Abstract：The ash melting temperature of X coal with high ash melting temperature was reduced by adding calcium-magnesium compound flux (WCaO/WMgO=1). In the process of simulated coal gasification, the ash and slag were prepared, and the existence form and evolution process of oxygen, silicon, aluminum, calcium, magnesium at different temperature were analyzed by X-ray photoelectron spectroscopy (XPS). Calcium-magnesium compound flux can reduce ash melting temperature and mainly affect structure change of silicon, aluminum and oxygen. The change of the coordination mode of aluminum and oxygen was shown, namely aluminum-oxide tetrahedrons [AlO4] and aluminum-oxide tetrahedrons [AlO6] varied with temperature changes. The addition of Ca2+ and Mg2+ can destroy the silica chain, making bridging oxygen silicon change into non bridge oxygen silicon; Bridged oxygen bond fracture was broken and non bridging oxygen bond was formed in oxygen element structure. Combined with the Factsage thermodynamic analysis software, the high temperature phase equilibrium composition of coal ash was analyzed after adding calcium-magnesium compound flux, and the fluxing mechanism of flux was studied from the change of mineral structure. The results showed that Ca2+ and Mg2+ were easy to combine with the non bridging oxygen bonds in the silicon-oxide and aluminum-oxide tetrahedrons and aluminum-oxide octahedrons to produce low melting temperature feldspar minerals and magnesia minerals. Therefore the ash melting temperatures were reduced.
Key words：X-ray photoelectron spectroscopy; Coal ash and slag; Compound flux; Transformation of mineral structure; High temperature phase equilibrium
武成利，王蓓蓓，陶 然，方刘伟，李寒旭. 用XPS研究高灰熔融温度煤灰的矿物结构转化[J]. 光谱学与光谱分析, 2018, 38(07): 2296-2301.
WU Cheng-li, WANG Bei-bei, TAO Ran, FANG Liu-wei, LI Han-xu. Study of Mineral Structure Transformation of Coal Ash with High Ash Melting Temperature by XPS. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2018, 38(07): 2296-2301.
[1] LU Xiao-quan(陆小泉). Coal Engineering(煤炭工程), 2016, 48(3): 8.
[2] Chang S, Zhuo J, Meng S, et al. Engineering, 2016, 2(4): 447.
[3] Anne-Gaelle Collot. International Journal of Coal Geology, 2006, 65(3-4): 191.
[4] XU Rong-sheng, WANG Yong-gang, LIN Xiong-chao, et al(徐荣声, 王永刚, 林雄超, 等). Journal of Fuel Chemistry and Technology(燃料化学学报), 2015, (11): 1303.
[5] LI Ji-bing, SHEN Ben-xian, ZHAO Ji-gang, et al(李继炳, 沈本贤, 赵基钢, 等). Journal of China Coal Society(煤炭学报), 2010，(1): 140.
[6] Wu Xiaojiang, Zhang Zhongxiao, Chen Yushuang, et al. Fuel Processing Technology, 2010, 91(11): 1591.
[7] LI Rui-lian, DU Mei-fang, WU Xiao-jiang, et al(李瑞连, 杜梅芳, 乌晓江, 等). Journal of Fuel Chemistry and Technology(燃料化学学报), 2016, 44(5).
[8] Li J, Du M F, Zhang Z X, et al. Energy & Fuels, 2009, 23(2): 704.
[9] LI Mei, YANG Jun-he, ZHANG Qi-feng, et al(李 梅, 杨俊和, 张启锋, 等). Journal of Fuel Chemistry and Technology(燃料化学学报), 2013, 41(11): 1287.
[10] MA Ling-ling, QIN Zhi-hong, ZHANG Lu, et al(马玲玲, 秦志宏, 张 露, 等). Journal of Fuel Chemistry and Technology(燃料化学学报), 2014, 42(3): 277.
[11] ZHANG Lan-jun, LI Zeng-hua, YANG Yong-liang, et al(张兰君, 李增华, 杨永良, 等). Safety in Coal Mines(煤矿安全), 2016, 47(5): 85.