Effect of Temperature and Applied Voltage on the Recombination Efficiency in Double Layer Organic Light Emitting Diodes |
XU Xue-mei1, 2, PENG Jing-cui1, LI Hong-jian1, QU Shu1, ZHAO Chu-jun1 |
1. Department of Applied Physics, Hunan University, Changsha 410082, China 2. School of Physics Science and Technology, Central South University, Changsha 410083, China |
|
|
Abstract In this paper, the theoretical model of recombination was presented and the effect of temperature and applied voltage on the recombination efficiency was investigated in double layer organic light-emitting diodes: ITO/PPV/PBD/Ca. At lower applied voltage, two peaks have been observed in the curve of recombination efficiency vs. temperature. With increasing voltage, the two peaks shifted toward each other, and at voltage around 9 V the two peaks converged. These phenomena were attributed to the excited deep and shallow trap levels and the change of recombination zone. In the Frenkel exciton model,the temperature dependence of the quantum efficiency depended on the carriers mobilities and carriers densities.The carriers mobilities increased with decreasing temperature, while the carriers densities decreased with decreasing temperature. Therefore, a peak in the curve of quantum efficiency vs. temperature was expected in the model. The high-temperature peak originated due to radiative recombination of the deep trap levels, but the low-temperature peak due to shallow ones. On the other hand, as the voltage increased, the recombination zone would be changed, which had some effects on the recombination efficiency. Some experiments proved our theoretical prediction.
|
Received: 2002-08-30
Accepted: 2002-12-30
|
|
Corresponding Authors:
LI Hong-jian
|
|
Cite this article: |
XU Xue-mei,PENG Jing-cui,LI Hong-jian, et al. Effect of Temperature and Applied Voltage on the Recombination Efficiency in Double Layer Organic Light Emitting Diodes [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(01): 12-14.
|
|
|
|
URL: |
http://www.gpxygpfx.com/EN/Y2004/V24/I01/12 |
[1] Tang C W, Vanslyke S A. Appl. Phys. Lett., 1987, 51: 913. [2] Burroughes J H, Jones C A, Friend R H. Nature, 1990, 347: 539. [3] Ruhstaller B, Carter S A, Barth S et al. J.Appl. Phys., 2001, 89: 4574. [4] Yang S Y, Xu Z, Wang Z J et al. Appl. Phys. Lett., 2001, 79: 2529. [5] Forrest S R, Burrows P E,Thomson M E. In Organic Electroluminescent Materials and Devices, 1997:425. [6] Brown A R, Bradey D D C, Burn P L. Appl. Phys, Lett., 1993, 61: 2793. [7] Friedman L. Phys, Rev., 1945: 140, A 1649. [8] Morgado J, Cacialli F, Grüner J et al. J. Appl, Phys., 1999: 85, 1784. |
[1] |
CUI Can1,2, SONG Dan-dan1,2, ZHAO Su-ling1,2, QIAO Bo1,2, XU Zheng1,2*. Improving the Efficiency of Solution-Processed, Blue Fluorescent Organic Light-Emitting Diodes (OLEDs) by Employing TADF Exciplex Hosts[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 700-705. |
[2] |
GUAN Yun-xia1, CHEN Li-jia1, CHEN Ping2, FU Xiao-qiang1, NIU Lian-bin1,3* . Influence of MnO3 on Photoelectric Performance in Organic Light Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(03): 648-652. |
[3] |
LI Xue1, SHAO Qiu-ping1, CHEN Shu-fen2*, HUANG Wei2 . Highly Efficient, Color-Stable White Top-Emitting Organic Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(09): 2360-2364. |
[4] |
HUANG Qing-yu1,2, ZHAO Su-ling1,2*, XU Zheng1,2, FAN Xing1,2, WANG Jian1,2, YANG Qian-qian1,2 . White Organic Light-Emitting Diodes Applied for Lighting Technology [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(01): 27-33. |
[5] |
YAN Guang, ZHAO Su-ling*, XU Zheng, ZHANG Fu-jun, KONG Chao, LIU Xiao-dong, GONG Wei, GAO Li-yan . Study on the Movement of the Carrier Recombination Region in Organic Light-Emitting Diodes (OLEDs) Based on DPVBi/Alq3 [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(07): 1729-1733. |
[6] |
LIAN Jia-rong,LIAO Qiao-sheng,YANG Rui-bo,ZHENG Wei,ZENG Peng-ju . Performance Dependence of Organic Light-Emitting Devices on the Thickness of Alq3 Emitting Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(10): 2616-2619. |
[7] |
QIAN Jin-cheng1, JIA Kun-peng2, YU Jun-sheng1*, LOU Shuang-ling1, JIANG Ya-dong1, ZHANG Qing3 . Spectral Characteristics of Novel Small Molecular Fluorene Derivative for Organic Light-Emitting Device [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2010, 30(03): 625-629. |
[8] |
XU Wei, LU Fu-han,CAO Jin,ZHU Wen-qing,JIANG Xue-yin*,ZHANG Zhi-lin,XU Shao-hong. Multiplayer White Organic Light-Emitting Diodes with Different Order and Thickness of Emission Layers [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2008, 28(02): 265-268. |
[9] |
CHENG Bao-mei1,DENG Zhen-bo1*,LIANG Chun-jun1,XU Deng-hui1,WANG Rui-fen2 . Emitting Characteristics and Carrier Composite Regions Variety of the Blend of Terbium Complex and Poly-N-Vinylcarbazole [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(02): 228-231. |
|
|
|
|