Influence of Parameters of ZnS Film on the Organic/Inorganic Composite Luminescence Devices |
SONG Ling-yun1, CAI Chun-feng1, LIU Bo-zhi1, HU Lian1, ZHANG Bing-po1, WU Jian-zhong2*, BI Gang2, WU Hui-zhen1* |
1. Department of Physics, State Key Laboratory of Silicon Materials, Zhejiang University, Hangzhou 310027, China 2. City College, Zhejiang University, Hangzhou 310015, China |
|
|
Abstract In the present paper, to fabricate electroluminescent devices CdSe QDs were used as active materials, TPD (N,N′-biphenyl-N,N′-bis-(3-methylphenyl)-1,1′-biphenyl-4,4′-diamine) was used as a hole transport layer, and ZnS was used as an electron transport layer. The electroluminescent properties of the organic/inorganic composite ITO/TPD/CdSe QDs/ZnS/Ag light emitting devices were studied. Both TPD and CdSe QDs thin films were spin-coated and ZnS thin films were deposited by magnetron sputtering. The surfaces of the devices are smooth. The luminescence (EL) peak of the CdSe QDs is at 580 nm which is assigned to the band-edge exciton emission. Compared to the previous EL device of ITO/ZnS/CdSe QDs/ZnS/Ag, it is seen that the new devices do not display surface state related emission peaks and EL intensity is about 10 folds that of the previous device. The enhancement of luminescence efficiency is attributed to both of the excitation of CdSe QDs by accelerated electron collision and carriers injection into QDs: (1) electrons are accelerated by the ZnS layer and collide with CdSe QDs, which excites electrons in QDs to excited states and allows them to emit photons; (2) the holes injected into QDs recombine with some of electrons excited in the QDs. The authors further studied the influence of thickness variation of ZnS on the luminescent properties. ZnS thin films are of 80, 120, and 160 nm thickness, respectively. It was found that as the thickness of ZnS increases the threshold voltage rises and EL intensity increases, but breakdown voltage decreases. The EL peak position blue shifts when the thickness of ZnS decreases. The explanation of underlying mechanism is given.
|
Received: 2013-06-14
Accepted: 2013-10-10
|
|
Corresponding Authors:
Jian-zhong
E-mail: wujianzhong@zucc.edu.cn; hzwu@zju.edu.cn
|
|
[1] Hu L, Wu H Z, Wan C F, et al. New Journal of Physics, 2012, 14. [2] Sano Y, Nunomura K, Koyama N, et al. IEEE Transactions on Electron Devices, 1986, 33: 1155. [3] Zhang T, Xu Z, Liu R, et al. Chem. Phys. Lett., 2007, 437: 248. [4] Fitting H J. Journal of Vacuum Science & Technology B, 1993, 11: 433. [5] Lou Tenggang, Hu Lian, Wu Dongkai, et al. Journal of Inorganic Materials,2012, 27: 1211. [6] Stolka M, Yanus J F, Pai D M. Journal of Physical Chemistry, 1984, 88: 4707. [7] Bourdakos K N, Dissanayake D, Lutz T, et al. Applied Physics Letters, 2008, 92:. [8] Du L X, Hu L, Zhang B P, et al. Acta Physica Sinica, 2011, 60:. [9] Wu D G, Kordesch M E, Van Patten P G. Chemistry of Materials, 2005, 17: 6436. [10] Zhou Y, Bi X F. Journal of Applied Physics, 2005, 98:. [11] Liu Shanshan, Teng Feng, Xu Zheng, et al. Spectroscopy and Spectral Analysis, 2004, 24(7): 790. [12] Sisodia A S, Dagar H S, Sisodia N. Size Effect on Stark Signal of CdSe Nano Crystals: A Theoretical Approach, in: Mittal R, Chauhan A K, Mukhopadhyay R(Eds.) Solid State Physics, Pts 1 and 22012, 243. [13] Banerjee S, Shore K A. Journal of Applied Physics, 2005, 97: 1. |
[1] |
ZHENG Xu-gang1, 2, SONG Dan-dan1, 2, ZHAO Su-ling1, 2, QIAO Bo1, 2, SHEN Chong-yu3, XU Zheng1, 2*. Effect of Water Vapor Treatment on the Performance of Quantum Dot Light-Emitting Diodes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1034-1039. |
[2] |
YANG Jian1, 2, ZHAO Su-ling1, 2*, SONG Dan-dan1, 2, XU Zheng1, 2, QIAO Bo1, 2, WANG Peng1, 2, WEI Peng1, 2. Highly Efficient Solution Processed Blue Thermally Activated Delayed Fluorescent Organic Light-Emitting Devices with a Mixed Hole Injection Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2020, 40(04): 1028-1033. |
[3] |
LI Zhao, CAO Jing, WANG Yong-feng. Synthesis and Spectral Properties of Phosphors Based on Schiff Base Complexes[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(09): 2879-2882. |
[4] |
WANG Hao1, 2, ZHAO Su-ling1, 2*, XU Zheng1, 2, SONG Dan-dan1, 2, QIAO Bo1, 2, WANG Peng1, 2, ZHENG Wei-ye1, 2, WEI Peng1, 2. The Influence of Deep Trap on the Efficiency Decrease in PhOLEDs Based on Double Dopants Strategy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2019, 39(04): 1018-1024. |
[5] |
CHEN Yi-xiang, ZHAO Su-ling*, XU Zheng, ZHANG Cheng-wen, XU Xu-rong. The Establishment and the Application of the Electroluminescence Decay Measurement System[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(07): 1993-1996. |
[6] |
HONG Xiao-xia1, 2, XU Zheng1, 2*, ZHAO Su-ling1, 2, QIAO Bo1, 2, ZHANG Cheng-wen1, 2, WANG Peng1, 2 . Study on the Overshoot Effect of Doped PhOLED with Transient Electroluminescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(03): 710-714. |
[7] |
WANG Guang-hua1,2, ZHAO Hui-qiong1,2, DENG Rong-bin1, DUAN Yu1,2, SUN Hao1, ZHANG Xiao-dan1,2, ZHOU Qin1, QIAN Jin-mei1, WAN Rui-min1,2, JI Hua-xia1, JI Rong-bin2. Research on the Preparation and Chromaticity Coordinates Shift Mechanism of Organic White Light Top-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(11): 3758-3763. |
[8] |
YANG Zhao-kun, ZHAO Su-ling*, XU Zheng*, HUANG Qing-yu . The Inside Charge Behavior of Organic Light-Emitting Diodes Investigated with Transient Electroluminescent Measurements[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(10): 3134-3137. |
[9] |
DAI Shuang, YU Tong-jun*, LI Xing-bin, YUAN Gang-cheng, LU Hui-min . The Electroluminescence Spectra of InGaN/GaN Blue LEDs During Aging Time [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 327-330. |
[10] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Effect of Spacer on Red and Green Phosphorescent Organic Light-Emitting Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2014, 34(02): 322-326. |
[11] |
YANG Yi-fan, ZHAO Su-ling*, GAO Song . Tunneling Electroluminescence of the ZnO Nanorods/MEH-PPV Heterojunction Devices[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(11): 2895-2899. |
[12] |
HUANG Shan, MA Jian-qiang, XIAO Qi*, DONG Ming-yue, LI Xue-hua, LUO Qiu-ling . Direct Determination of Isocarbophos by Using Oil-Soluble CdSe Quantum Dots as Fluorescence Probe [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(10): 2853-2857. |
[13] |
ZHANG Wei, ZHANG Fang-hui*, HUANG Jin . Properties of Phosphorescent Organic Light-Emitting Diodes with Different Doping Order on Light Emitting Layer[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(07): 1763-1766. |
[14] |
MA Zhu1, YU Jun-sheng1*, JIANG Long-feng1, DONG Shou-cheng2, LI Zhen2*, HU Song3 . Spectra Characteristics and Electroluminescence Performance of Novel Fluorene Derivatives with Aggregation Fluorescence Enhancement[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(04): 935-939. |
[15] |
LIU Sheng-qiang1, YU Jun-sheng1*, ZENG Yan-bo1, ZHAO Juan1, DU Chun-lei2 . Spectral Characteristics of White Organic Light-Emitting Devices Based on Phosphorescent System of Three Iridium Chelates [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2013, 33(03): 636-641. |
|
|
|
|