Stuay of Mineral Admixtures as Fine Aggregate on Hydration Products and Spectral Performance of Mortar |
WU Fu-fei1, 2, DONG Shuang-kuai1*, ZHAO Zhen-hua1, GONG Jing-wei2, SHI Ke-bin2 |
1. School of Materials and Architectural Engineering Guizhou Normal University, Guiyang 550025,China
2. College of Civil and Hydraulic Engineering,Xinjiang Agricultural University,Urumqi 830052,China |
|
|
Abstract Fly ash, lithium slag and steel slag as industrial waste, replace quality cement to prepare cement mortar and concrete, but its utilization is often low, so using these industrial waste in large quantities by using X-ray diffraction (XRD), thermal analyzer, Fourier infrared spectrometer and scanning electron microscope analysis method, we studied the hydration products, spectral performance and microstructure of mortar after mineral admixtures as fine aggregate, and the change laws of mortar strength with the replacement rate (0%, 30%, 50%, 70% and 100%) were analyzed. Test results showed that the hydration products were CSH gel, Ca(OH)2, a small amount of AFt and Four kinds of slurry hydration products mainly for CSH gel, Ca(OH)2, a small amount of AFt and unhydrated particles (Al2O3 and SiO2) for cement paste, cement-lithium slag paste, cement-fly ash paste, cement-steel slag paste, which contain a certain Li2O·Al2O3·SiO2, Ca1.56SiO3.5·xH2O, and RO phase, respectively. Characteristic peak was 3 467, 3 438, 2 923, 2 348, 1 638, 1 429, 1 111, 1 000, 768, 696 and 462 cm-1 for four paste, but its strong peak was different and activity was also different, which was involved in the level of secondary hydration reaction is also different, so the content of Ca(OH)2 in cement-steel slag paste was significantly higher than cement-lithium slag paste and cement-fly ash paste. It played volcanic activity and filling effect when mineral admixtures replaced cement or fine aggregate. The flexural strength and compressive strength of mortar with 100% mineral admixture (lithium slag, fly ash and steel slag) were higher than pure cement mortar, it was about 37.77%/51.88%, 14.71%/11.70%, 14.71%/34.88%, respectively, But the flexural strength and compressive strength reached the maximum when the dosage of mineral admixtures was different. Therefore, mineral admixtures as fine aggregate of mortar were feasible, which can greatly improve the use of industrial waste in the concrete industry, and can achieve the result of energy conservation and emissions reduction.
|
Received: 2017-09-15
Accepted: 2017-12-30
|
|
Corresponding Authors:
DONG Shuang-kuai
E-mail: 849099914@qq.com
|
|
[1] Wang Qiang,Yan Peiyu,Han S. Sci. China Tech. Sci.,2011,54(2):388.
[2] Wu Fufei,Shi Kebin,Dong Shuangkuai. Key Engineering Materials,2014,(599):52.
[3] Li Xiang,Yan Peiyu. Science China-Technological Sciences,2010,53(11):3033.
[4] Lopez-Gayarre F,Lopez Colina C,Serrano-Lopez M A,et al. Construction and Building Materials,2014,53:260.
[5] WU Fu-fei, CHEN Liang-liang, CI Jun, et al(吴福飞,陈亮亮,慈 军,等). Concrete(混凝土), 2015,(12):51.
[6] Gencel O,Ozel C, Koksal F,et al. Journal of Cleaner Production,2012,21(1):62.
[7] Singh M,Siddique R. Construction and Building Materials,2014,50:246.
[8] Turhan B,Osman G,Ilker B T. Construction and Building Materials,2015,93:782.
[9] Topcu I B,Bilir T. Aci. Materials Journal,2010,107(1):48.
[10] Gencel O,Koksal F,Ozel C,et al. Construction and Building Materials,2012,29:633.
[11] Park S B, Lee B C,Kim J H. Cement and Concrete Research,2004,34(12):2181.
[12] Miguel ángel Sanjuán, Cristina Argiz, Jaime C Gálvez, et al. Construction and Building Materials, 2015,96: 55.
[13] Guilherme A Calligaris, Margareth K K D Franco, Laurence P. Construction and Building Materials, 2015,98: 44.
[14] Shi Mengxiao, Wang Qiang, Zhou Zhikai. Construction and Building Materials, 2015,98: 649.
[15] Bensted J,Barnes P. Structure and Performance of Cement. London:Spon Press,1984. 1.
[16] Persson B. Mat Struct,2000,33:352.
[17] WU Fu-fei, DONG Shuang-kuai, GONG Jing-wei, et al (吴福飞, 董双快, 宫经伟, 等). Transactions of the Chinese Society of Agricultural Engineering(农业工程学报), 2016, 32(3): 48. |
[1] |
LI Xiao-dian1, TANG Nian1, ZHANG Man-jun1, SUN Dong-wei1, HE Shu-kai2, WANG Xian-zhong2, 3, ZENG Xiao-zhe2*, WANG Xing-hui2, LIU Xi-ya2. Infrared Spectral Characteristics and Mixing Ratio Detection Method of a New Environmentally Friendly Insulating Gas C5-PFK[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3794-3801. |
[2] |
SUN Wei-ji1, LIU Lang1, 2*, HOU Dong-zhuang3, QIU Hua-fu1, 2, TU Bing-bing4, XIN Jie1. Experimental Study on Physicochemical Properties and Hydration Activity of Modified Magnesium Slag[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3877-3884. |
[3] |
ZHU Yu-qi1, 2, ZHANG Xin2, DU Pan-pan2, LIU Shu1, ZHANG Gui-xin1, 2, GUAN Song-lei2*, ZHENG Zhong1*. Infrared Spectroscopy and X-Ray Spectroscopy Combined With
Inductively Coupled Plasma Mass Spectrometry for Quality
Control of Mongolian Medicine Yu Grain Soil[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3163-3169. |
[4] |
LI Yu-tang1, WANG Lin-zhu1, 2*, LI Xiang3, WANG Jun1. Characterization and Comparative Analysis of Non-Metallic Inclusions in Zirconium Deoxidized Steel[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(09): 2916-2921. |
[5] |
GAO Ya1, LIAO Cui-ping1, ALATAN Chaolumen2, CHEN Jian-bo3, TU Ya4*. X-Ray Diffraction and Infrared Spectral Analysis of the Differential Chemical Indicators Between the Raw and Milk-Processed Corals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2494-2499. |
[6] |
YAN Ming-liang1, ZHANG Chen-long2, ZHAO Lian-xiang3, ZHAO Hua-he4, GAO Xun2*. Spectral Characteristics of Ge Plasma Induced by Femtosecond Pulsed Laser Ablation[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(07): 2095-2098. |
[7] |
YUAN Kai-xin, ZHUO Jin, ZHANG Qing-hua, LI Ya-guo*. Study on the Spectral and Laser Damage Resistance of CO2 Laser Modified Sol-Gel SiO2 Thin Films[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1752-1759. |
[8] |
XU Ming-kun, LIN Jia-xiang, ZHANG Xiao-lin, LI Zhen-yin, WANG Ya-ming, LIU Chun-tai, SHEN Chang-yu, SHAO Chun-guang*. In Situ Detection of Structural Evolution of Isotropic Polypropylene Crystals During Uniaxial Stretching by Two-Dimensional X-Ray Diffraction Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1426-1433. |
[9] |
SHI Zhi-feng1, 2, LIU Jia2, XIAO Juan2, ZHENG Zhi-wen1*. Investigation of Novel Method for Detecting Vanillin Based on X-Ray Diffraction Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1563-1568. |
[10] |
WANG Mei-li1, 2, SHI Guang-hai2*, ZHANG Xiao-hui1, YANG Ze-yu2, 3, XING Ying-mei1. Experimental Study on High-Temperature Phase Transformation of Calcite[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(04): 1205-1211. |
[11] |
SHAO Jin-fa1, LI Rong-wu2, PAN Qiu-li1, CHENG Lin1*. The Study of Non-Destructive Analysis of Tang Sancai Firing Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 781-787. |
[12] |
ZHANG Dian1, WANG Hui1, CHEN Yin-wei2, 3, WANG Ju-lin2, 3*. Identification and Influence of Color Components in Red Lime From the Roof of Yangxin Hall in the Palace Museum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 877-882. |
[13] |
ZHANG Yan1, 2, WANG Hui-le1, LIU Zhong2, ZHAO Hui-fang1, YU Ying-ying1, LI Jing1, TONG Xin1. Spectral Analysis of Liquefaction Residue From Corn Stalk Polyhydric
Alcohols Liquefaction at Ambient Pressure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 911-916. |
[14] |
AN Huan1, YAN Hao-kui2, XIANG Mei1*, Bumaliya Abulimiti1*, ZHENG Jing-yan1. Spectral and Dissociation Characteristics of p-Dibromobenzene Based on External Electric Field[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 405-411. |
[15] |
WANG Jia-kun1, ZHOU Shuang-lin2*. Analysis and Research on the White Bedding Material of the House Ground of Hamin-Mangha Site in Tongliao[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 508-513. |
|
|
|
|