Study on the Theory and Experiments of Radiative Parameters of the Eu3+ Ion in Transparent Optical Resin |
WANG Fu-xiang1, 2, PEI Song-hao1, 2, PENG Wei-xian1, 2*, WANG Dong-mei3, YANG Bai3, WANG Feng-min1, 2, LI Xin-guo1, 2 |
1. Department of Physics, Jilin University, Changchun 130023, China 2. Coherent Light and Atom-Molecule Spectroscopy Lab of Education Department, Changchun 130023, China 3. Department of Chemistry, Jilin University, Changchun 130023, China |
|
|
Abstract The optical properties of a transparent optical resin (HMA/ST) containing ternary rare earth complex are reported. Based on Judd-Ofelt(J-O) theory, the J-O parameters were calculated to be Ω2=10.139 4×10-20cm2, Ω4=3.810 9×10-20cm2, Ω6=9.050 7×10-20cm2 by using the emission spectrum of optical resin containing Eu(TTA)3phen-0.31 wt%. The J-O parameters were used to calculate the total radiative transition rate (456.6 s-1) and radiative lifetime (2 190.1 μs) of the excited state 5D0. The stimulated emission cross-sections σ and the fluorescence branch ratio β parameters for the transitions of 5D0→7FJ′(where J′= 1, 2, 4 and 6) were also evaluated. By analyzing the calculated J-O parameters, it is concluded that the excited state of Eu3+ in optical resin has a long radiative lifetime and large emission cross-section, which shows that the optical resin containing rare earth complex can be used for stimulated emission amplification or as a laser material.
|
Received: 2004-11-16
Accepted: 2005-02-08
|
|
Corresponding Authors:
PENG Wei-xian
|
|
Cite this article: |
WANG Fu-xiang,PEI Song-hao,PENG Wei-xian, et al. Study on the Theory and Experiments of Radiative Parameters of the Eu3+ Ion in Transparent Optical Resin[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(02): 248-250.
|
|
|
|
URL: |
https://www.gpxygpfx.com/EN/Y2006/V26/I02/248 |
[1] ZHANG Li, YANG Zhan-lan, SUN Ying, TAO Dong-liang, YAO Guang-qing, WU Jin-guang(张 莉,杨展澜,孙 颖,陶栋梁,姚光庆,吴瑾光). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2000,20(5):661. [2] YANG Sheng-yi, WANG Zhen-jia, XU Xu-rong, ZHANG Li, YANG Zhan-lan,WU Jin-guang(杨盛谊,王振家,徐叙瑢,张 莉,杨展澜,吴瑾光). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2000, 20(6):872. [3] WANG Dong-mei, LIN Quan, XIE Zhen-guo, et al(王冬梅,林 权,谢振国, 等). Acta Polymerica Sinica(高分子学报), 2004, 3(6): 313. [4] Xu Huailiang, Dai Zhenwen, Jiang Zhankui, et al. Physica B, 2002, 324: 43. [5] Judd B R. Phys. Rev., 1962, 127: 750. [6] Ofelt G S. J. Chem. Phys., 1962, 37: 511. [7] Wang G J. Opt. Soc. Am., B, 2001, 18: 173. [8] Guo Y, Zheng X, Ming H, et al. Chin. Phys. Lett., 2001, 18: 1337. [9] Xu X S, Ming H, Zhang Q J. Opt. Commun., 2001, 199: 369. [10] Carnall W T, Fields P R, Wybourne B G. J. Chem. Phys., 1965, 42: 3797. [11] ZHANG Si-yuan,BI Xian-zhang(张思远,毕宪章). The Theory of Rare Earth Spectroscopy(稀土光谱理论). Changchun: Jilin Science and Technology Press(长春: 吉林科学技术出版社), 1991. 155. [12] Kumar Akshaya, Rai D K, Rai S B. Spectrochimica Acta Part A, 2002, 58: 2115. [13] Capobianco J A, Proulx P P, Bettinelli M, et al. Phys. Rev. B, 1990, 42: 5936. [14] Babu P, Jayasankar C K. Physica B, 2000, 279: 262. [15] Weber M J, Crosswhite H M, Moos H W. Optical Properties of Ions in Crystal. New York: Interscience, 1967. 467. [16] Zheng Z Q, Liang H, Ming H, et al. Chin. Phys. Lett., 2003, 20(5): 654. [17] Yasuchika Hasegawa, Masaki Yamamuro, Yuji Wada. J. Phys. Chem. A, 2003, 107: 1697. [18] Yasuchika Hasegawa, Yuji Wada, Shozo Yanagida. Appl. Phys. Lett., 2003, 83(17): 3599. |
[1] |
YANG Xiao-dong1, CHEN Ying1, CHEN Xiao-bo1*, Sawarobori N2, WANG Shui-feng1, ZHOU Yong-fen3, LI Song1, XU Yi-zhuang3, CHENG Huan-li1, YANG Guo-jian1. Spectroscopy Parameters of Ho3+ in Ho3+:FOG and Ho3+:FOV[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1734-1738. |
[2] |
CHEN Ying1, CHEN Xiao-bo1*, CHEN Luan1, YANG Xiao-dong1, HU Li-li2, WU Zheng-long1, YU Chun-lei2, WANG Ya-fei1, LIU Da-he1, TIAN Qiang1. Spectroscopic Properties of Pr3+ Doped Transparent Oxyfluoride Vitroceramics[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(12): 3213-3217. |
[3] |
CHEN Yue-e1, HOU Lan-tian2 . Preparation and Luminescence Properties of Eu3+-Doped Cadmium Aluminium Silicate Glass [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(05): 1205-1208. |
[4] |
WEI Hua-jiang1, GUO Zhou-yi1*,XIE Shu-sen2,GU Huai-min1,WU Guo-yong3,HE Bo-hua4,JIN Ying1 . Comparison of Light Attenuation Characteristics and Optical Penetration Depths between Native and Coagulated Human Liver Tissues [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(09): 1757-1760. |
[5] |
WEI Hua-jiang1, XING Da1*, WU Guo-yong2, JIN Ying1, GU Huai-min1 . Comparative Research on Attenuation Characteristics of Human Bladder Cancer Tissue at Different Wavelengths of Laser and Their Linearly Polarized Laser in Vitro[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2004, 24(11): 1296-1298. |
|
|
|
|