Syntheses and Luminescence Investigation of CaAl12O19:xMn4+ Red Phosphors |
TONG Yi-ping, YAN Jia-yan |
Department of Chemical Engineering, Huizhou University, Huizhou 516007, China |
|
|
Abstract CaAl12O19:xMn4+(x=0.0~0.001 84 mol) red phosphors were prepared by high-temperature solid state method. Different influencing factors, i.e. the doping amount of Mn4+, and sintering temperature, were investigated by the orthogonal experiment design. The optimum conditions for preparing CaAl12O19∶xMn4+ phosphors are: sintering temperature 1 500 ℃, and x=0.014 7 mol. It emits strong deep red light with emission maximal peak at 656 nm, and two shoulder peaks (643 and 666 nm), the corresponding excitation peak is located at 470 nm. The 656 nm emission peak is ascribed to the 2E→4A2 transition, and the shoulder peaks (643 and 666 nm) are attributed to phonon sideband transitions. The 470 nm excitation peak is ascribed to the ligand-field 4A2→4T2 transition (d→d band). Owing to the fact that the excitation peak (470 nm) is near the emission (460 nm) of commercial LED chips, it is quite suitable for red light candidate for LED light resources.
|
Received: 2013-08-29
Accepted: 2013-12-18
|
|
Corresponding Authors:
TONG Yi-ping
E-mail: typ2469@163.com
|
|
[1] Park J, Kim G, Kim Y J. Ceramics International, 2013, 39: S623. [2] Xie R J, Hirosaki N, Mitomo M, et al. Appl. Phys. Lett., 2006, 88: 101104. [3] Chiang C C, Tsai M S, Hon M H. J. Electrochem. Soc., 2007, 154: J326. [4] Kottaisamy M, Thiyagarajan P, Mishra J, et al. Mater. Res. Bull., 2008, 43: 1657. [5] Brika M G, Pan Y X, Liu G K. Journal of Alloys and Compounds, 2011, 509: 1452. [6] Pan Y X, Liu G K. J. Lumin., 2011, 131: 465. [7] Murata T, Tanoue T, Iwasaki M, et al. J. Lumin., 2005, 114: 207. [8] Pan Y X, Liu G K. Opt. Lett., 2008, 33: 1816. [9] Xu Y D, Wang D, Wang L. Journal of Alloys and Compounds, 2013, 550: 226. [10] Yen W M, Shionoya S, Yamamoto H. Phosphor Handbook, The Chemical Rubber Company Press, Boca Raton, Florida, USA, 2006. [11] Zhan K, Liu H Z, Wu Y T, et al. J. Mater. Sci., 2007, 42: 9200. [12] Kemeny G, Haake C H. J. Chem. Phys., 1960, 33: 783. [13] Singh V, Chakradhar R P S, Rao J L, et al. J. Solid State Chem., 2007, 180: 2067. [14] Yamada M, Naitou T, Izuno K, et al. Jpn. J. Appl. Phys., 2003, 42: L20. |
[1] |
SUN Chuan-yao1, LUO Lan1, 2*, WANG Yu1, GUO Rui1, ZHANG Yuan-bo1. Photoluminscence Spectra and Ternary CIE Colour Image of (Mg1-x-yBaxSry)1.95SiO4∶0.05Eu Phosphor Series[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(01): 98-106. |
[2] |
JING Qiu-min1, LIU Sheng-gang1*, LIU Yong-gang2, BI Yan1 . Fluorescent Characteristics of Strontium Tetraborate (SrB4O7) Doped with Divalent Lanthanide Elements [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(01): 130-133. |
[3] |
MA Yuan-yuan, HE Jiu-yang, Aziguli·Reheman, Bahadeer·Rouzi, Aierken·Sidike* . Photoluminescence of Sinthetic Scapolite Na4Ca4Al6Si9O24 Phosphors Activated with Ce3+ and Tb3+ and Energy Transfer from Ce3+ to Tb3+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2015, 35(11): 3241-3246. |
[4] |
XU Guo-tang1, LIANG Pei1*, HUANG Jie1, WANG Le1, DONG Qian-min1, LIU Yang1, HUA You-jie2 . Study on Sr3LiMgV3O12∶Eu3+ Single-Phase Phosphor for White LED [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(04): 945-948. |
[5] |
ZHOU He-feng1, 2, ZHANG Shu-quan1, 2, WANG Hua1, 2*, LI Jie1, 3, WANG Li1, 2, WANG Shu-hao1, 2, LIN Wen-jing1, 2, LIU Hong-li1, 2 . Preparation and Characterization of Upconversion Phosphor Based on AlF3-YbF3∶Er3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(01): 23-26. |
[6] |
LIU Chong1, GUAN Li1,2*, ZHANG Hao1, LI Pan-lai1, GUO Qing-lin1,2, YANG Zhi-ping1,2, FU Guang-sheng1,2 . Study on the Spectral Properties of Ca7(SiO4)2Cl6 Phosphor for White LED [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(04): 1016-1019. |
[7] |
PENG Tie-qiu, WANG Yin-hai*, LI Ya,XIONG Yi. Thermoluminescence Study on Sr2SiO4 Long Afterglow Material Doped with Eu2+[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(12): 3223-3227. |
[8] |
ZHOU Guo-xiong1,ZHAO Wei-ren1*, SONG En-hai1, DOU Xi-hua1, YI Chun-yu2,ZHOU Min-kang2 . Preparation and Luminescence Characteristics of White-Light Emitting Ca9.95-xNa0.75K0.25(PO4)7∶Eu2+0.05, Mn2+x Phosphors [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(08): 2058-2062. |
[9] |
YANG Li-li1,WAN Wen-jiao1,LI Jin-qing1,MENG Jian-xin2* . Near-Infrared Fluorescence and Energy Transfer in Sr2SiO4∶Eu2+,Nd3+ [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2011, 31(01): 43-46. |
[10] |
DONG Hong-jun,CHANG Shu-lan*. Study on Spectral Properties of Ca2B5O9Cl∶Eu Prepared with Hydrothermal Method and Solid Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2007, 27(11): 2167-2170. |
|
|
|
|