| Synthesis and Photoluminescence of Zn1-x Mo1-ySiyO4∶Eu3+x Phosphor |
| ZHOU Li-ya1, XU Ting-bo1, PANG Qi2, GONG Fu-zhong1, WANG Wei1, HUANG Jun-li1, YI Ling-hong1 |
1. School of Chemistry and Chemical Engineering, Guangxi University, Nanning 530004, China
2. Department of Chemistry and Biology, Yulin Normal University, Yulin 537000，China |
|
|
|
|
Abstract The phosphors Zn1-xMo1-ySiyO4∶Eu3+x(0.05≤x≤0.30, 0≤y≤0.09) were prepared by solid state reaction technique at 800 ℃. The powder X-ray diffraction patterns of the samples show that the phosphors are of single phase and the doping Eu ion and Si ion have little influence on the host structure. The effects of flux and calcination temperature on the luminescent properties of the phosphors were investigated. The results showed that flux content has effects on the luminescent properties, and the optimized flux content and the best calcination temperature is 4% and 800 ℃, respectively. The presence of the Na+ ion strengthens the photoluminescence intensity of the phosphors. The addition of Na+ ions balanced the charge in samples, enhanced the luminescence intensity of samples, and the luminescence intensity reached the maximum when the doping concentration of Na2CO3 was 4 Wt%. The luminescent properties of Zn0.80Mo1-ySiyO4∶Eu3+0.20 were studied by the excitation and emission spectra, and the influence of Eu3+ and Si4+ concentrations on the luminescent property was discussed. As the calcination temperature rises from 700 to 800 ℃, the emission intensity increases due to the improvement of crystallinity. The excitation spectra consist of a broad band and a series of narrow lines, and the narrow lines are attributed to the intrinsic transition from 7FJ(J=1-4) to 5DJ(J=0, 1) of Eu3+. It was found that the PL emission intensity was enhanced with the increase in the Eu3+ doping ratio and reached a maximum value at x=0.20. The result indicated that Zn1-xMo1-ySiyO4∶Eu3+x phosphors can be excited effectively at 393 and 464 nm light. The presence of the Si4+ ion strengthens the photoluminescence intensity of the phosphors and the strong red emission lines at 616 nm correspond to the forced electric dipole 5D0→7F2 transitions on Eu3+. Compared with Y2O2S∶0.05Eu3+, the obtained Zn0.80Mo0.97Si0.03O4∶Eu3+0.20 phosphor shows an enhanced red emission under 393 nm excitation and the emission intensity of Y2O2S∶0.05Eu3+ is only 50% of that of Zn0.80Mo0.97Si0.03O4∶Eu3+0.20. The optical properties suggest that Zn0.80Mo0.97Si0.03O4∶Eu3+0.20 is an efficient red emitting phosphor for light emitting diode (LED) applications.
|
|
Received: 2008-11-08
Accepted: 2009-02-12
|
|
|
|
Corresponding Authors:
ZHOU Li-ya
E-mail: zhouliyatf@163.com
|
|
[1] Nishida T, Ban T, Kobayashi N. Appl. Phy. Lett., 2003, 82(22): 3817.
[2] Smet P F, Korthout K, Van Haecke J E, et al. Mat. Sci. Eng., 2008, B146: 264.
[3] Wang Z L, Liang H B, Gong M L, et al. Opt. Mater., 2007, 29: 896.
[4] Kim J S, Jeon P E, Choi J C, et al. Appl. Phys. Lett., 2004, 84: 2931.
[5] Sheu J K, Chang S J, Kuo C H, et al. IEEE Photonics Tech. Lett., 2003, 15: 18.
[6] Hu Y S, Zhuang W D, Ye H Q, et al. J. Alloy. Comp. 2005, 390: 226.
[7] Sivakumar V, Varadaraju U V. J . Electrochem. Soc., 2005, 150(10): H168.
[8] Neeraj S, Kijima N, Cheetham A K. Chem. Phys. Lett., 2004，387(1-3): 2.
[9] Liu J, Lian H, Shi C. Opt. Mater., 2007, 29(12): 1591.
[10] LIDE D, Editor-in-Chief, The CRC Handbook of Chemistry and Physics on CD-ROM, CRC Press, Version, 2002. 12.
[11] Li X, Yang Z, Guan L, et al. J. Cryst. Growth, 2008, 310: 3117.
[12] Reddy K R, Annapurna K, Buddhudu S. Mater. Res. Bull., 1996, 31: 1355. |
| [1] |
HAN Zhao-xia1, 2, 3*, YANG Zhi-jin1, ZHANG Zhi-hong1, DING Shu-hui1, ZHANG Da-wei1, 2, 3, HONG Rui-jin1, 2, 3, TAO Chun-xian1, 2, 3, LIN Hui1, 2, 3, YU De-chao1, 2, 3. Preparation of Full-Color Carbon Quantum Dots and Their Application in WLED[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1358-1366. |
| [2] |
LI Zhao, WANG Ya-nan, XU Yi-pu, CAO Jing, WANG Yong-feng, WU Kun-yao, DENG Lu. Synthesis and Photoluminescence of Blue-Emitting Phosphor
YVO4∶Tm3+ for White Light Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 623-628. |
| [3] |
ZHANG Yuan-zhe1, LIU Yu-hao1, LU Yu-jie1, MA Chao-qun1, 2*, CHEN Guo-qing1, 2, WU Hui1, 2. Study on the Spectral Prediction of Phosphor-Coated White LED Based on Partial Least Squares Regression[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(08): 2347-2352. |
| [4] |
LI Zhao, WU Kun-yao, WANG Ya-nan, CAO Jing, WANG Yong-feng, LU Yuan-yuan. Synthesis and Luminescence Properties of Yellow-Emitting Phosphor Y2.93Al5O12∶0.07Ce3+ Under Blue Light Excitation[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(02): 381-385. |
| [5] |
ZHAN Ying-fei, LIU Chun-guang*, WANG Ming-wei, YANG Jian, ZHU Han-cheng, YAN Duan-ting, XU Chang-shan, LIU Yu-xue. Preparation, Microstructure and Optical Properties of Cr3+ Single-Doped and Eu3+/Cr3+ Co-Doped GdAlO3 Near Infrared Long Persistent Luminescent Nanoparticles[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(01): 80-87. |
| [6] |
LI Zhao, WANG Yong-feng, CAO Jing, WU Kun-yao, WANG Ya-nan. Preparation and Performance of Red Phosphor ScVO4∶Eu3+ for White LEDs[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3077-3080. |
| [7] |
FENG Ai-ming1, WANG Fu-qiang1, ZHANG Hong1*, AN Peng2, LI Yang-hui1, 3, WANG Le1*. Significantly Improved Luminescence Properties of YAG Phosphor via Localized Surface Plasmon Resonance of Nanotitania[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(10): 3081-3085. |
| [8] |
JIANG Fu-chun1, HE Si-yu1, LIU Yuan-hai1, LIU Wen1*, CHAI Guang-yue1, 2, LI Bai-kui1, PENG Dong-sheng1. A Measurement Method Base on FWHM for Determining Junction Temperature of LED[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(07): 2087-2091. |
| [9] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
| [10] |
XU Jian-wen1, 2 , CHEN Guo-qing1, 2*, WU Ya-min1, 2, MA Chao-qun1, 2, GU Jiao1, 2. Establishment of the Spectral Equation of Two Phosphor-Coated White LEDs[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 799-803. |
| [11] |
CUI Can1,2, SONG Dan-dan1,2, ZHAO Su-ling1,2, QIAO Bo1,2, XU Zheng1,2*. Improving the Efficiency of Solution-Processed, Blue Fluorescent Organic Light-Emitting Diodes (OLEDs) by Employing TADF Exciplex Hosts[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 700-705. |
| [12] |
ZHANG Nan, LIU Chun-guang*, ZHANG Meng, YANG Jian, LI Sheng-nan, ZHU Han-cheng, YAN Duan-ting, XU Chang-shan, LIU Yu-xue. Preparation and Optical Properties of Near Infrared Persistentluminescent CaGdAlO4∶Cr3+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(02): 373-378. |
| [13] |
FAN Bin1, LIU Jun2, QI Shi-mei3, ZHAO Wen-yu1*. Preparation and Luminescent Properties of Green Phosphors LaGaO3∶Tb3+,Sn4+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 65-70. |
| [14] |
ZHANG Hong1, WANG Le1*, LUO Dong1, ZHENG Zi-shan1, LI Yang-hui1, 2, PAN Gui-ming1. Structural and Luminescence Properties of Eu2+ Doped CaAlSiN3 Silicon Nitride Red Emitting Phosphor[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 59-64. |
| [15] |
SUN Chuan-yao1, LUO Lan1, 2*, WANG Yu1, GUO Rui1, ZHANG Yuan-bo1. Photoluminscence Spectra and Ternary CIE Colour Image of (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu Phosphor Series[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 98-106. |
|
|
|
|