Texture Variation of CC 5052 Aluminum Alloy Slab from Surface to Center Layer by XRD |
CHEN Ming-biao1, 2*, LIU Wen-chang2, MA Xiao-yi1, LI Jian1, YANG Qing-xiang2, WANG Shan1, MA Min2, LIU Chang2, Zhao Y M3 |
1. College of Mechanical Engineering, Qinghai University, Xining 810016, China 2. Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004, China 3. Division of Internal Medicine, Department of Medicine, Medical University of South Carolina, 171 Ashley Avenue, Charleston, SC 29425, USA |
|
|
Abstract For improvement of the processing and gaining uniformity texture structure and performance of direct chill cast CCAA 5052 aluminum alloy band after first hot rolling with different reduction, the material was annealed at 454 ℃ and then cold rolling with different reduction was conducted, the texture at surface, quarter and center layer of the sample was tested and examined by X-ray diffraction method, the data calculated using special software and the difference of texture at surface, quarter and center layer was analyzed. There existed an elevated gradient of intensity from surface layer to center layer after cold rolled with less than or equal to 40% reduction, The main texture of β is stronger mainly due to transformation from remainder exposure, while the goss and remainder is infirm, the state of texture at each layer is close to each other after cold rolling with reduction high than 56.1%.
|
Received: 2012-10-10
Accepted: 2012-12-26
|
|
Corresponding Authors:
CHEN Ming-biao
E-mail: chenmingbiaozyx@126.com
|
|
[1] Liu W C, Morris J G. Scripta Materialia, 2002: 47743. [2] Zhao Y M, Liu W C, Morris J G. Materials Science and Technology October, 2003,(19): 1379. [3] Zhao Y M, Morris J G. Metallurgical and Materials Transactions A, 2005, 36A: 2505. [4] Liu J, Morris J G. Metallurgical and Materials Transactions A, 2003, 34A: 951. [5] Liu W C, Man C S, Raabe D, et al. Scripta Materialia, 2005, 53: 1273. [6] Liu W C, Radhakrishnan B, Li Z, et al. Materials Science and Engineering A, 2008, 472: 170. [7] Liu J, Morris J G. Materials Science and Engineering A, 2004, 385: 342. [8] Liu W C, Man C S, Raabe D, et al. Cripta Materialia, 2005, 53: 1273. [9] Chen M B, Li J, Zhao Y M, et al. Materials Scharacterization, 2011: 1188. [10] CHEN Ming-biao, LIU Wen-chang, LI Jian, et al(陈明彪,刘文昌,李 戬,等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2012,32(11):3123. [11] MAO Wei-min, YANG Ping, CHEN Leng(毛卫民,杨 平,陈 冷). Principle of Technology of Materials Texture Analysis and Texture Inspect(材料织构分析原理与检测技术). Beijing: Publishing of Metallurgy(北京:冶金出版社),2008. 21. [12] LIU W C, Radhakrishnan B, Li Z. Materials Science and Engineering A, 2008, 472: 170. |
[1] |
SUN Wei-ji1, LIU Lang1, 2*, HOU Dong-zhuang3, QIU Hua-fu1, 2, TU Bing-bing4, XIN Jie1. Experimental Study on Physicochemical Properties and Hydration Activity of Modified Magnesium Slag[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(12): 3877-3884. |
[2] |
LIU Pan1, 2, 3, DU Mi-fang1*, LI Bin1, LI Jing-bin1, ZENG Lei1, LIU Guo-yuan1, ZHANG Xin-yao1, 4, ZHA Xiao-qin1, 4. Determination of Trace Tellurium Content in Aluminium Alloy by
Inductively Coupled Plasma-Atomic Emission Spectrometry Method[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3125-3131. |
[3] |
ZHU Yu-qi1, 2, ZHANG Xin2, DU Pan-pan2, LIU Shu1, ZHANG Gui-xin1, 2, GUAN Song-lei2*, ZHENG Zhong1*. Infrared Spectroscopy and X-Ray Spectroscopy Combined With
Inductively Coupled Plasma Mass Spectrometry for Quality
Control of Mongolian Medicine Yu Grain Soil[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(10): 3163-3169. |
[4] |
LI Yu-tang1, WANG Lin-zhu1, 2*, LI Xiang3, WANG Jun1. Characterization and Comparative Analysis of Non-Metallic Inclusions in Zirconium Deoxidized Steel[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(09): 2916-2921. |
[5] |
ZHANG Zhi-fen1, LIU Zi-min1, QIN Rui1, LI Geng1, WEN Guang-rui1, HE Wei-feng2. Real-Time Detection of Protective Coating Damage During Laser Shock Peening Based on ReliefF Feature Weight Fusion[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2437-2445. |
[6] |
GAO Ya1, LIAO Cui-ping1, ALATAN Chaolumen2, CHEN Jian-bo3, TU Ya4*. X-Ray Diffraction and Infrared Spectral Analysis of the Differential Chemical Indicators Between the Raw and Milk-Processed Corals[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(08): 2494-2499. |
[7] |
XU Ming-kun, LIN Jia-xiang, ZHANG Xiao-lin, LI Zhen-yin, WANG Ya-ming, LIU Chun-tai, SHEN Chang-yu, SHAO Chun-guang*. In Situ Detection of Structural Evolution of Isotropic Polypropylene Crystals During Uniaxial Stretching by Two-Dimensional X-Ray Diffraction Spectroscopy[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1426-1433. |
[8] |
SHI Zhi-feng1, 2, LIU Jia2, XIAO Juan2, ZHENG Zhi-wen1*. Investigation of Novel Method for Detecting Vanillin Based on X-Ray Diffraction Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(05): 1563-1568. |
[9] |
WANG Mei-li1, 2, SHI Guang-hai2*, ZHANG Xiao-hui1, YANG Ze-yu2, 3, XING Ying-mei1. Experimental Study on High-Temperature Phase Transformation of Calcite[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(04): 1205-1211. |
[10] |
SHAO Jin-fa1, LI Rong-wu2, PAN Qiu-li1, CHENG Lin1*. The Study of Non-Destructive Analysis of Tang Sancai Firing Technology[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 781-787. |
[11] |
ZHANG Dian1, WANG Hui1, CHEN Yin-wei2, 3, WANG Ju-lin2, 3*. Identification and Influence of Color Components in Red Lime From the Roof of Yangxin Hall in the Palace Museum[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 877-882. |
[12] |
ZHANG Yan1, 2, WANG Hui-le1, LIU Zhong2, ZHAO Hui-fang1, YU Ying-ying1, LI Jing1, TONG Xin1. Spectral Analysis of Liquefaction Residue From Corn Stalk Polyhydric
Alcohols Liquefaction at Ambient Pressure[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2023, 43(03): 911-916. |
[13] |
FAN Qing-jie, SONG Yan, LAI Shi-quan*, YUE Li, ZHU Ya-ming, ZHAO Xue-fei. XRD Structural Analysis of Raw Material Used as Coal-Based Needle Coke in the Coking Process[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(06): 1979-1984. |
[14] |
HAN Bing1, SUN Dan-dan2*, WAN Wei-hao1, WANG Hui3, DONG Cai-chang2, ZHAO Lei3, WANG Hai-zhou3*. Element Segregation of Cast-Rolled 7B05 Aluminum Alloy Based on
Microbeam X-Ray Fluorescence[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(05): 1413-1419. |
[15] |
PAN Qiu-li1, SHAO Jin-fa1, LI Rong-wu2, CHENG Lin1*, WANG Rong1. Non-Destructive Analysis of Red and Green Porcelain in Qing Dynasty[J]. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2022, 42(03): 732-736. |
|
|
|
|