1. Lab of Printing and Packaging Material and Technology, Beijing Area Major Lab, Beijing Institute of Graphic Communication, Beijing 102600, China 2. Research Center of the Ministry of Education for High Gravity Engineering and Technology; Beijing University of Chemical Technology, Beijing 100029, China 3. Nanomaterials Technology Pte. Ltd.，Singapore 049889, Singapore
Abstract：The nano-zinc sulfide was prepared in RPBR (rotating packed bed reactor) using zinc nitrate and hydrogen sulfide as the raw materials. The size and morphology, crystal structure, composition and optical properties of the nano-zinc sulfide were analyzed by transmission electron microscopy(TEM), X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), Fourier transform infrared spectrometry(FTIR), UV-visible spectrophotometer and energy dispersive X-ray detector(EDX). The results show that the nano-zinc sulfide particles are spherical and their average size is about 42 nm. The XRD pattern shows that the nano-zinc sulfide is in a good sphalerite crystal phase. The XPS spectra show that the binding energy of the S (2p) is 162.6 eV，while those of the Zn 2p3/2 and 2p1/2 are 1021.4 and 1 044.6 eV respectively. The IR spectrum shows that the nano-zinc sulfide has good transmittance within the wavelength number range from 400 to 4000 cm-1. The UV-Vis spectrum shows that the nano-zinc sulfide has strong absorption within the wavelength range from 200 to 340nm. The optical gap of the nano-zinc sulfide is 3.57eV by calculation. The EDX spectrum shows that the nano-zinc sulfide has high purity.
Key words：Znic Sulfide;Nanomaterials;Rotating packed bed reactor;Spectra analysis
[1] HUANG Shu-wan(黄书万). Optoelectronics Materials(光电材料). Shanghai: Shanghai Scientific and Technical Publishers(上海: 上海科学技术出版社)，1987. [2] Nanda J, Sapra Sameer, Sarma D D. Chemistry of Materials, 2000, 12(4): 1018. [3] Sun Xiaolin, Hong Guangyan. Chinese Chemical Letters, 2001, 12(2): 187. [4] Wang L P, Hong G Y. Materials Research Bulletin, 2000, 35: 695. [5] GUO Guang-sheng, LIU Ying-rong, WANG Zhi-hua(郭广生，刘颖容，王志华). Chinese Journal of Inorganic Chemistry(无机化学学报), 2000，16(3)：492. [6] Qian Yitai, Su Yi, Chen Qianwang, et al. Materials Research Bulletin, 1995, 30(5): 601. [7] NIE Fu-de, ZENG Gui-yu, YIN Li-sha, et al(聂福德，曾贵玉，尹莉莎，等). Materials Science and Technology(材料科学与工艺)，2002，10(2): 160. [8] Zhang Yining, Narayan Raman, Joseph K. Bailey, et al. The Journal of Physical Chemistry, 1992, 96(23): 9098. [9] Jiang Xuchuan, Xie Yi, Lu Jun, et al. Chemistry of Materials, 2001, 13: 1213. [10] Xu Jianfeng，Ji Wei. Journal of Materials Science Letters, 1999, 18: 115. [11] CHEN Shuang, LIU Wei-min(陈 爽，刘维民). Chemical Journal of Chinese Universities(高等学校化学学报)，2000，21(3)：472. [12] Richard Williams, Yocom P N, Stofko F S. Journal of Collid and Interface Science, 1985, 106: 388. [13] HUANG Xiao-bin, MA Ji-ming, CHENG Hu-min, et al(黄宵滨，马季铭，程虎民，等). Chinese Journal of Applied Chemistry(应用化学)，1997，14(1)：117. [14] LI Ya-ling, WANG Yu-hong, CHEN Jian-feng, et al(李亚玲，王玉红，陈建峰, 等). Journal of Inorganic Materials(无机材料学报)，2003, 18 (6): 1362. [15] Chen Jianfeng, Li Yaling, Wang Yuhong, et al. Materials Research Bulletin, 2004, 39(2): 185. [16] MA Ru-zhang, JIANG Min-hua, XU Zu-xiong(马如璋，蒋民华，徐祖雄). Introduction to Functional Materials(功能材料学概论). Beijing: Metallurgical Industry Press(北京：冶金工业出版社)，1999. [17] Ekimov A I, Onushechenko A A. Journal of Experimental and Theoretical Physics Letters, 1984, 40: 1136. [18] LI Jie, ZHOU He-feng, HAO Yu-ying, et al(李 洁，周禾丰，郝玉英，等). Spectroscopy and Spectral Analysis(光谱学与光谱分析)，2006, 26(2): 235.
