%A WEI Jian;SHEN Chang-yu*;SUN Yu-huan;ZHANG Hong;WANG Le*;LI Chen-xia
%T Preparation and Luminescent Properties of Blue Emitting Phosphor of Sr3(PO4)2∶Eu2+ for White LED
%0 Journal Article
%D 2015
%J SPECTROSCOPY AND SPECTRAL ANALYSIS
%R 10.3964/j.issn.1000-0593(2015)11-3028-04
%P 3028-3031
%V 35
%N 11
%U {https://www.gpxygpfx.com/CN/abstract/article_8014.shtml}
%8 2015-11-01
%X A series of Sr3(PO4)2∶Eu2+ blue phosphors were synthesized by high temperature solid state method under N2-H2 reducing atmosphere. The crystal structures, excitation and emission spectra were characterized by X-ray diffraction (XRD) and Photoluminescence (PL), respectively. The results show that the Sr3(PO4)2∶Eu2+ phosphor can be efficiently excited by the wavelengths ranging from 310 to 390 nm, and the excitation peak wavelength locates at 359 nm. A wide emission spectrum (~150 nm, originating from the 4f65d1→4f7 of the Eu2+) with a peaking wavelength of 438 nm was obtained. Through the Gaussian fitting, we found that the emission band formed by two luminescence centers(430 and 459 nm), which indicated that the Eu2+ occupied two different Sr2+ sites in the substrate of Sr3(PO4)2. As the Eu2+ doping concentration is 7%, the maximum luminous intensity was obtained. With the increasing of the doping concentration of the Eu2+, the concentration quenching effect occurred, and the emission peak wavelength has a red shift. The PL intensity of the Sr3(PO4)2∶Eu2+ phosphor is about 1.3 times than that of the blue emitting phosphor BaMgAl10O17∶Eu2+(BAM) which means that it is a promising candidate for the blue phosphor material for white LED.