%A ZHANG Jing-yu;BAI Zhi-min*;ZHAO Dong %T Raman and Infrared Spectrograms of Organic Borate Intercalated Hydrotalcite %0 Journal Article %D 2013 %J SPECTROSCOPY AND SPECTRAL ANALYSIS %R 10.3964/j.issn.1000-0593(2013)03-0704-05 %P 704-708 %V 33 %N 03 %U {https://www.gpxygpfx.com/CN/abstract/article_6191.shtml} %8 2013-03-01 %X The pattern of X-ray diffraction, the Raman and infrared spectra of organic borate intercalated hydrotalcite were discussed. The well crystallized zinc-aluminum layered double hydroxides (Zn-Al LDHs) intercalated by carbonate ions and borate ions were respectively prepared by co-precipitation method. Patterns of X-ray diffraction showed that the (003) reflection of borate-LDHs was sharp and symmetric and shifted to lower angle than that of carbonate-LDHs. The gallery height of borate-LDHs increased from 0.28 nm to 0.42 nm after intercalation, indicating that interlayered carbonate ions were substituted by borate anions. The Raman and IR spectra showed that specific bands of carbonate ions in the borate-LDHs disappeared, but with the presence of B3O3(OH)-4,B4O5(OH)2-4 and B(OH)-4 in the interlayer galleries. The hydroxide interlayer anions had a significant influence on the band positions in Raman and infrared spectra of modes related to the hydroxyl group. Our results indicate that single phase and pure borate-pillared LDHs can be obtained using tributyl orthoborate as intercalating agents,and the change in the structure and nature of hydrotalcite can be detected precisely by Raman spectroscopy.