| Photoluminescence from Interface of SiO/SiO2 Superlattices |
| WANG Shen-wei,YI Li-xin*,HE Zhen,HU Feng,WANG Yong-sheng |
| Key Laboratory of Luminescence and Optical Information，Ministry of Education，Institute of Optoelectronic Technology，Beijing Jiaotong University，Beijing 100044，China |
|
|
|
|
Abstract SiO/SiO2 superlattices with different thickness of SiO and SiO2 films were deposited on the Si substrates at 200 ℃ by thermo-evaporation technology. The photoluminescence (PL)spectrum centers of the samples shifted from 400 nm to 600 nm with the increase in SiO films thickness. Similar phenomena were also found when increasing the thickness of SiO2 film but forming SiO film. It was found that the PL was attributed to the defects located at the interfaces between SiO and SiO2 films. The deconvolution of the PL spectra showed that the WOB(O3≡Si—O—O·), NOV(O3≡Si—Si≡O3), the E′center(O≡Si·)and NBOHC (O3≡Si—O·)defects contributed to the PL spectra. A mass of Si—O dangling bonds formed on the interfaces of the SiO and SiO2 during the deposition process，could provide many free O atoms and intrinsic defects. When the SiO film was thin (such as 1 nm), most of the Si6 rings were broken, and more WOB defects(415 nm)would be formed because of the combination of the intrinsic NBOHC defects and the diffusing O atoms on the interfaces. With the increase in the SiO film thickness, more Si6 rings were formed in the SiO films, that is the number of the Si—O dangling bonds decreased, less of WOB defects could be formed as both of the free O atoms and intrinsic defects decreased, but the NOV defects(470 nm)increased because of more E′center defects would be combined in pairs. With increasing of the SiO film thickness, the combination of the intrinsic defects became more difficult, so the E′center defects(520 nm)and NBOHC defects(630 nm)would dominate the PL of the SiO/SiO2 superlattices in turn. In conclusion, the evolution of the defects located at the interfaces induced the red shift of the PL.
|
|
Received: 2008-09-10
Accepted: 2008-12-20
|
|
|
|
Corresponding Authors:
YI Li-xin
E-mail: 06118326@bjtu.edu.cn
|
|
[1] Canham L T. Appl. Phys. Lett., 1990, 57: 1046.
[2] Cullis A G, Canham L T, Calcott P D. J. Appl. Phys., 1997, 82: 909.
[3] Ono Takahito, Saitoh Hiroaki, Esashi Masayoshi. Appl. Phys. Lett., 1997, 70: 1852.
[4] Beyer V, Borany J von, Heinig K H. J. Appl. Phys., 2007, 101: 053516.
[5] Shklyaev A A, Nakamura Y, Ichikawa M. J. Appl. Phys., 2007, 101: 033532.
[6] Yang D Q, Meunier M, Sacher E. J. Appl. Phys., 2006, 99: 084315.
[7] Kendrick X Liu, Chin-Jen Chiang, Jonathan P Heritage. J. Appl. Phys., 2006, 99: 034502.
[8] Inokuma T, Wakayama Y, Muramoto T, et al. J. Appl. Phys., 1998, 83: 2228.
[9] Yi L X, Heitmann J, Scholz R, et al. Appl. Phys. Lett., 2002, 81: 4248.
[10] Mutti P, Ghislotti G, Bertoni S, et al. Appl. Phys. Lett., 1995, 66: 851.
[11] CHEN En-guang, YI Li-xin, WANG Shen-wei，et al(陈恩光，衣立新，王申伟, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2008, 28(2): 246.
[12] SUN Xiao-jing, MA Shu-yi, WEI Jin-jun, et al(孙小菁，马书懿，魏晋军，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2008, 28(9): 2033.
[13] Yoshihiko Kanemitsu, Toshiro Futagi, Takahiro Matsumoto, et al. Phys. Rev. B, 1994, 49: 14732.
[14] Tsutomu Shimizu-Iwayama, Norihiro Kurumado. J. Appl. Phys., 1998, 83: 6018.
[15] Rinnert H, Vergnat M, Marchal G. Appl. Phys. Lett., 1998, 72: 3157.
[16] Lin Gong-ru, Lin Chun-jung, Lin Chi-kuan. J. Appl. Phys., 2005, 97: 094306.
[17] Qin G G, Li A P, Zhang B R, et al. J. Appl. Phys., 1995, 78: 2006.
[18] Nishikawa H, Watanabe E, Ito D, et al. J. Appl. Phys., 1995, 78: 842.
[19] Liao L S, Bao X M, Zheng X Q, et al. Appl. Phys. Lett., 1996, 68: 850.
[20] Song Hai-zhi, Bao Xi-mao, J. Appl. Phys., 1997, 82: 4028.
[21] WANG Shen-wei, YI Li-xin, SU Meng-chan, et al(王申伟, 衣立新, 苏梦蟾, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2007, 27(3): 456.
|
| [1] |
QIN Li-mei, Andy Hsitien Shen*. Photoluminescence Spectral Characteristics of Jet From Fushun, Liaoning Province[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3180-3185. |
| [2] |
ZHU Hong-wei1, CHENG You-fa1, CHEN Shu-xiang2*, FAN Chun-li1, LI Ting1, LIU Hai-bin1, ZHAO Xiao-xue1SHAN Guang-qi1, LI Jian-jun1. Spectroscopic Characteristics of a Natural Diamond Suspected of Synthetic Diamond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1690-1696. |
| [3] |
YAN Xue-jun1, ZHOU Yang2, HU Dan-jing1, YU Dan-yan1, YU Si-yi1, YAN Jun1*. Application of UV-VIS Diffuse Reflectance Spectrum, Raman and
Photoluminescence Spectrum Technology in Nondestructive
Testing of Yellow Pearl[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1703-1710. |
| [4] |
LI Zhao, WANG Ya-nan, XU Yi-pu, CAO Jing, WANG Yong-feng, WU Kun-yao, DENG Lu. Synthesis and Photoluminescence of Blue-Emitting Phosphor
YVO4∶Tm3+ for White Light Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 623-628. |
| [5] |
LIAO Yi-min1, YAN Yin-zhou1, WANG Qiang2*, YANG Li-xue3, PAN Yong-man1, XING Cheng1, JIANG Yi-jian1, 2. Laser-Induced Growth Device and Optical Properties of ZnO
Microcrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3000-3005. |
| [6] |
WANG Tao1, 2, LIU Jian-xun2, GE Xiao-tian2, WANG Rong-xin2, SUN Qian2, NING Ji-qiang2*, ZHENG Chang-cheng3*. Fine Photoluminescence Spectroscopic Characterization of Interfacial Effects on Emission Properties of InGaN/GaN Multiple Quantum Wells in a Blue-Light Laser Diode Structure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(04): 1179-1185. |
| [7] |
LI Zhao, WU Kun-yao, WANG Ya-nan, CAO Jing, WANG Yong-feng, LU Yuan-yuan. Synthesis and Luminescence Properties of Yellow-Emitting Phosphor Y2.93Al5O12∶0.07Ce3+ Under Blue Light Excitation[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(02): 381-385. |
| [8] |
CHEN Cai-yun-fei, LI Li-ping*. The Application of Photoluminescence Spectra on Identification of Different Types of Pearls[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(01): 20-25. |
| [9] |
ZHAO Tong1, WANG Ya-mei1,2, LIU Ling1, LI Yan1,3*. Gemological and Spectral Characteristics of Mexican Red Blue Amber[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(08): 2618-2625. |
| [10] |
CHEN Yan-ping1, LUO De-li2*, HUANG Bin1, CHENG Hao1, TANG Xian-chen1, LI Qiang1, LEI Hong-bo1, CHEN Dan-ping3. Photoluminescence and Radioluminescence of Tb3+ Ion-Doped Lithium Aluminosilicate Glasses[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1863-1868. |
| [11] |
ZHAN Ying-fei, LIU Chun-guang*, WANG Ming-wei, YANG Jian, ZHU Han-cheng, YAN Duan-ting, XU Chang-shan, LIU Yu-xue. Preparation, Microstructure and Optical Properties of Cr3+ Single-Doped and Eu3+/Cr3+ Co-Doped GdAlO3 Near Infrared Long Persistent Luminescent Nanoparticles[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(01): 80-87. |
| [12] |
ZHAO Yuan, LÜ Zhao-yue*, DENG Jian, ZENG Guo-qing. The Emissive Mechanism of C545T Thin Layer at the Exciplex and Non-Exciplex Interfaces[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(12): 3711-3715. |
| [13] |
LIN Shun-hui，ZHANG Li-hui, LIU Yong-quan, WANG Xiao-kun, LIN Chun-lei, YU Yun-peng*. Thermal Annealing Effect on Photoluminescence of Y2O3∶Eu3+ Thin Films Prepared by Magnetron Sputtering[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(11): 3336-3340. |
| [14] |
YAN Jun1,2, SUN Qing2, YAN Xue-jun1, FANG Shi-bin1, SHENG Jia-wei2, ZHANG Jian2*. The Categories of the UV-Vis Reflectance Spectra of Seawater Cultured Black Pearl and Its Unique PL Spectral Characteristics[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2781-2785. |
| [15] |
ZHENG Bao-feng1, YANG Xiao-yun2，3, MIN Chun-gang2，3, CUI Xiao-ying2，3, DONG Kun2，3*. Study on Raman Spectra and Fluorescence Spectra of Dy3Al2(AlO4)3 in Aluminosilicate Substrates[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 809-812. |
|
|
|
|