Electroluminescence Property of MEH-PPV/ZnO Nano-Crystal Structure |
LI Hai-ling,WANG Yong-sheng,TENG Feng,XU Zheng |
Institute of Optoelectronic Technology Beijing Jiaotong University, Key Lab of Material for Information Storage and Display, Beijing 100044, China |
|
|
Abstract A new structure with Ⅱ-Ⅵ nano-crystal ZnO film as the electron transport layer and MEH-PPV as the hole transport layer and emitting layer was fabricated. The new structure’s brightness and efficiency were improved markedly compared with that of the single MEH-PPV layer structure. And a new peak at 620 nm was found in the ITO/MEH-PPV/ZnO/Al structure’s electroluminescence spectrum, which should resulted from ZnO layer. In addition, the turning-on voltage of the two-layer structure decreased from 9 V of the single layer structure to 4 V. From the I-V curve, the authors concluded that the emitting area was around the interface of MEH-PPV/ZnO and the combination area could shift with changing the voltage.
|
Received: 2003-01-06
Accepted: 2003-06-26
|
|
Corresponding Authors:
LI Hai-ling
|
|
Cite this article: |
LI Hai-ling,WANG Yong-sheng,TENG Feng, et al. Electroluminescence Property of MEH-PPV/ZnO Nano-Crystal Structure [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(10): 1172-1175.
|
|
|
|
URL: |
http://www.gpxygpfx.com/EN/Y2004/V24/I10/1172 |
[1] Greenham N C, Moratti S C, Bradley D D et al. Nature,1993, 365: 628. [2] Tang C W, Vanslyke S A, Chen C H et al. J. Appl. Phys., 1989, 65(9): 3610. [3] WANG Wei, DING Xiao-ping, MENG Guang-zheng(王 薇, 丁小平,孟广政). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2000, 20(2): 219. [4] Colvin V L, Schlamp M C, Alivisatos A P et al. Nature,1994,370:354. [5] TENG Feng,YANG Xiao-hui,XU Zheng et al(滕 枫,杨晓辉,徐 征等). Chinese Journal of Luminescence(发光学报),1997,18:348. [6] TENG Feng,YANG Xiao-hui,XU Zheng et al(滕 枫,杨晓辉,徐征 等). Journal of Functional Materials(功能材料),1998,29:543. [7] LI Jian-hong, QU Shu, XU Xue-mei,PENG Jing-cui(李宏建,瞿 述,许雪梅,彭景翠). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2002, 22(3): 360. [8] Young Kwan Kim, Kwaung Youn Lee et al. Synthetic Metals,2000,111-112:207. [9] Huang J M, Yang Y, Liu S Y et al. Appl. Phys. Lett.,1997,70:2335. [10] Spanhel Lubomir et al. J. Am. Chem. Soc.,1991,113:2826. [11] Brus L E. J. Chem. Phys.,1986,90:2555. [12] Brus L E. J. Chem. Phys.,1983, 79(11):5566. [13] Brus L E. J. Nanostruct. Mater.,1992,(1):71. [14] Wilson W L. Science,1993, 262:1242.
|
[1] |
ZHANG Tian-yao1,2, ZHANG Zhao-hui1*, ZHAO Xiao-yan1, WEI Qing-yang1, CAO Can1, YU Yang1, LI Ying1, LI Xing-yue1. Polarizability Measurements for Salicylic Acid Embedded in Polymer Matrix Using Terahertz Time-Domain Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1688-1694. |
[2] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
[3] |
YANG Jian1, 2, ZHAO Su-ling1, 2*, SONG Dan-dan1, 2, XU Zheng1, 2, QIAO Bo1, 2, WANG Peng1, 2, WEI Peng1, 2. Highly Efficient Solution Processed Blue Thermally Activated Delayed Fluorescent Organic Light-Emitting Devices with a Mixed Hole Injection Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1028-1033. |
[4] |
CHEN Shi, WU Jing, WANG Chao-nan, FANG Jing-huai*. Preparation of SERS Substrates Based on Polymer Nano-Needle Arrays Modified by Ag Nanoparticles[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 765-769. |
[5] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
[6] |
LEI Yu, GUO Xue-mei, ZHU Shi-chao, WANG Meng-meng, JIN Gang*. Application Progress of Near-Infrared Spectroscopy in the Polymer Field[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(07): 2114-2118. |
[7] |
ZHANG Tian-yao1, 2, 3, ZHANG Zhao-hui1, 2*, Arnold Mark A.3. Dielectric Analysis of Polymeric Materials and Mixtures Using Terahertz Time Domain Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(06): 1689-1694. |
[8] |
SUN Tian-lei1, YAN Jing-hui1*, GENG Ai-fang1*, ZHANG Hong2, ZOU Ming-qiang3, 4. Design and Synthesis of Rare Earth Organic-Inorganic Hybrid Material Based on Polyoxometalate and 1,4,5,8-Naphthalenediimide Derivatives[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(06): 1915-1921. |
[9] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
[10] |
GONG Chen, ZUO Jian*, ZHANG Cun-lin. Analysis of Complex Dielectric Constant and Loss Properties of Cyclic Olefin Polymer Substrate by Terahertz Time-Domain Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(10): 2998-3003. |
[11] |
HU Wen-hua, DONG Jun, CHI Zi-fang*, REN Li-ming. Preparation and Spectroscopy Characterization of Magnetic Pb(Ⅱ)-Ion Surface Imprinted Polymers(Fe3O4/GO-IIP)[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(11): 3499-3503. |
[12] |
MA Hui-yan1,2, ZHOU Dan1, LIU Ju-ming2, ZHANG Qian-cheng1,2*. Preparation and Spectral Characteristics of SO2-4/CeO2-TiO2 Photocatalyst[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(10): 3315-3320. |
[13] |
CHEN Yi-xiang, ZHAO Su-ling*, XU Zheng, ZHANG Cheng-wen, XU Xu-rong. The Establishment and the Application of the Electroluminescence Decay Measurement System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 1993-1996. |
[14] |
LEI Yong, LIU Zhen, FAN Chang-jun, JI Xia-xia, PENG Xue-feng, LI Guo-qing, YANG Xiao-hui* . Study on Tandem Polymer Light Emitting Devices [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 715-722. |
[15] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
|
|
|
|