| Study on the Low Temperature Photoluminescence Spectra of Ⅱ-Ⅵ Group Telluride Bulk Crystals |
| XU Ya-dong, LIU Hang, HE Yi-hui, ZHOU Yan, JIE Wan-qi |
| State Key Laboratory for Solidification Processing, Northwestern Polytechnical University, Xi’an 710072, China |
|
|
|
|
Abstract The dominant point defects in Ⅱ-Ⅵ group telluride bulk crystals grown from melt usually varied due to different growth conditions and cooling history, in turn affect the electrical and optical behaviors of corresponding single crystals and devices. Low temperature photoluminescence (PL) spectra acts as a contact-less and non-destructive technique, can be used to evaluate the behaviors of point defects and impurities in the as-grown telluride bulk crystals. With the purpose of comparing the defect structures in un-doped ZnTe and CdTe crystals grownunder Te-rich condition, 8.6 K PL spectra were obtained. The conductivity type and resistivity were investigated by Hall-effect measurements at room temperature (RT). For p-type low resistivity ZnTe crystal, the intensity of free electron to neutral acceptor (e, A0) transition is higher than the donor-acceptorpair (DAP) transition, which predominates in the PL spectra. However, in the contrary, DAP peak dominates the PL emissions for n-type high resistivity CdTe. This difference is mainly attributed to the distinct properties of the grown-in point defects due to different growth velocities and cooling processes. In termsof the un-doped CdZnTe crystal grown under stoichiometry, neutral donor bound exciton (D0, X) emission is predominated in the 9.2 K PL spectra, with the intensity of (e, A0) peak is higher than DAP peak, which then overlaps to each other when the temperature higher then 15 K. In the case of In-doped CdZnTe crystal grown by Te-rich situation, A-center emission is clearly observed, which introduces an energy level approximately of 0.15 eV, with the intensity proportional to the concentration of indium dopant. This defect is seemingly related to the complex of [In+CdV2-Cd]- formed by a shallow donor InCd and Cd vacancy.
|
|
Received: 2014-03-08
Accepted: 2014-06-18
|
|
|
|
Corresponding Authors:
XU Ya-dong
E-mail: xyd220@nwpu.edu.cn
|
|
[1] Carmody M, Mallick S, Margetis J, et al. Appl. Phys. Lett., 2010, 96: 153502.
[2] Fulop J, Palfalvi L, Almasi G, et al. Journal of Optics Express, 2010, 18(12): 12311.
[3] Schlesinger T, Toney J, Yoon H, et al. Materials Science and Engineering: R, 2001, 32: 103.
[4] Babentsov V, Boiko V, Schepelskii A, et al. Journal of Luminescence, 2010, 130: 1425.
[5] Yang G, Bolotnikov E, Cui Y, et al. Applied Physics Letters, 2011，98: 261901.
[6] Xu Y, Jie W, Sellin J, et al. IEEE Transaction on Nuclear Science, 2009, 56: 2808.
[7] YANG Rui, SUN Ye, LIU Chang-you, et al(杨 睿, 孙叶, 刘长友，等). Journal of Synthetic Crystals (人工晶体学报), 2011, 40: 1102.
[8] Schmidt T, Lischka K, Zulehner W. Physical Review B, 1992,45(16): 8989.
[9] Hjelt K, Juvonen M, Tuomi T. et al. Physica Status Solidi(A), 1997, 162: 747.
[10] Garcia A, Remon A, Munoz V, et al. Journal of Crystal Growth, 1998, 191:685.
[11] Varshni Y. Physica, 1967, 34: 1149.
[12] Properties of Wide Bandgap Ⅱ-Ⅵ Semiconductors, edited by B. Rameshwar, Institution of Engineering and Technology, London, 1997.
[13] Shin H, Sun C. Journal of Crystal Growth, 1998, 186: 354.
[14] Wang T, Jie W, Zhang J, et al. Journal of Crystal Growth, 2007, 304: 313.
[15] Fougeres P, Chibani L, Hageali M, et al., Journal of Crystal Growth, 1999, 197: 641.
[16] Zappettini A, Marchini L, Zha M, et al. Cryst. Eng. Comm., 2013, 15: 2227. |
| [1] |
CHEN Yan-ping1, LUO De-li2*, HUANG Bin1, CHENG Hao1, TANG Xian-chen1, LI Qiang1, LEI Hong-bo1, CHEN Dan-ping3. Photoluminescence and Radioluminescence of Tb3+ Ion-Doped Lithium Aluminosilicate Glasses[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(06): 1863-1868. |
| [2] |
WANG Shi-xia, HU Tian-yi, YANG Meng. Study on Preparation of Ag-Doped ZnO Nanomaterials and Phase Transition at High Pressure Using Diamond Anvil Cell and Raman Spectra[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2021, 41(02): 484-488. |
| [3] |
JIAO Dian, XIAO Si-guo*. Luminescence and Long Afterglow Properties of In3+ and Si4+ Co-Doped ZnBi0.02Ga1.98O4∶Cr3+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(12): 3716-3721. |
| [4] |
LIU Cui-mei1, HAN Yu1, JIA Wei1, HUA Zhen-dong1, MIN Shun-geng2*. Rapid Quantitative Analysis of Methamphetamine by Near Infrared Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(09): 2732-2736. |
| [5] |
LIN Lin1, YANG Ju-cai2*, YING Chun1, LI Ji-jun1, ZHAO Er-jun1. Structures, Stablity and Spectroscopic Property of Chromium Doped Silicon Clusters[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(05): 1388-1392. |
| [6] |
WANG Shi-xia, GAO Jin-jin. Study on the Influence of Pb Doping on High Pressure Structural Properties of Tin Dioxide Using Diamond Anvil Cell and Raman Spectra[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(02): 415-419. |
| [7] |
ZHANG Hong1, WANG Le1*, LUO Dong1, ZHENG Zi-shan1, LI Yang-hui1, 2, PAN Gui-ming1. Structural and Luminescence Properties of Eu2+ Doped CaAlSiN3 Silicon Nitride Red Emitting Phosphor[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 59-64. |
| [8] |
SUN Chuan-yao1, LUO Lan1, 2*, WANG Yu1, GUO Rui1, ZHANG Yuan-bo1. Photoluminscence Spectra and Ternary CIE Colour Image of (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu Phosphor Series[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 98-106. |
| [9] |
RU Ping1, YUAN Cui-fang1, QIAO Hai-xia1, HUANG Yong1, 2*, ZHANG Xue-jiao1, DONG Xin-yu1, Lü Zi-wei1, ZHANG Min1, WANG Yi-rao1, DANG Xian-yang1, CHEN Yun-long1, YANG He-jie3, ZHANG Xiao-jun4, ZHANG Xiao-yun1*. Preparation and Characterization of Bionic Mg-Ag-HA/Gelatin Antibacterial Biocoating Based on FTIR and ICP-MS[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(11): 3352-3358. |
| [10] |
YANG Lei, LIN Bin-bin, ZHENG Qi-wei, WU Shu-lan, ZHENG Bing-yun, ZHU Zhi-fei, HU Wen-ying. Its Photochemical Recognition to Hg2+ and Preparation of Nitrogen and Sulfur-Codoped Carbon Dots by Sulfanilamide[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(11): 3388-3394. |
| [11] |
DUAN Liang-fei1, WANG Guang-hua1, 2, QIAN Fu-li1, GAO Si-bo1, DUAN Yu1, 2*, JI Hua-xia1, FAN Heng1. Study on Blue Dopant Ratio on the Performance of TOP-Emitting White OLED Microdisplays[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(08): 2630-2633. |
| [12] |
WU Qi-xiao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, ZHANG Jun-jie1, 2, ZUO Peng-fei1, 2. Synthesis and Upconversion Mechanism of NaYF4∶Yb3+,Er3+ Nanocrystal Doped with Different Concentration of Sensitizer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(05): 1406-1411. |
| [13] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
| [14] |
ZHENG Jia-jin1, 2, LU Qiang1, ZHENG Rui-lin1, ZOU Hui1, YU Ke-han1, WEI Wei1. Preparation and Photoluminescence Properties of Fluorophosphate Glasses with High Efficient White Light Emission[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(01): 39-44. |
| [15] |
ZHANG Guo-fang1, ZHAI Ting-ting1, HOU Zhong-hui1, XU Jian-yi1, WU Yue1, GE Qi-lu2. Research on the Influence of Spectrum Characteristics on the Catalysis Effect of Nanosized CeO2-xNx Solid Solutions[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(10): 3192-3198. |
|
|
|
|