| Multiple Emissions in Organic Electroluminescent Device Using a Mixed Layer as an Emitter |
| ZHU Wen-qing, WU You-zhi, ZHENG Xin-you, JIANG Xue-yin, ZHANG Zhi-lin, SUN Run-guang, XU Shao-hong |
| Department of Materials, Shanghai University，Jiading Campus, Shanghai 201800, China |
|
|
|
|
Abstract A organic electroluminescent device has been fabricated by using a mixed layre as an emitter. The configuration of the device is ITO/TPD/TPD: PBD(equimole)/PBD/Al, in which TPD (N, N′-diphenyl-N, N′-bis(3-methylphenyl)-1, 1′-biphenyl-4, 4′-diamine) and PBD(2-(4′-biphenyl)-5-(4″-tert-butylphenyl)-1, 3, 4-oxadiazole) are used as hole transport material and electron transport material, respectively. Broad and red-shifted electroluminescent spectra related to the fluorescence of constituent materials were observed. It is suggested that the monomer, exciplex and electroplex emissions are simultaneously involved in EL spectra by comparison of the EL with the PL spectra and decomposition of the EL spectrum. The type of exciplex is the interaction between the excited state TPD(TPD*) and PBD in the ground state, and the type of electroplex is a (D+-A-)* complex by cross-recombination of hole on the charged hole transport molecule(D+) and electron on the charged electron transport molecule(A-). All types of excited states show different formation mechanisms and recombination processes under electric field. The change of emission strengths from monomer and excited complexes lead to a blue-shift of the emissive spectra with an increasing electric field. The maximum luminance and external quantum efficiency of this device are 240 cd·(cm2)-1 and 0.49%, respectively. The emissions from exciplex or electroplex formation at the organic solid interface generally present a broad and red-shifted emissive band, providing an effective method for tuning of emission color in organic electroluminescent devices.
|
|
Received: 2003-10-28
Accepted: 2004-02-16
|
|
|
|
Corresponding Authors:
ZHU Wen-qing
|
|
| Cite this article: |
|
ZHU Wen-qing,WU You-zhi,ZHENG Xin-you, et al. Multiple Emissions in Organic Electroluminescent Device Using a Mixed Layer as an Emitter [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2005, 25(04): 509-511.
|
|
|
|
| URL: |
|
https://www.gpxygpfx.com/EN/Y2005/V25/I04/509 |
[1] Wang J F, Kawabe Y, Shaheen S E et al. Adv. Mater., 1998, 10(3): 230.
[2] Cocchi M, Virgili D, Giro G et al. Appl. Phys. Lett., 2002, 80(13): 2401.
[3] Granlund T, Pettersson L A A, Anderson M R et al. J. Appl. Phys., 1997, 81(12): 8097.
[4] Cao H, Gao X，Huang C H. Appl. Surf. Sci., 2000, 161(3-4): 443.
[5] Jenekhe S A，Osaheni J A. Science, 1994, 265(5173): 765.
[6] Chao C I and Chen S A. Appl. Phys. Lett., 1998, 73(4): 426.
[7] Berggren M, Gustafsson G，Ingans O. J. Appl. Phys., 1994, 76(11): 7530.
[8] Ogawa H, Okuda R，Shirota Y. Appl. Phys. A, 1998, 67(5): 599.
|
| [1] |
ZHAO Yuan, LÜ Zhao-yue*, DENG Jian, ZENG Guo-qing. The Emissive Mechanism of C545T Thin Layer at the Exciplex and Non-Exciplex Interfaces[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(12): 3711-3715. |
| [2] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
| [3] |
YANG Jian1, 2, ZHAO Su-ling1, 2*, SONG Dan-dan1, 2, XU Zheng1, 2, QIAO Bo1, 2, WANG Peng1, 2, WEI Peng1, 2. Highly Efficient Solution Processed Blue Thermally Activated Delayed Fluorescent Organic Light-Emitting Devices with a Mixed Hole Injection Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1028-1033. |
| [4] |
CUI Can1,2, SONG Dan-dan1,2, ZHAO Su-ling1,2, QIAO Bo1,2, XU Zheng1,2*. Improving the Efficiency of Solution-Processed, Blue Fluorescent Organic Light-Emitting Diodes (OLEDs) by Employing TADF Exciplex Hosts[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 700-705. |
| [5] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
| [6] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
| [7] |
ZHU Wei-yi1, JIN Min-feng1, TU Xie-hao1, ZHANG Ye-feng1, YIN Yue-hong2, Lü Zhao-yue1*. Bimolecular Excited States Based on 3DTAPBP: Electromer and Exciplex[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(08): 2344-2349. |
| [8] |
CHEN Yi-xiang, ZHAO Su-ling*, XU Zheng, ZHANG Cheng-wen, XU Xu-rong. The Establishment and the Application of the Electroluminescence Decay Measurement System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 1993-1996. |
| [9] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
| [10] |
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763. |
| [11] |
YANG Zhao-kun, ZHAO Su-ling*, XU Zheng*, HUANG Qing-yu . The Inside Charge Behavior of Organic Light-Emitting Diodes Investigated with Transient Electroluminescent Measurements[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3134-3137. |
| [12] |
SONG Ling-yun1, CAI Chun-feng1, LIU Bo-zhi1, HU Lian1, ZHANG Bing-po1, WU Jian-zhong2*, BI Gang2, WU Hui-zhen1*. Influence of Parameters of ZnS Film on the Organic/Inorganic Composite Luminescence Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(04): 898-902. |
| [13] |
DAI Shuang, YU Tong-jun*, LI Xing-bin, YUAN Gang-cheng, LU Hui-min . The Electroluminescence Spectra of InGaN/GaN Blue LEDs During Aging Time [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 327-330. |
| [14] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326. |
| [15] |
YANG Yi-fan, ZHAO Su-ling*, GAO Song . Tunneling Electroluminescence of the ZnO Nanorods/MEH-PPV Heterojunction Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2895-2899. |
|
|
|
|