Investigation on Degradation of Polypropylene/Stabilizers Composites Irradiated by Gamma Rays |
ZHOU Li-juan1,2, ZHANG Xiu-qin1, ZHAO Ying1, YANG Ming-shu1, WANG Du-jin1*, XU Duan-fu1 |
1. Beijing National Laboratory for Molecular Sciences, Chinese Academy of Sciences Key Laboratory of Engineering Plastics, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China 2. Graduate University of Chinese Academy of Sciences, Beijing 100049, China |
|
|
Abstract The degradation behavior of polypropylene and polypropylene/stabilizer composites, caused by gamma radiation, was studied in the present work. The stabilizers used were hindered phenol antioxidant and hindered amine light stabilizer. FTIR spectroscopy and DSC analysis were used to determine the structural variation induced by gamma radiation. It can be seen that the evolution of PP and composites PP/stabilizers on gamma irradiation is an increase in absorbance in the hydroxyl and carbonyl absorption regions. Carbonyl index calculated from FTIR spectra was used to characterize the rate of degradation. When the irradiation dose was small (<50 kGy), the degradation of pure polypropylene and polypropylene/stabilizers composites was not obvious; while the irradiation dose increased (≥50 kGy), the carbonyl indexes of all the samples increased obviously, and the degradation degree of polypropylene/stabilizer composites was bigger than pure polypropylene. This result might be partially attributed to the molecular chain scission of hindered phenol and hindered amine under larger irradiation dose. The chain scission of stabilizers forms hydroperoxides and peroxide radicals, catalyzing the degradation of polypropylene. As the irradiation dose was small (<50 kGy), the crystallization temperatures of pure polypropylene and polypropylene/stabilizer composites all showed no remarkable changes; as the irradiation dose exceeded 50 kGy, the crystallization temperatures of pure polypropylene and polypropylene/stabilizer composites all decreased obviously. Correspondingly, the melting peaks of both pure polypropylene and polypropylene/stabilizer composites moved to lower temperature and split into two peaks with increasing the irradiation dose. The decrease of crystallization and melting temperatures might be attributed to the destruction of chemical structure and stereo-regularity of the molecular chain, due to the increasing of carbonyl and hydroxyl groups brought by the oxidation of polypropylene molecular chain. At the same irradiation dose (≥50 kGy), the crystallization and melting temperatures of polypropylene/stabilizer composites were lower than that of pure polypropylene. It indicates that the stabilizers accelerate the degradation of polypropylene. The results were accordant with the IR results.
|
Received: 2009-11-23
Accepted: 2010-02-26
|
|
Corresponding Authors:
ZHOU Li-juan
E-mail: djwang@iccas.ac.cn
|
|
[1] Spadaro G, Valenza A. Polymer Degradation and Stability, 2000, 67: 449. [2] Ikada Y, Nakamura K, Ogata S, et al. Journal of Polymer Science: Part A: Polymer Chemistry, 1999, 37: 159. [3] Perera R, Albano C, Gonzalez J, et al. Polymer Degradation and Stability, 2004, 85: 741. [4] Lu Hong-dian, Hu Yuan, Kong Qing-hong, et al. Polymers for Advanced Technologies, 2005, 16: 688. [5] Magda M I Khalil, Naeem M El-Sawy, Gamil A El-Shobaky. Journal of Applied Polymer Science, 2006, 102: 506. [6] Karger-Kocsis J. Polypropylene: An A-Z Reference, 1999, 706. [7] Utracki L. Polymer Blends Handbook, 2003, 757. [8] O’Donnell J H. Radiation Effects in Polymers, 1991, 402. [9] Lacoste J, Vaillant D, Carlsson D. J. Journal of Polymer Science: Part A: Polymer Chemistry, 1993, 31: 715. [10] Drahomir V, Jan P. Polymer Degradation and Stability, 1990, 27: 227. [11] Pospisil J. Polymer Degradation and Stability, 1991, 34: 85. [12] Decker C, Mayo F. Journal of Polymer Science: Polymer Chemistry, 1973, 11: 2879.
|
[1] |
XU Ming-kun, LIN Jia-xiang, ZHANG Xiao-lin, LI Zhen-yin, WANG Ya-ming, LIU Chun-tai, SHEN Chang-yu, SHAO Chun-guang*. In Situ Detection of Structural Evolution of Isotropic Polypropylene Crystals During Uniaxial Stretching by Two-Dimensional X-Ray Diffraction Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1426-1433. |
[2] |
NIU An-qiu, WU Jing-gui*, ZHAO Xin-yu. Infrared Spectrum Analysis of Degradation Characteristics of PPC Plastic Film Under Different Covering Methods[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 533-540. |
[3] |
SHANG Chao-nan1, XIE Yan-li2, GAO Xiao3, ZHOU Xue-qing2, ZHAO Zhen-dong2, MA Jia-xin1, CUI Peng3, WEI Xiao-xiao3, FENG Yu-hong1, 2*, ZHANG Ming-nan2*. Research on Qualitative and Quantitative Analysis of PE and EVA in Biodegradable Materials by FTIR[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(11): 3380-3386. |
[4] |
LI Peng-hui, JIANG Zheng-wei, LI Jia-quan, REN Jian-peng, WU Wen-juan*. Research Progress in Quantitative Determination of Phenolic Hydroxyl Groups in Lignin[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(09): 2666-2671. |
[5] |
SUN Nan, TAN Hong-lin*, ZHANG Zheng-dong, REN Xiang, ZHOU Yan, LIU Jian-qi, CAI Xiao-ming, CAI Jin-ming. Raman Spectroscopy Analysis and Formation Mechanism of Carbon
Nanotubes Doped Polyacrylonitrile/Copper Cyclized to Graphite
at Room Temperature[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(09): 2983-2988. |
[6] |
YAO Jing-jing1, 2, YAN Yue-er3, ZHANG Ruo-hong1, LUO Chan1, LIU Jun1, BI Ning1*, TANG Yi2*. Spectroscopic Detection and Analysis for Micro Structure of Aged Traditional Handmade Paper[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(05): 1559-1565. |
[7] |
LI Yuan-peng1, 2, ZHANG Liu-qing1, JIANG Wei3, SHI Yu1, GUO Yan-ni1, ZHOU Lei1, 4, ZHOU Yong-qiang1, 4*, ZHANG Yun-lin1, 4. Variability of the Bio-Labile Fraction of Chromophoric Dissolved Organic Matter in Lake Qiandao, a Large Drinking Water Reservoir[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(03): 858-864. |
[8] |
XIA Xue, PAN Yun-xia*, LI Meng-zhu. Photocatalytic Degradation of RhB Dye by Copolymerization Modification g-C3N4-N Under Visible Light[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(02): 517-522. |
[9] |
YUAN Cheng, ZHAI Sheng-cheng*, ZHANG Yi-meng, ZHANG Yao-li. Simple Evaluation of the Degradation State of Archaeological Wood Based on the Infrared Spectroscopy Combined With Thermogravimetry[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2943-2950. |
[10] |
JI Bang1,2, ZHAO Wen-feng3, DUAN Jie-li4, FU Lan-hui1, MA Li-zhe3, YANG Zhou1*. Spectral Characteristics of Ag3PO4/GO on Nickel Foam and Photocatalytic Degradation of Ethylene Under Visible Light[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2743-2750. |
[11] |
GE Hao-ran1, 3, WANG Fang-yuan1, 3, LI Gui-qin2, YE Song1, 3, WANG Jie-jun1, 3 , LI Shu 1, 3, WANG Xin-qiang1, 3*. Theoretical Study on the Molecular Structure and Infrared Spectroscopy of Indometacin in External Electric Field[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(08): 2447-2452. |
[12] |
TENG Yuan-jie, WEI Qi-zhen, LIU Wen-han, LIU Jiang-mei, NIE Yong-hui, LI Pan. Cy3-Labeled Aptamer Combined with Surface-Enhanced Raman Scattering Using for Specific Detection of Trace Acetamiprid[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(08): 2462-2467. |
[13] |
LAO Wan-li, LI Gai-yun*, CHEN Yi, XIANG Qin, WANG Chao, HUANG An-min. Qualitative and Quantitative Analysis of Two Types of Wood Plastic Composites[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2807-2811. |
[14] |
HU Yuan1,2, CHAI Yi-di2, LIU Bo2, WANG Wen-xia2, TANG Jiu-kai2, FU Xin-mei1, WU Jing2*. Properties of Fluorescence Aqueous Fingerprint of Veterinary Antibiotic Wastewater[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(10): 3144-3147. |
[15] |
SONG Yu-dong1, 3, CAO Gang1, 2, 3, XU Shou-qiang1, 2, 3, MA Tian-wu4, CHANG Fu-cheng4, ZHOU Yue-xi1, 3*, HE Xu-wen2, ZHANG Li-ping2. Spectral Analysis for the Identification of Anion Exchange Membrane Pollutants in Butyl-Acrylate Wastewater[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(09): 2832-2837. |
|
|
|
|