Study on High-Temperature Phase Change of Tobermorite |
YANG Xiu-li1, CUI Xiao-yu1, CUI Chong1*, MA Hai-long2, YANG Qing1 |
1. School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China 2. Institute of Ethnic Preparatory Education, Ningxia University, Yinchuan 750021, China |
|
|
Abstract In the present paper, the high-temperature phase change of pure tobermorite was investigated by TGA/DSC, X-ray diffraction and infrared spectroscopy (IR) respectively. The DSC results showed that four interlayer water molecules were lost when they were heated at 300 ℃. As the temperature increased to 724 ℃, Si—O—H bonds were cleaved and dehydroxylation occurred. The XRD results showed that many diffraction peaks of tobermorite disappeared and the crystal structure was broken and collapsed. Then tobermorite tends to be disordered and amorphous. When the calcination temperature increased to 861 ℃, the disordered structure recombined to wollastonite, and the crystal structure became ordered and stable. Finally, the structure completely transformed to 2M-wollastonite at 1 000 ℃. It should include the process of high-temperature phase change of tobermorite: tobermorite→dehydration tobermorite→dehydroxylation tobermorite→wollastonite.
|
Received: 2012-12-08
Accepted: 2013-03-22
|
|
Corresponding Authors:
CUI Chong
E-mail: cuichong@njust.edu.cn
|
|
[1] Hirotaka Maedaa, Emile H Ishidab, Toshihiro Kasugac. Materials Letters, 2012, 68(1): 382. [2] Bernstein S, Fehr K T. Progress in Crystal Growth and Characterization of Materials, 2012, 58(2-3): 84. [3] Richardson I G. Cement and Concrete Research, 2008, 38 (2): 137. [4] Francesco Battocchioa, Paulo J M. Cement and Concrete Research, 2012, 42(11): 1534. [5] Kunio Matsui, Jun Kikuma, Masamichi Tsunashima. Cement and Concrete Research, 2011, 41(5): 510. [6] Yunliang Zhaoa, Yimin Zhanga, Tiejun Chenb. Construction and Building Materials, 2012, 2(1): 450. [7] Ali Zaoui. Cement and Concrete Research, 2012, 42(2): 306. [8] Domingos De Sousa Menesesa, Myriam Eckesa, Leire del Campoa. Vibrational Spectroscopy, 2013, 65: 50. [9] Liewa Y M, Kamarudina H, Mustafa A M. Construction and Building Materials, 2012, 30: 794. [10] García Lodeiro, Macphee D E, Palomo A. Cement and Concrete Research, 2009, 39(3): 147. [11] WANG Ding, JIAN Li, CHENG Lin, et al(王 鼎,简 丽,程 琳,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2012, 32(8): 2209.
|
[1] |
WANG Mei-li1, 2, SHI Guang-hai2*, ZHANG Xiao-hui1, YANG Ze-yu2, 3, XING Ying-mei1. Experimental Study on High-Temperature Phase Transformation of Calcite[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(04): 1205-1211. |
[2] |
CHENG Si-meng1,2, JIU Shao-wu1,2, LI Hui1,2*, CHEN Yan-xin1,2, ZHAO Bo1,2. Study on the Oxidation Roasting of High-Sulfur Bauxite by DSC-TG-FTIR Coupling[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(09): 2730-2734. |
[3] |
HOU Shao-gang1, JIA Tai-xuan1*, ZHANG Huan-ping1, LI Hong-liang2, ZHAO Ling1, TIAN Da-yong1, WANG Ti1 . Preparation of TBSI with NS-Acetic Anhydride Method and Its Spectral Analysis[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(09): 2870-2873. |
[4] |
SONG Yong-hui, MA Qiao-na, HE Wen-jin, LAN Xin-zhe . Regularity of Gaseous Product Release During Direct Coal Liquefaction Residue Pyrolysis Process [J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2016, 36(07): 2017-2021. |
[5] |
CHEN Xi1, QIN Ying1*, LI Xiao-li2 . Analysis of the Process of Chinese Purple Pigment Synthesis Using X-Ray Diffraction and Thermal Analysis Methods[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32(04): 1111-1113. |
[6] |
ZHANG Fan, DENG Yu-heng*, ZHU Hui-ju, YANG Yong-li, WANG Shao-ting. Spectroscopy and Thermostability of Series Rare-Earth Complexes with 3-Nitrophthalic Acid[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2009, 29(10): 2773-2776. |
[7] |
FANG Ping, HE Mai, XIE Yun-long, LUO Meng-fei*. XRD and Raman Spectroscopic Comparative Study on Phase Transformation of γ-Al2O3 at High Temperature[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2006, 26(11): 2039-2042. |
|
|
|
|