| Studies on the Anomalous IR Properties of CoPt Nanorods |
| ZHOU Xin-wen1*, ZHANG Rong-hua1, JIANG Yan-xia2, SUN Shi-gang2* |
1. Department of Chemistry, College of Chemistry and Life Science, China Three Gorges University, Yichang 443002, China
2. State Key Laboratory for Physical Chemistry of Solid Surfaces, Department of Chemistry, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, China |
|
|
|
|
Abstract One-dimensional CoPt nanorods were obtained through the galvanic displacement reaction and chemical reduction. The average diameter of the nanorods was measured to be about 166.3 nm and the length was mostly between 1.0 and 5.0 μm obtained from the scanning electron microscopy (SEM) measurement. The IR optical properties of the CoPt nanorods and bulk Pt were investigated by in situ FTIR reflection spectroscopy employing CO adsorption as probe reaction at the solid/gas interface. The results of in situ FTIR indicated that bulk Pt shows a normal IR optical property and the CoPt nanorods display abnormal infrared effects (AIREs). The authors can obtain the same results whether the CoPt nanorods were loaded on glassy carbon (GC) or Au substrates. These results demonstrated that the AIREs were generated mainly by CoPt nanorods and the influence of the substrate materials can be neglected. The study confirmed that one-dimensional CoPt nanorods show AIREs, and throw a new sense to comprehend the anomalous IR properties observed on low-dimensional nanomaterials.
|
|
Received: 2010-08-11
Accepted: 2011-01-28
|
|
|
|
Corresponding Authors:
ZHOU Xin-wen,SUN Shi-gang
E-mail: sgsun@xmu.edu.cn
|
|
[1] Wang Y G, Wang Y Q, Ren J W, et al. J. Solid State Chem., 2010, 183: 277.
[2] Lee W R, Piao L H, Park C H, et al. J. Colloid Interface Sci., 2010, 342: 198.
[3] Hartstein A, Kirtley J R, Tsang J C. Phys. Rev. Lett., 1980, 45: 201.
[4] Osawa M. Bull. Chem. Soc. Jpn., 1997, 70: 2861.
[5] Lu G Q, Sun, S G. Cai L R. et al. Langmuir, 2000, 16(2): 778.
[6] Orozco G, Gutierrez C. J. Electroanal. Chem., 2000, 484(1): 64.
[7] Bjerke A E, Griffiths P R, Theiss W. Anal. Chem., 1999, 71: 1359.
[8] Zhou Y, Uchida H, Watanabe M. Langmuir, 1999, 15: 8757.
[9] Kroner M, Govorov A O, Remi S. et al. Nature, 2008, 451(17): 311.
[10] Chen W, Sun S G, Zhou Z Y, et al. J. Phys. Chem. B, 2003, 107: 9808.
[11] JIANG Yan-xia, CHEN Wei, LIAO Hong-gang, et al(姜艳霞，陈 卫，廖宏刚，等). Chin. Sci. Bull.(科学通报)，2004，49(14)：1363.
[12] Zhou X W, Zhang R H, Zeng D M. et al. J. Solid State Chem., 2010，183: 1340.
[13] Oritz R, Cuesta A, Márquez O P, et al. J. Electroanal. Chem., 1999, 465: 234.
[14] Pecharromán C, Cuesta A, Gutierrez C. J. Electroanal. Chem., 2004, 563: 91.
[15] Jiang Y X, Weng W Z, Si D, et al. J. Phys. Chem. B, 2005, 109: 7637.
[16] Su Z F, Sun S G, Wu C X, et al. J. Chem. Phys., 2008, 129: 44707. |
| [1] |
HAO Hua-hua1,2, YUAN Hui1,2, XU Guang-tong1,2*, XIANG Yan-juan1,2, MA Ai-zeng1,2. In Situ FTIR Study of CO Adsorption on Pt-Sn/Al2O3 Reforming Catalyst[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(03): 761-764. |
| [2] |
Qiherima1, 3，YUAN Hui2，ZHANG Yun-hong1，LI Hui-feng2，XU Guang-tong2* . In Situ FTIR and XPS Study on Selective Hydrodesulfurization Catalyst of FCC Gasoline [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(07): 1752-1757. |
| [3] |
YUAN Hui,SUN Shu-ling,ZHENG Ai-guo,XU Guang-tong*. In-situ FTIR Study of CO Adsorption on Co-Mo/Al2O3 Hydrodesulphurization Catalysts[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(09): 2044-2047. |
| [4] |
JIANG Zhi1 , YUAN Kai-jun1,LI Shu-fen1*,CHOW W K2 . Study of FTIR Spectra and Thermal Analysis of Polyurethane[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(04): 624-628. |
| [5] |
SUN Shi-gang, GONG Hui, ZHOU Zhi-you, CHEN Sheng-pei, CHEN You-jiang, SI Di, LI Jun-tao . Solid/Liquid Interfacial In Situ IR Microscope and Step-Scan Time-Resolved FTIR Spectroscopy and Applications in Studies of Nanomaterials[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(04): 431-433. |
|
|
|
|