Effect of N+(N=Li, Na, K) on the Spectra of M3(M=Ca, Sr, Ba)Y2(BO3)4∶Eu3+ Luminescent Phosphor |
LI Pan-lai1,WANG Zhi-jun1*,GAO Hui-ying2,YANG Zhi-ping1 |
1. College of Physics Science & Technology, Hebei University, Baoding 071002, China 2. North China Electric Power University Science & Technology College, Baoding 071051, China |
|
|
Abstract The M3(M=Ca, Sr, Ba)Y2(BO3)4∶Eu3+ red phosphor was synthesized by firing twice at 800 and 1 050 ℃ each for 4 h and 4 h in air, respectively. Y2O3(99.9%), Eu2O3(99.9%), H3BO3(99.9%), CaCO3(99.9%), SrCO3(99.9%), BaCO3(99.9%), Li2CO3(99.9%), Na2CO3(99.9%) and K2CO3(99.9%) were used as starting materials, and the doping Eu3+ concentration was 3 mol%. The excitation spectrum was measured by a SHIMADZU RF-540 ultraviolet spectrophotometer. The emission spectrum was measured by a SPEX1404 spectrophotometer. All the luminescence characteristics of the phosphors were investigated at room temperature. The emission spectrum of M3(M=Ca, Sr, Ba)Y2(BO3)4∶Eu3+ phosphor exhibited a 613 nm red emission corresponding to the electric dipole 5D0-7F2 transition of Eu3+ under 365 nm excitation. The excitation spectrum for 613 nm indicates that the phosphor can be effectively excited by ultraviolet (UV) (254, 365 and 400 nm) and blue (470 nm) light. The effect of Li+,Na+ and K+ on the excitation and emission spectra of M3(M=Ca, Sr, Ba)Y2(BO3)4∶Eu3+ phosphor was studied. The results show that the location of the excitation and emission spectrum of M3(M=Ca, Sr, Ba)Y2(BO3)4∶Eu3+ phosphor was not influenced by Li+,Na+ and K+. However, the excitation and emission spectrum intensities were greatly influenced by Li+,Na+ and K+,and the emission peak intensities were all enhanced. Under the condition of the same Li+,Na+ and K+ concentration, the emission peak intensities of M3(M=Ca, Sr, Ba)Y2(BO3)4∶Eu3+ phosphor were compared, and the result shows that the accretion effect of doping Li+ is the best. The effect of Li+ concentration on the emission peak intensity of Sr3Y2(BO3)4∶Eu3+ phosphor was studied. The results show that the emission peak intensity firstly increased with the increasing Li+ concentration, then decreased, and reached the maximum value at 5 mol% Li+,and the maximum value is about twice as much as the Li-undoped one.
|
Received: 2007-09-03
Accepted: 2007-12-08
|
|
Corresponding Authors:
WANG Zhi-jun
E-mail: wangzhijunmail@yahoo.com.cn
|
|
[1] LIU Hong-li, HE Da-wei, SHEN Fang(刘红利, 何大伟, 沈 芳). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(10): 1790. [2] ZHAO Su-ling, HOU Yan-bing, XU Zheng, et al(赵谡玲, 侯延冰, 徐 征, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(4): 597. [3] SHEN Fang, HE Da-wei, LIU Hong-li, et al(沈 芳, 何大伟, 刘红利, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(7): 1195. [4] SHI Yan-ning, HE Da-wei, LIANG Zhong-yi(史艳宁, 何大伟, 梁忠益). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(5): 809. [5] WANG Xin-zi, WANG Yong-sheng, SUN Li, et al(王欣姿, 王永生, 孙 力, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(3): 399. [6] CHANG Jian-jun, HUANG Shi-hua, PENG Hong-shang, et al(常建军, 黄世华, 彭洪尚, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(2): 231. [7] Kim J S, Jeon P E, Choi J C, et al. Applied Physics Letters, 2004, 84(15): 2931. [8] Lakshminarasimhan N, Varadaraju U V. J. Electrochemical Society, 2005, 152(9): H152. [9] Park K P, Lim M A, Choi K J, et al. J. Materials Science, 2005, 40: 2069. [10] Park J K, Choi K J, Kim K N, et al. Applied Physics Letters, 2005, 87: 031108-1. [11] Kim J S, Lim K T, Jeong Y S, et al. J. Solid State Communication, 2005, 135: 21. [12] Park J K, Choi K J, Park S H, et al. J. Electrochemical Society, 2005, 152(8): H121. [13] GUO Feng-yu, HUANG Xiao-hua, YAO Guang-qing(郭凤瑜, 黄晓华, 姚光庆). Chinese Journal of Inorganic Chemistry(无机化学学报) 1995, 11(2): 109. [14] LI Qi-hua, LIU Li-min, LEI Chun-hua, et al(李其华, 刘利民, 雷春华, 等). Hunan Nonferrous Metals(湖南有色金属), 2004, 20(1): 29. [15] PENG Yi-an, GUO Feng-yu(彭夷安, 郭凤瑜). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 1994, 14(6): 15. [16] Yang C H, Pan Y X, Zhang Q Y. Materials Science and Engineering B, 2007, 137: 195. [17] Sun L D, Qian C, Liao C S, et al. Solid State Communications, 2001, 119: 393. [18] Tian L H, Mho S I. Solid State Communications, 2003, 125: 647. [19] Mckittrick J, Shea L E, Bacalski C F, et al. Displays, 1999, 19: 169. [20] Hyeon K A, Byeon S H, Park J C, et al. Solid State Communication, 2000, 115: 99. |
[1] |
YU Hao-zhang, WANG Fei-fan, ZHAO Jian-xun, WANG Sui-kai, HE Shou-jie*, LI Qing. Optical Characteristics of Trichel Pulse Discharge With Needle Plate
Electrode[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3041-3046. |
[2] |
LIU Hong-wei1, FU Liang2*, CHEN Lin3. Analysis of Heavy Metal Elements in Palm Oil Using MP-AES Based on Extraction Induced by Emulsion Breaking[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3111-3116. |
[3] |
LIU Pan1, 2, 3, DU Mi-fang1*, LI Bin1, LI Jing-bin1, ZENG Lei1, LIU Guo-yuan1, ZHANG Xin-yao1, 4, ZHA Xiao-qin1, 4. Determination of Trace Tellurium Content in Aluminium Alloy by
Inductively Coupled Plasma-Atomic Emission Spectrometry Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3125-3131. |
[4] |
TIAN Fu-chao1, CHEN Lei2*, PEI Huan2, BAI Jie-qi1, ZENG Wen2. Diagnosis of Emission Spectroscopy of Helium, Methane and Air Plasma Jets at Atmospheric Pressure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(09): 2694-2698. |
[5] |
ZHANG Zhi-fen1, LIU Zi-min1, QIN Rui1, LI Geng1, WEN Guang-rui1, HE Wei-feng2. Real-Time Detection of Protective Coating Damage During Laser Shock Peening Based on ReliefF Feature Weight Fusion[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2437-2445. |
[6] |
LI Zhi-xiong1, 2, LU Qian-shu1, ZHANG Lian-kai1, 2*, ZHANG Song1, YANG Wan-tao1, LI Can-feng1, FENG Jun1, LIU Zhen-chao1. Study on the Determination of Silver, Boron, Molybdenum, Tin in Geochemical Samples by the Method of Solid Sampling Carrier Distillation Atomic Emission Spectrum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(07): 2132-2138. |
[7] |
SI Yu1, LIU Ji1*, WU Jin-hui2, ZHAO Lei1, YAN Xiao-yan2. Optical Observation Window Analysis of Penetration Process Based on Flash Spectrum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 718-723. |
[8] |
YU Cheng-hao, YE Ji-fei*, ZHOU Wei-jing, CHANG Hao*, GUO Wei. Characteristics of the Plasma Plume and Micro-Impulse Generated by
Irradiating the Aluminum Target With a Nanosecond Laser Pulse at
Oblique Incidence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 933-939. |
[9] |
WANG Wei, WANG Yong-gang*, WU Zhong-hang, RAO Jun-feng, JIANG Song, LI Zi. Study on Spectral Characteristics of Pulsed Argon Vacuum Dielectric
Barrier Discharge[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 455-459. |
[10] |
LI Ru, YANG Xin, XING Qian-yun, ZHANG Yu. Emission Spectroscopy Study of Remote Ar Plasma[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 394-400. |
[11] |
HAO Jun1, WANG Yu2, LIU Cong2, WU Zan2, SHAO Peng2, ZU Wen-chuan2*. Application of Solution Cathode Glow Discharge-Atomic Emission Spectrometry for the Rapid Determination of Calcium in Milk[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(12): 3797-3801. |
[12] |
FU Hong-bo1, WU Bian1, WANG Hua-dong1, ZHANG Meng-yang1, 2, ZHANG Zhi-rong1, 2*. Quantitative Analysis of Li in Lithium Ores Based on Laser-Induced Breakdown Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3489-3493. |
[13] |
YANG Kun, CHEN Lei*, CHENG Fan-chong, PEI Huan, LIU Gui-ming, WANG Bao-huai, ZENG Wen. Emission Spectroscopy Diagnosis of Air Gliding Arc Plasma Under
Atmospheric Pressure Condition[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3006-3011. |
[14] |
HU Xuan1, CHENG Zi-hui1*, ZHANG Shu-chao2, SHI Lei2. Matrix Separation-Determination of Rare Earth Oxides in Bauxite by
Inductively Coupled Plasma-Atomic Emission Spectrometry[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3130-3134. |
[15] |
LIU Pan1, 2, LI Jing-bin1, ZHANG Jian-hao1, ZHANG Yi1, CHANG Guo-liang1, HE Peng-fei1, ZHANG Bin-bin1, ZHANG Xin-yao1, 3. Determination of Phosphorus in Welding Flux by Inductively Coupled Plasma Atomic Emission Spectrometry With Ultrasonic Assisted
Hydrochloric Acid Extraction[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(09): 2824-2829. |
|
|
|
|