The Relationship between FTIR Spectra of PVA Film and Its Heat Preservation Capability |
CUI Hai-long1, 2, XU Wen-guo1, HE Fu-qing2, WANG Zhao-hui3, JIAO Hong-wen2, LU Shi-xiang1 |
1. Department of Chemistry, School of Science, Beijing Institute of Technology, Beijing 100081, China 2. Beijing Huadunxuehua Plastics Corporation Co. Ltd., Beijing 100160,China 3. Guangdong Huanan Fine Chemical Research Institute,Xinhui 529141, China |
|
|
Abstract Polyvinyl alcohol (PVA), polyethylene (PE) and ethylene-vinyl acetate copolymer (EVA) film was prepared. The optic capability, infrared transmittance and heat preservation capability of the films were studied respectively. The result indicated that the haze degree of the PVA film decreased about 15% and 12% than PE film and EVA film; PVA film transmittance of IR was more or less than other films in the 7~14 μm wavelength range so that the temperature of greenhouse could be increased effectively in daylight. It was just 16.2% about 20% less than EVA film, and 50% less than PE film. The PVA film could be used as agricultural film in greenhouse to promote heat preservation performance greatly.
|
Received: 2011-05-11
Accepted: 2011-08-30
|
|
Corresponding Authors:
CUI Hai-long
E-mail: cuihailong1976@sina.com, zhaohui7512@163.com
|
|
[1] HUANG Rui. The Plastics Engineers Data Book. Beijing: Machinery Industry Press, 2000. [2] KANG Zhi-yong, LIU Wan-chan, XIANG Ai-min(康智勇, 刘万婵, 项爱民). China Plastics(中国塑料), 2006, 20(11): 71. [3] XU Li-fan, YUAN Hui-lin, LI Hong-fei(许立帆, 苑会林, 李洪飞). Plastics(塑料), 2008, 37(2): 83. [4] CHEN Zhi-zhou, MU Jian-lou, WANG Lin(陈志周, 牟建楼, 王 林). Transaction of the CSAE(农业工程学报),2008, 24(7): 247. [5] Zhang Chunhua, Yang Fenglin, Wang Wenjun, et al. Separation and Purification Technology, 2008, 61: 276. [6] Faheem A. Sheikh A, Nasser A M Barakat, et al. Materials Science and Engineering C, 2009, 29: 869. [7] Zhang Lei, Yu Ping, Luo Yunbai. Separation and Purification Technology, 2006, 52: 77. [8] KONG Wei-dong, JIA Chang-jiang(孔卫东, 贾长江). Plastical Technology(塑料科技), 2002, (6): 31. [9] LIU Qing-shan(刘青山). Journal of Guangdong Industry Technical College(广东轻工职业技术学院学报), 2005, 4(3): 5. [10] TIAN Yan(田 岩). China Plastics(中国塑料), 2004, 18(11): 1. [11] CHEN Zu-xin, KANG Jun(陈祖欣, 康 军). China Plastics(中国塑料), 2006, 20(2): 13. [12] KAKUTA Kunihiko(角田邦彦). China Plastics(中国塑料), 2003, 17(1): 1. [13] LI Li, WANG Qi, WANG Ru, et al(李 莉, 王 琪, 王 茹, 等). Polymer Materials Science and Engineering(高分子材料与工程), 2003, 19(1): 112. [14] GB/T 20202—2006, Ethylene-Vinyl Acetate (EVA) Blown Covering Film for Agriculture(农业用乙烯-乙酸乙烯酯共聚物(EVA)吹塑棚膜). Beijing: China Standards Press(北京: 中国标准出版社), 2006. 3.
|
|
|
|