, Xie S, Liu Y, et al. Applied Surface Science, 2015, 345: 310.