Preparation and Luminescence of Eu3+/Yb3+ Codoped ZrO2 Powders |
CHENG Xue-rui,WEI Xian-tao,CHEN Yong-hu*,YIN Min |
Department of Physics, University of Science and Technology of China, Hefei 230026, China |
|
|
Abstract Samples of Eu3+/Yb3+ co-doped ZrO2 powders were prepared by co-precipitation method. The dependence on the sintering temperature and doping concentration of the structure and luminescence was studied. The results confirmed that the sintering temperature has significant influence on the crystalline phases of ZrO2. As the sintering temperature increased the tetragonal phase was transformed into monoclinic phase. After sintered at 1 150 ℃, single monoclinic phase was observed. In contrast, with the increase in the doping concentration of Yb3+, the crystalline phase was also changed, and the monoclinic phase was transformed back to tetragonal phase. With 1% Eu3+ and 10% Yb3+ doping, single tetragonal phase presents. It was observed that the luminescent properties of Eu3+ ions in two structures were different. Experiment results reveal that the luminescence can be affected by both sintering temperature and doping concentration. With single Yb3+ doping, no NIR emission was observed under ultraviolet light excitation (270 nm). However, with Eu3+/Yb3+ codoping, NIR emission around 980 nm from Yb3+ (2F5/2→2F7/2) was observed under the same excitation. Furthermore, it is confirmed that Yb3+ has the same excitation spectrum with Eu3+. This down-conversion result indicates that there is an energy transfer process between Eu3+ and Yb3+. Cooperative energy transfer process and cross-relaxation process were assigned as the possible mechanism for the near-infrared emission of Yb3+.
|
Received: 2009-10-16
Accepted: 2010-01-18
|
|
Corresponding Authors:
CHEN Yong-hu
E-mail: yhuchen@ustc.edu.cn
|
|
[1] Yuan Junlin, Zeng Xiaoyan, Zhao Jingtai, et al. J. Phys. D: Appl. Phys., 2008, 41: 105406. [2] Huang X Y, Zhang Q Y. J. Appl. Phys., 2009, 105: 053521. [3] De la Rosa E, Salas P, Desirena H, et al. Appl. Phys. Lett., 2005, 87: 241912. [4] YANG Zhi-ping, DU Hai-yan, SUN Jia-yue, et al(杨志萍,杜海燕,孙家跃,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析),2009,29(6):1489. [5] Zhou Wenwen, Zhang Weiping, Yin Min. Journal of Rare Earth, 2008, 29(3): 459. [6] Dwivedi Y, Thakur S N, Rai S B. Appl. Phys. B: Lasers and Optics, 2007, 89: 45. [7] Maciel G S, Biswas A, Prasad P N. Opt. Commun., 2000, 178: 65. [8] Diaz-Torres L A, De la Rosa E, Salas P, et al. Journal of Solid State Chemistry, 2008, 181: 75. [9] Liu Huangqing, Wang Lingling, Chen Shuguang, et al, Journal of Alloys and Compounds, 2008, 448: 336. [10] Solís D, López-Luke T, DelaRosa E, et al. Journal of Luminescence, 2009, 129: 449. [11] Patra Amitava. Chemical Physics Letters, 2004, 387: 35. [12] LI Xiu-ming, Lü Shu-chen, LIU Jin-xia(李秀明, 吕树臣, 刘金霞). Chinese Journal of Luminescence(发光学报), 2005, 26(2): 220. [13] Li Ping, Chen I-Wei. Phys. Rev. B, 1993, 48: 1063. [14] Wang Chaonan, Zhang Weiping, Yin Min. Journal of Alloys and Compounds, 2009, 474: 180. [15] Chen Limiao, Liu Younian, Li Yadong. Journal of Alloys and Compounds, 2004, 381: 266. [16] Nato Yamada, Shigeo Shionoya, Takashi Kushida. Journal of the Pysical Society of Japan, 1972, 32: 1577.
|
[1] |
QIN Li-mei, Andy Hsitien Shen*. Photoluminescence Spectral Characteristics of Jet From Fushun, Liaoning Province[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3180-3185. |
[2] |
ZHU Hong-wei1, CHENG You-fa1, CHEN Shu-xiang2*, FAN Chun-li1, LI Ting1, LIU Hai-bin1, ZHAO Xiao-xue1SHAN Guang-qi1, LI Jian-jun1. Spectroscopic Characteristics of a Natural Diamond Suspected of Synthetic Diamond[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1690-1696. |
[3] |
YAN Xue-jun1, ZHOU Yang2, HU Dan-jing1, YU Dan-yan1, YU Si-yi1, YAN Jun1*. Application of UV-VIS Diffuse Reflectance Spectrum, Raman and
Photoluminescence Spectrum Technology in Nondestructive
Testing of Yellow Pearl[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(06): 1703-1710. |
[4] |
LI Zhao, WANG Ya-nan, XU Yi-pu, CAO Jing, WANG Yong-feng, WU Kun-yao, DENG Lu. Synthesis and Photoluminescence of Blue-Emitting Phosphor
YVO4∶Tm3+ for White Light Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(02): 623-628. |
[5] |
LIAO Yi-min1, YAN Yin-zhou1, WANG Qiang2*, YANG Li-xue3, PAN Yong-man1, XING Cheng1, JIANG Yi-jian1, 2. Laser-Induced Growth Device and Optical Properties of ZnO
Microcrystals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(10): 3000-3005. |
[6] |
WANG Tao1, 2, LIU Jian-xun2, GE Xiao-tian2, WANG Rong-xin2, SUN Qian2, NING Ji-qiang2*, ZHENG Chang-cheng3*. Fine Photoluminescence Spectroscopic Characterization of Interfacial Effects on Emission Properties of InGaN/GaN Multiple Quantum Wells in a Blue-Light Laser Diode Structure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(04): 1179-1185. |
[7] |
LI Zhao, WU Kun-yao, WANG Ya-nan, CAO Jing, WANG Yong-feng, LU Yuan-yuan. Synthesis and Luminescence Properties of Yellow-Emitting Phosphor Y2.93Al5O12∶0.07Ce3+ Under Blue Light Excitation[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(02): 381-385. |
[8] |
CHEN Cai-yun-fei, LI Li-ping*. The Application of Photoluminescence Spectra on Identification of Different Types of Pearls[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(01): 20-25. |
[9] |
ZHAO Tong1, WANG Ya-mei1,2, LIU Ling1, LI Yan1,3*. Gemological and Spectral Characteristics of Mexican Red Blue Amber[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(08): 2618-2625. |
[10] |
CHEN Yan-ping1, LUO De-li2*, HUANG Bin1, CHENG Hao1, TANG Xian-chen1, LI Qiang1, LEI Hong-bo1, CHEN Dan-ping3. Photoluminescence and Radioluminescence of Tb3+ Ion-Doped Lithium Aluminosilicate Glasses[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1863-1868. |
[11] |
ZHAN Ying-fei, LIU Chun-guang*, WANG Ming-wei, YANG Jian, ZHU Han-cheng, YAN Duan-ting, XU Chang-shan, LIU Yu-xue. Preparation, Microstructure and Optical Properties of Cr3+ Single-Doped and Eu3+/Cr3+ Co-Doped GdAlO3 Near Infrared Long Persistent Luminescent Nanoparticles[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(01): 80-87. |
[12] |
ZHAO Yuan, LÜ Zhao-yue*, DENG Jian, ZENG Guo-qing. The Emissive Mechanism of C545T Thin Layer at the Exciplex and Non-Exciplex Interfaces[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(12): 3711-3715. |
[13] |
LIN Shun-hui,ZHANG Li-hui, LIU Yong-quan, WANG Xiao-kun, LIN Chun-lei, YU Yun-peng*. Thermal Annealing Effect on Photoluminescence of Y2O3∶Eu3+ Thin Films Prepared by Magnetron Sputtering[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(11): 3336-3340. |
[14] |
YAN Jun1,2, SUN Qing2, YAN Xue-jun1, FANG Shi-bin1, SHENG Jia-wei2, ZHANG Jian2*. The Categories of the UV-Vis Reflectance Spectra of Seawater Cultured Black Pearl and Its Unique PL Spectral Characteristics[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2781-2785. |
[15] |
ZHENG Bao-feng1, YANG Xiao-yun2,3, MIN Chun-gang2,3, CUI Xiao-ying2,3, DONG Kun2,3*. Study on Raman Spectra and Fluorescence Spectra of Dy3Al2(AlO4)3 in Aluminosilicate Substrates[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(03): 809-812. |
|
|
|
|