| Characterization and Photoluminescence Properties of an Azomethin-Zinc Complex |
| HOU Li-xin1,2,JIA Hu-sheng1,2,HAO Yu-ying1,3,WANG Hua1,2,CHEN Liu-qing1,2,XU Bing-she1,2* |
1. Key Laboratory of Interface Science and Engineering in Advanced Materials, Taiyuan University of Technology, Ministry of Education, Taiyuan 030024, China
2. The College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China
3. The College of Science, Taiyuan University of Technology, Taiyuan 030024, China |
|
|
|
|
Abstract A Schiff base organic metal complex,Bis(salicylidene)-1,2-phenylenediam-ine Zinc(Ⅱ) with high purity, was synthesized and purified by vacuum sublimation. Its structure, thermal stability and energy band structure were investigated by element analysis, FTIR spectra, TG-DTA curve, UV-Vis absorption spectra, fluorescece emission spectra and PL spectra. Experimental results showed that the complex is a thermally stable, polycrystalline material, with glass temperature and decomposition temperature being 183 and 449 ℃, respectively. In its infrared spectrum, a high intensity band was at about 1 385 cm-1. This band was typical of the conjugated CN stretching vibration, which shifted to higher frequency in relation to the free ligand of salicylaldehyde with 1,2-phenylenediamine. The new bnd at 529 cm-1 was assigned to Zn—O stretching vibration. Its UV absorption bands were at about 297 and 406 nm, and its tetrahydrofuran solution emitted intensive blue-green fluorescence at the peak wavelength of 508 nm. The absorption band at about 406 nm can be assigned to the intrinsic absorption of CN. Its optical gap was about 2.62 eV，which was determined by the intrinsic absorption band edge of the complex in tetrahydrofuran solution. Under UV excitation at 365 nm, the complex in film emitted yellow-green fluorescence with the maximum emission peak at 562 nm and a full-width at half-maximum of 48.5 nm in PL spectra. Finally, yellow organic light-emitting devices using this complex as the emissive layer were fabricated and investigated.
|
|
Received: 2006-12-12
Accepted: 2007-03-16
|
|
|
|
Corresponding Authors:
XU Bing-she
E-mail: xubs@public.tysx.cn
|
|
[1] YANG Yu-hui, ZHAN Yi-qiang, DING Huan-jun, et al(杨玉惠，詹义强，丁焕军，徐 健，等). Chin J. Lumin.(发光学报), 2003, 24(6): 583.
[2] LI Jie, ZHOU He-feng, HAO Yu-ying, et al(李 洁，周禾丰，郝玉英，等). Spectroscopy and SpectralAnalysis(光谱学与光谱分析), 2006, 26(2): 235.
[3] Tang C W, Van Slyke S A. Appl. Phys. Lett., 1987, 51(12): 913.
[4] Yuji Hamada, Takeshi Sano, Masayuki Fujita, et al. Japanese Journal Applied Physics，part 2-letters, 1993, 32(4A): L511.
[5] YU Gui, LIU Yun-qi, SONG Ya-ru, et al. Synthetic Metals, 2001, 117(1-3): 211.
[6] HAO Yu-ying, GAO Zhi-xiang, WANG Hua, et al(郝玉英，高志翔，王 华，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2006, 26(3): 491.
[7] HAO Yu-ying, LI Jie, GAO Zhi-xiang, et al(郝玉英，李 洁，高志翔，等). Chinese Journal of Luminescence(发光学报), 2006, 27: 254.
[8] FANG Rong-chuan(方容川). Solid State Spectroscopy(固体光谱学). Hefei: University of Science and Technology of China Press(合肥：中国科技大学出版社), 2001. 58.
[9] HAO Yu-ying, HAO Hai-tao, WANG Hua, et al(郝玉英，郝海涛，王 华，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2004, 24(12): 1524. |
| [1] |
CHEN Huan-quan1, DONG Zhong-ji2, CHEN Zhen-wei1, ZHOU Jin1, SU Jun-hao1, WANG Hao1, ZHENG Jia-jin1, 3*, YU Ke-han1, 3, WEI Wei1, 3. Study on the High Temperature Annealing Process of Thermal
Regeneration Fiber Bragg Grating[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(06): 1934-1938. |
| [2] |
GAO Jian-kui1，2, LI Yi-jie3, ZHANG Qin-nan1, LIU Bing-wei1, LIU Jing-bo1, LING Dong-xiong1, LI Run-hua2, WEI Dong-shan1*. Temperature Effects on the Terahertz Spectral Characteristics of PEEK[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(11): 3347-3351. |
| [3] |
TIAN Zhen-hua1, 2, HE Jing-xuan1, WANG Ying1, DUAN Lian3, LI Cong-hu4. Interaction and Thermal Stability of Oxidized Carboxymethyl Cellulose/Collagen Based on Two-Dimensional Infrared Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(09): 2782-2788. |
| [4] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
| [5] |
YANG Jian1, 2, ZHAO Su-ling1, 2*, SONG Dan-dan1, 2, XU Zheng1, 2, QIAO Bo1, 2, WANG Peng1, 2, WEI Peng1, 2. Highly Efficient Solution Processed Blue Thermally Activated Delayed Fluorescent Organic Light-Emitting Devices with a Mixed Hole Injection Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1028-1033. |
| [6] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
| [7] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
| [8] |
PAN Hua-yan, WANG Le*, LI Yang-hui, WU Tuo, LUO Dong. Preparation and Luminescence Properties of a New Green Emitting Ca3Mg3Si4O14∶Eu2+ Phosphor[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(08): 2627-2631. |
| [9] |
CHEN Yi-xiang, ZHAO Su-ling*, XU Zheng, ZHANG Cheng-wen, XU Xu-rong. The Establishment and the Application of the Electroluminescence Decay Measurement System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 1993-1996. |
| [10] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
| [11] |
LU Bao-qi, XU Yao-xian, SHEN Guang-yao, JI Jiang-hua, WANG Lin-jun. Raman Spectra Study on the Structure and Thermal Stability of Vacuum Annealed Cr-DLC Films Prepared with UBMS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3568-3571. |
| [12] |
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763. |
| [13] |
YANG Zhao-kun, ZHAO Su-ling*, XU Zheng*, HUANG Qing-yu . The Inside Charge Behavior of Organic Light-Emitting Diodes Investigated with Transient Electroluminescent Measurements[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3134-3137. |
| [14] |
ZHANG Feng1, DONG Ya-bo2, MENG Fan-cheng2* . Study on the Raman Spectrum, Thermal Stability and UV-Vis Optical Absorption of Amorphous Peroxpolytungstic Acid[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(04): 991-995. |
| [15] |
CAO Juan1, HUANG Yan1*, ZHANG Qi1, 2*, HUA Yu-jie1, HUA Ming-qing1, GONG Jian-bo1, ZHU Wei-hua1 . Study on the Interaction between Low Molecular Weight Chitosan-Based Schiff Bases and Bovine Serum Albumin [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(04): 1090-1094. |
|
|
|
|