| Preparation and Characterization of Wood/Methylolurea Composite with In-Situ Polymerization |
| WU Guo-feng, LANG Qian, CHEN He-yu, JIANG Yi-fei, PU Jun-wen* |
| College of Material Science and Technology, Beijing Forestry University, Beijing 100083, China |
|
|
|
|
Abstract Wood/methylolurea composite was prepared with the in-situ polymerization. The green timber with high moisture content was impregnated by a pulse-dipping machine and then was dried in a hot-press drying kiln. The cross-linking reaction was taken under the heat treatment between the wood modifier and the wood composition, including cellulose, hemicelluloses, and lignin. The chemical composition was analyzed according to the Chinese standard, including X-ray photoelectron spectroscopy (XPS), nuclear magnetic resonance (NMR) and energy dispersive analysis of X-rays (EDXA). The changes in chemical composition of modified wood and carbon and nitrogen element were disused in the research. The results showed that the content of water extraction and benzene alcohol extraction increased 187.43% and 230.87% respectively compared with the natural wood, while the lignin and holocellulose decreased 26.55% and 26.39% respectively. XPS showed that the concentrations of O and C atoms increased 9.4% and N element content increased 137.2%. 13C-NMR analysis showed that chemical reaction of the hydroxyl methyl urea with the hydroxyl in timber structure took place, with the reduction of hydroxyl content and increase in ether bond content. EDXA showed that the processing method can get impregnated modification wood and nitrogen element is evenly distributed in wood cell walls and intercellular space.
|
|
Received: 2011-01-23
Accepted: 2011-05-10
|
|
|
|
Corresponding Authors:
PU Jun-wen
E-mail: jwpu@bjfu.edu.cn
|
|
[1] Forest Products Laboratory. Wood Handbook-Wood as Engineering Materials. Madison, WI: U. S Forest Products Laboratory, 1999. 463.
[2] Rowell R M, Banks W. Water Repellency and Dimensional Stability of Wood. Madison, WI: U. S Forest Products Laboratory, 1985. 24.
[3] LI Jian(李 坚). Wood Science(木材科学). Beijing：Higher Education Press(北京：高等教育出版社), 2002.
[4] Gao Zhenhua, Li Dong. J. Appl. Sci., 2007, 104: 2980.
[5] YANG Xi-kun, DU Guan-ben, QIAN Tian-cai, et al(杨喜昆, 杜官本, 钱天才, 等). J. Instrument Analysis(分析测试学报), 2003, 22: 5.
[6] Roger M Rowell. Chemical Modification of Wood. In: Handbook on Wood and Cellulosic Materials. Chapter 15, 1991. 703.
[7] QIAN jun, YE Liang-ming, WANG Guo-du(钱 俊, 叶良明, 王国杜). China Wood Industry(木材工业), 2001, 15(2): 14.
[8] Glazkov S S, Biryukova I P. J. Appl. Chem., 2005, 78: 673.
[9] Smulski S, Cté W A. Wood Sci. Tech., 1984, 18: 59.
[10] FANG Gui-zhen(方桂珍). Wood Functional Modification(木材功能性改良). Beijing：Chemical Industry Press(北京：化学工业出版社), 2008.
[11] PU Jun-wen, WU Guo-feng, JIANG Yi-fei(蒲俊文, 武国峰, 姜亦飞). China Patent(中国专利), 101549508, 2009.
[12] PU Jun-wen, WU Guo-feng, JIANG Yi-fei(蒲俊文, 武国峰, 姜亦飞). China Patent(中国专利), 101618559, 2009.
[13] PU Jun-wen, WU Guo-feng, JIANG Yi-fei(蒲俊文, 武国峰, 姜亦飞). China Patent(中国专利), 101531018, 2009.
[14] WU Guo-feng, JIANG Yi-fei, ZHANG Hao，et al. Advanced Materials Research, 2010, 129-131: 46.
[15] LI Jian(李 坚). Wood Spectrum(木材波谱学). Beijing：Science Press(北京: 科学出版社), 2003.
[16] Wu G F, Lang Q，Qu P，et al. BioResources, 2010, 5: 2581.
[17] Kono H, Numata Y, Nagai N, et al. Carbohydrate Research, 1999，322: 256. |
| [1] |
YUE Kong, LU Dong, SONG Xue-song. Influence of Thermal Modification on Poplar Strength Class by Fourier Infrared Spectroscopy Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 848-853. |
| [2] |
GUO Yong1, ZHENG Yu-ying2*, LONG Hai1, GE Liang1, LI Feng1 . Intercalation of Polystyrene in Kaolin via in-situ Polymerization [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(01): 99-102. |
| [3] |
WU Guo-feng, JIANG Yi-fei, SONG Shu-ping, QU Ping, YAO Sheng, PU Jun-wen* . Preparation and Properties of Wood/Modified UF Prepolymer Composite Materials [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(04): 1083-1086. |
| [4] |
LI Jie1,XU Bing-she2,LI Ying-chun1,XIE Jiang-bo1 . Spectral Analysis and Photoluminescence Properties of Eu-Tb Codoped Polymer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(04): 891-895. |
| [5] |
ZHENG Yu-ying1,PENG Cao2, SUN Rui-qing1, FU Ming-lian1, WANG Can-yao1 . Study on the Modification of Short Chain Phoshate Ammonium Salt of Bentonites [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(10): 1603-1605. |
| [6] |
ZHENG Yu-ying，ZHANG Han-hui，CAI Wei-long, FU Ming-lian, WANG Liang-en* . Preparation and Properties of Organobentonites [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(01): 62-64. |
|
|
|
|