Study on Preparation Stage and Mechanism of Modified Desulfurization Ash-Based Eco Rubber by X-Ray Diffraction |
ZHANG Hao1,2, ZHANG Lei1, LIU Xiu-yu1 |
1. School of Civil Engineering and Architecture, Anhui University of Technology, Ma’anshan 243032, China
2. Key Laboratory of Metallurgical Emission Reduction & Resources Recycling (Anhui University of Technology), Ministry of Education, Ma’anshan 243002, China |
|
|
Abstract As main by-product of semi-dry desulfurization technology, desulfurization ash is very difficult to be utilized and there is a high -cost for its utilization. It cannot be disposed through direct stacking and landfill, otherwise it will cause environmental pollution and waste of potential resources. Rubber is a kind of widely used polymer material, of which the mechanical properties, machining properties and filling capacity can be improved by using large amounts of fillers during preparation. Carbon black and white carbon black, as the commonly used rubber packing, can only be prepared by complicated process, which always leads to large consumption of energy and resources, resulting in higher costs. Thus, the development of desulfurization ash into low-cost inorganic rubber fillers has become one of the main methods to achieve resource sustainable development and enhance economic performance by high value-added utilization of solid wastes and cost reduction of fillers in rubber industry to a great extent, respectively. The desulfurization ash is organic while rubber is inorganic. Therefore, chemical modification is necessary to be conducted for desulfurization ash to weaken incompatibility of interface(organic/inorganic) between them. Based on the research results obtained in the early stage of this research group, in this paper, modified desulfurization ash was innovatively used to replace part of carbon black to prepare modified desulfurization ash-based eco rubber. Production materials in every stage of preparation process of modified desulfurization ash-based eco rubber were measured by XRD, such as preparation stage of styrene butadiene rubber mixer glue, preparation stage of modified desulfurization ash-based eco rubber mixer glue and preparation stage of modified desulfurization ash-based eco rubber. The preparation process of styrene butadiene rubber mixer glue, preparation process of modified desulfurization ash-based eco rubber mixer glue and preparation process of modified desulfurization ash-based eco rubber were revealed at the microscopic level, respectively, in order to explain the bonding mechanism of styrene butadiene rubber mixer glue and modified desulfurization ash in vulcanization process. Meanwhile, microstructures of styrene butadiene rubber mixer glue and modified desulfurization ash-based eco rubber mixer glue were tested by SEM so as to further support the obtained mechanism. The results showed that after adding modified desulphurizing ash to styrene butadiene rubber, modified desulfurization ash-based eco rubber’ maximum torque Fmax drops dramatically, minimum torque FL remains stable, △F=Fmax-FL is significantly reduced, meanwhile scorch time and optimum cure time are shortened. Vulcanization induction stage is 0~387 s, vulcanization reaction stage is 387~1 586 s and vulcanization flat stage is 1 586~1 800 s. Form the non- crosslinking network structure in vulcanization induction stage, form the basic crosslinking network structure in early of vulcanization reaction stage, improve the crosslinking network structure in later of vulcanization reaction stage and maintain the crosslinking network structure in vulcanization flat stage. It aims to provide some theoretical basis and technical support for high value-added desulphurization ash resource utilization.
|
Received: 2018-12-19
Accepted: 2019-04-24
|
|
|
[1] You C F, Li Y. Environmental Science & Technology, 2013, 47(6): 2754.
[2] Chun T J, Long H M, Di Z X, et al. Process Safety and Environmental Protection, 2017, 105: 297.
[3] Subhan S, Gisèle B, Olivier G, et al. Advanced Materials Research, 2014, 844: 97.
[4] Morel F, Bounor-legare V, Espuche E, et al. European Polymer Journal, 2012, 48(5): 919.
[5] Zhang H, Fang Y. Journal of Alloys and Compounds, 2019, 781: 201.
[6] Matchawet S, Kaesaman A, Bomlai P, et al. Electrical, Dielectric, and Dynamic Mechanical Properties of Conductive Carbon Black/Epoxidized Natural Rubber Composites, 2015, 50(16): 2191.
[7] ZHANG Hao, ZHANG Xin-yu, LIU Xiu-yu(张 浩, 张欣雨, 刘秀玉). The Chinese Journal of Process Engineering(过程工程学报), 2018, 18(4): 834.
[8] ZHANG Hao, GAO Qing, LIU Xiu-yu, et al(张 浩, 高 青, 刘秀玉, 等). The Chinese Journal of Process Engineering(过程工程学报), 2018, 18(5): 1088. |
[1] |
SUN Wei-ji1, LIU Lang1, 2*, HOU Dong-zhuang3, QIU Hua-fu1, 2, TU Bing-bing4, XIN Jie1. Experimental Study on Physicochemical Properties and Hydration Activity of Modified Magnesium Slag[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3877-3884. |
[2] |
ZHU Yu-qi1, 2, ZHANG Xin2, DU Pan-pan2, LIU Shu1, ZHANG Gui-xin1, 2, GUAN Song-lei2*, ZHENG Zhong1*. Infrared Spectroscopy and X-Ray Spectroscopy Combined With
Inductively Coupled Plasma Mass Spectrometry for Quality
Control of Mongolian Medicine Yu Grain Soil[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3163-3169. |
[3] |
LI Yu-tang1, WANG Lin-zhu1, 2*, LI Xiang3, WANG Jun1. Characterization and Comparative Analysis of Non-Metallic Inclusions in Zirconium Deoxidized Steel[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(09): 2916-2921. |
[4] |
GAO Ya1, LIAO Cui-ping1, ALATAN Chaolumen2, CHEN Jian-bo3, TU Ya4*. X-Ray Diffraction and Infrared Spectral Analysis of the Differential Chemical Indicators Between the Raw and Milk-Processed Corals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2494-2499. |
[5] |
SUN Da-wei1, 2, 3, DENG Jun1, 2*, JI Bing-bing4. Study on the Preparation Mechanism of Steel Slag-Based Biomass Activated Carbon by Special Steel Slag-Discard Walnut Shells Based on ICP-MS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(07): 2308-2312. |
[6] |
XU Ming-kun, LIN Jia-xiang, ZHANG Xiao-lin, LI Zhen-yin, WANG Ya-ming, LIU Chun-tai, SHEN Chang-yu, SHAO Chun-guang*. In Situ Detection of Structural Evolution of Isotropic Polypropylene Crystals During Uniaxial Stretching by Two-Dimensional X-Ray Diffraction Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1426-1433. |
[7] |
SHI Zhi-feng1, 2, LIU Jia2, XIAO Juan2, ZHENG Zhi-wen1*. Investigation of Novel Method for Detecting Vanillin Based on X-Ray Diffraction Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1563-1568. |
[8] |
WANG Mei-li1, 2, SHI Guang-hai2*, ZHANG Xiao-hui1, YANG Ze-yu2, 3, XING Ying-mei1. Experimental Study on High-Temperature Phase Transformation of Calcite[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(04): 1205-1211. |
[9] |
SHAO Jin-fa1, LI Rong-wu2, PAN Qiu-li1, CHENG Lin1*. The Study of Non-Destructive Analysis of Tang Sancai Firing Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 781-787. |
[10] |
ZHANG Dian1, WANG Hui1, CHEN Yin-wei2, 3, WANG Ju-lin2, 3*. Identification and Influence of Color Components in Red Lime From the Roof of Yangxin Hall in the Palace Museum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 877-882. |
[11] |
ZHANG Yan1, 2, WANG Hui-le1, LIU Zhong2, ZHAO Hui-fang1, YU Ying-ying1, LI Jing1, TONG Xin1. Spectral Analysis of Liquefaction Residue From Corn Stalk Polyhydric
Alcohols Liquefaction at Ambient Pressure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 911-916. |
[12] |
FAN Qing-jie, SONG Yan, LAI Shi-quan*, YUE Li, ZHU Ya-ming, ZHAO Xue-fei. XRD Structural Analysis of Raw Material Used as Coal-Based Needle Coke in the Coking Process[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(06): 1979-1984. |
[13] |
PAN Qiu-li1, SHAO Jin-fa1, LI Rong-wu2, CHENG Lin1*, WANG Rong1. Non-Destructive Analysis of Red and Green Porcelain in Qing Dynasty[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(03): 732-736. |
[14] |
WANG Yi1, 2, LI Chang-rong1, 2*, ZENG Ze-yun1, 2,XI Zuo-bing1, 2, ZHUANG Chang-ling1, 2. Study on Alumina/Cerium Oxide X-Ray Diffraction and Raman Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1841-1845. |
[15] |
HUANG Wei-bo, CHEN Jia-yun, HUANG Fang, HUANG Li-shan, OUYANG Jian-ming*. Effects of Different Molecular Weight of Gracilaria Lemaneiformis Polysaccharide on Calcium Oxalate Crystal[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(04): 1163-1170. |
|
|
|
|