| Study on Electro-Degradation of New Conjugated Polymer PFO-BT15 Light Emitting Diodes |
| QIN Zhe1,XU Wei2,LIN Hai-bo1,WANG Bin1,SUN Xiu-feng1,XU Xiao-xuan1,YU Gang1,ZHANG Cun-zhou1 |
1.Photonics Center, Nankai University, Tianjin 300071, China
2.Institute of Polymer Optoelectronic Material & Devices(IPOM), South China University of Technology, Guangzhou 510640, China |
|
|
|
|
Abstract In the present paper electroluminescence spectrum and Raman spectrum were used to study electro-degradation of polymer light emitting devices (PLEDs) of PFO-BT15, a new and high-efficiency emitting polymer synthesized by the institute of polymer optoelectronic material & devices(IPOM) in South China University of Technology.The PLEDs with a configuration of ITO glass/PEDOT(120 nm)/PFO-BT15(80 nm)/Ba(4 nm)/Al(200 nm) emitted green light at 550 nm when 5 V dc voltage was applied.Three of those devices were used to study the electro-degradation mechanism of PLEDs.Device A was deposited in vacuum box in dark room to keep sample fresh；Device B was first lighted with current of 1 mA·0.25 cm-2 for 200 minutes, then with current of 5 mA·0.25 cm-2 for 60 minutes, finally with current of 10 mA·0.25 cm-2 for 40 minutes；Device C was lighted with current of 20 mA·0.25 cm-2 until the electroluminescence failure.Our experimental results indicate that the degradation speeds highly depend on the current through the devices.The stressed devices show the decrease in electroluminescence efficiency.However, the luminescence spectrum of the stressed device did not change compared with the fresh device, which suggest that the structure of the luminescent polymer did not change with the electro-stress.Raman spectrum was employed to probe the structure changes of the materials used in the device.We found that the PEDOT Raman peak disappeared and the PFO-BT15 Raman peak still existed in electro-stress device.The results confirmed that it was the breakage of the PEDOT layer instead of degradation of emitting polymer, that led to the final failure of the PLEDs device.This work gives some valuable information for the design and development of highly stable organic light-emitting device.
|
|
Received: 2007-05-28
Accepted: 2007-09-06
|
|
|
|
Corresponding Authors:
QIN Zhe
E-mail: qinzhe@mail.nankai.edu.cn
|
|
[1] Cao Yong, Parker I D, Yu Gang.Advanced Display, 2001,(2)：3.
[2] Do L M，Han E M，Niidome Y.J.Appl.Phys., 1994, 76(9)：5118.
[3] Parker I D, Cao Y.J.Appl.Phys., 1999, 85(4)：2441.
[4] Lim Shuang Fang, Ke Lin, Wang Wei.Appl.Phys.Lett., 2001, 78(15)：2116.
[5] Me Elvain J, Antoniadis H, Hueschen M R.J.Appl.Phys., 1996, 80(10)：6002.
[6] Lin Haibo, Xu Xiaoxuan, Yu Gang.Proceedings of SPIE, 2004, 5632：11.
[7] LIN Hai-bo, XU Xiao-xuan, WU Hong-bin, et al(林海波，徐晓轩，吴宏滨，等).Chinese Journal of Luminescence(发光学报)，2005, 26(4)：469.
[8] Adachi C, Nagai K, Tamoto N.Appl.Phys.Lett., 1995, 66：2679.
[9] Han E M, Do L M, Niidome Y, et al.Chemistry Letters, 1994，(5)：969.
[10] Fujihira M, Do L M, Koike A, et al.Appl.Phys.Lett., 1996, 68(13)：1787.
[11] Burrows P, Bulovic F, Forrest S, et al.Appl.Phys.Lett., 1994, 65(23)：2922.
[12] Slyke S V, Chen C, Tang C.Appl.Phys.Lett., 1996, 69(15)：2160.
[13] TANG Ai-wei, TENG Feng, GAO Yin-hao, et al(唐爱伟, 滕 枫, 高银浩, 等).Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2006，26(12)：2169.
[14] LIN Hai-bo, XU Xiao-xuan，WU Hong-bin, et al(林海波，徐晓轩，吴宏滨, 等).Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2004，24(6)：701.
[15] YU Ge, XU Xiao-xuan, L Shu-hua, et al(于 舸, 徐晓轩, 吕淑华, 等).Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2006，26(5)：869.
[16] Kim Ji-seon, Ho Peter K H, Murphy Craig E, et al.Adv.Mater., 2002, 14：2006. |
| [1] |
Salima Rahmat1, 2, LI Jia-jia1, Arzugul Muslim1, 2*, Kalbinur Matsawut1. Synthesis and Properties of Novel Benzidine-Based Narrow Band Gap Conjugated Polymer From Simple Monomers[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(12): 3751-3756. |
| [2] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
| [3] |
YANG Jian1, 2, ZHAO Su-ling1, 2*, SONG Dan-dan1, 2, XU Zheng1, 2, QIAO Bo1, 2, WANG Peng1, 2, WEI Peng1, 2. Highly Efficient Solution Processed Blue Thermally Activated Delayed Fluorescent Organic Light-Emitting Devices with a Mixed Hole Injection Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1028-1033. |
| [4] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
| [5] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
| [6] |
CHEN Yi-xiang, ZHAO Su-ling*, XU Zheng, ZHANG Cheng-wen, XU Xu-rong. The Establishment and the Application of the Electroluminescence Decay Measurement System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 1993-1996. |
| [7] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
| [8] |
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763. |
| [9] |
YANG Zhao-kun, ZHAO Su-ling*, XU Zheng*, HUANG Qing-yu . The Inside Charge Behavior of Organic Light-Emitting Diodes Investigated with Transient Electroluminescent Measurements[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3134-3137. |
| [10] |
SONG Ling-yun1, CAI Chun-feng1, LIU Bo-zhi1, HU Lian1, ZHANG Bing-po1, WU Jian-zhong2*, BI Gang2, WU Hui-zhen1*. Influence of Parameters of ZnS Film on the Organic/Inorganic Composite Luminescence Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(04): 898-902. |
| [11] |
DAI Shuang, YU Tong-jun*, LI Xing-bin, YUAN Gang-cheng, LU Hui-min . The Electroluminescence Spectra of InGaN/GaN Blue LEDs During Aging Time [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 327-330. |
| [12] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326. |
| [13] |
YANG Yi-fan, ZHAO Su-ling*, GAO Song . Tunneling Electroluminescence of the ZnO Nanorods/MEH-PPV Heterojunction Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2895-2899. |
| [14] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Properties of Phosphorescent Organic Light-Emitting Diodes with Different Doping Order on Light Emitting Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1763-1766. |
| [15] |
MA Zhu1, YU Jun-sheng1*, JIANG Long-feng1, DONG Shou-cheng2, LI Zhen2*, HU Song3 . Spectra Characteristics and Electroluminescence Performance of Novel Fluorene Derivatives with Aggregation Fluorescence Enhancement[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(04): 935-939. |
|
|
|
|