光谱学与光谱分析 |
|
|
|
|
|
Study on the Interface Characteristics of Cemented Carbide after Stripping Ti Department Coatings |
YAN Qiang1, 2, LIANG Zheng1, SONG Hui-jin3,WU Tao2, WU Jun2 |
1. School of Mechatronic Engineering, Southwest Petroleum University, Chengdu 610500, China 2. Sichuan Jinxing Compressor Manufacturing Co., Ltd., Chengdu 611731, China 3. College of Industrial and Manufacturing, Chengdu University,Chengdu 610106, China |
|
|
Abstract TiAlN Coatings were stripped by chemical method, which were deposited on YW2 Alloy by arc ion plating. The surface morphology and composition of the cemented carbide after stripping TiAlN coatings by chemistry method were analyzed. It was found that TiAlN coatings on the cemented carbide substrates could be removed by being taken in 30% of hydrogen peroxide and potassium oxalate in alkaline mixed solution(VNaOH solution∶V30%H2O2∶VCOOK solution=1∶1∶1)at 45 ℃ for 45 minutes. The surface of the cemented carbide substrate was bright,and the color was the same as that before depositing TiAlN coatings. The surface of the substrate after removing was studied by X-ray photoelectron spectrum (XPS). The results showed that binding energies of the W element and the main peak of N element on the substrate surface were much close to the criterion binding energy in the XPS data-base; and the valence of the element on the YW2 alloy changed little. The Al, Ti and N elements diffusing into the superficial zone of the sample during the coating depositing process made their contents increase and the band energy location offset after stripping the coating. TiN and AlN were formed, which benefit to increase the film-substrate cohesion during re-preparing coatings. The influence of stripping solution on the corrosion degree of cemented carbide substrate was small.
|
Received: 2014-08-21
Accepted: 2014-11-24
|
|
Corresponding Authors:
YAN Qiang
E-mail: yhd1210@163.com
|
|
[1] Simranpreet Singh Gill, Jagdev Singh, Harpreet Singh. International Journal of Machine Tools & Manufacture, 2011, 51: 25. [2] Shum P W, Li K Y, Zhou Z F. Surface and Coatings Technology, 2004, 185: 245. [3] Takaoka H, Nakamura E, Oshika T, et al. Surface and Coatings Technology, 2004, (177-178): 306. [4] WU Zi-jun(吴子军). China Patent(中国专利), CN169635OA, 2005. [5] Padture N P, Gell N, Jordan E H. Science, 2002, 296(5566): 280. [6] JIE Nian-suo, WANG Jin(解念锁, 王 瑾). China Tungsten Industry(中国钨业), 2006, 21(3): 4. [7] Sundar M, Kamara A M, Mativenga P T, et al. Surface and Coatings Technology, 2010, 2004(16-17): 2539. [8] WU Zi-jun, LIU Jian(吴子军, 刘 坚). Non-ferrous Metals Recycling and Utilization(有色金属再生与利用), 2005, 42(2):19. [9] CAI Yan, LU Feng, LI Jian-ping(蔡 妍,陆 峰,李建平). Rare Metal Materials and Engineering(稀有金属学报),2008, 38(1): 152. [10] SONG Hui-jin, YAN Qiang(宋慧瑾, 鄢 强). Chinese Journal of Vacuum Science and Technology(真空科学与技术学报), 2013, 33(1): 106. [11] JIA Heng, ZHANG Jun(贾 恒, 张 钧). Chinese Journal of Vacuum Science and Technology(真空科学与技术学报), 2012, 32(12): 1067. [12] Inoue A, Yanngata H, Masumoto T. Material Transaction JIM, 1993, 34: 548. [13] ZHANG Xing-hong, LI Ya-hui, HAN Jie-cai, et al(张幸红, 李亚辉, 韩杰才, 等). Acta Materiae Compositae Sinica(复合材料学报), 2001, 18(4): 87. [14] ZHANG Li, CHEN Shu, HUANG Fang-jie, et al(张 立, 陈 述, 黄方杰, 等). Cemented Carbide(硬质合金), 2011, 28(5): 271. |
|
|
|