Surface Enhanced Raman Scattering Spectrum Study on Graphene Oxide and Water Soluble Copper Phthalocyanine
CUI Shao-li1, DU Xiao-qing1*, NIU Lian-bin1,2, ZENG Chao1, BAO Jun1, LI Lu1, CHEN Wei-min1
1. Key Laboratory of Optoelectronic Technology and Systems of Education Ministry, Chongqing University, Chongqing 400044, China
2. College of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 400044, China
Abstract:Graphene oxide (GO) was chosen as the Raman enhancement substrate, and the effect of the number of GO layers and probe molecule water soluble copper phthalocyanine (TSCuPc) films thickness on surface enhanced Raman scattering (SERS) was investigated. In our work, spin-coating method was carried out for preparing GO films with different number of GO layers by using different concentrations, and then different TSCuPc films were prepared by adjusting the speed. The results of the experiments showed that: with the increasing of the layer number of GO films, both the polarizability induced by π—π conjugation and local dipole moment induced by oxygen-containing groups increased, resulting in a stronger Raman enhancement presenting a saturated tendency. Meanwhile, the enhancement of characteristic peaks of TSCuPc linearly increased with the increasing of the thickness of TSCuPc films and compared to the influence of GO layer number, the first-layer effect resulting from the thickness of TSCuPc was less pronounced. The TSCuPc molecule prepared by solution method is generally used for hole injection layer of organic optoelectronic devices and there will be of great significance to improve the hole injection efficiency, transmission efficiency and stability of organic optoelectronic devices by researching the surface enhanced Raman spectrum of GO and TSCuPc.
崔少丽,杜晓晴,牛连斌,曾 超,鲍 俊,李 露,陈伟民. 氧化石墨烯与水溶性酞菁铜的表面增强拉曼散射光谱特性研究[J]. 光谱学与光谱分析, 2017, 37(09): 2763-2767.
CUI Shao-li, DU Xiao-qing, NIU Lian-bin, ZENG Chao, BAO Jun, LI Lu, CHEN Wei-min. Surface Enhanced Raman Scattering Spectrum Study on Graphene Oxide and Water Soluble Copper Phthalocyanine. SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(09): 2763-2767.
[1] Jiang Xiaochen, Li Yanqing, Deng Yanhong, et al. Applied Physics Letters, 2013, 103: 073305.
[2] Shi Shengwei, Veera Sadhu, Reda Moubah, et al. The Royal Society of Chemistry, 2013, 1: 1708.
[3] Emmanuel Stratakis, Kyriaki Savva, Dimitrios Konios, et al. Nanoscale, 2014, 6: 6925.
[4] Chao Kong, Zheng Xu, Ling Zhaosu, et al. Chinese Journal of Luminescence, 2012, 33(1): 88.
[5] Ling Xi, Moura L G, Marcos A Pimenta, et al. J. Phys. Chem. C, 2012, 116: 25112.
[6] Yang Huanping, Hu Hailong, Ni Zhenhua, et al. Carbon,2013, 62: 422.
[7] Yu Xinxin, Cai Hongbing, Zhang Wenhua, et al. American Chemical Society, 2011, 5(2): 952.
[8] Liang Weizi, Chen Xiaoyun, Sa Yu, et al. Applied Physics A, 2012, 109: 81.
[9] Xu Weigao, Mao Nannan,Zhang Jin. Small, 2013, 9(8): 1206.
[10] Ling X, Wu J, Xu W, et al. Small, 2012, 8(9): 1365.
[11] Yu Xinxin, Cai Hongbing, Zhang Wenhua, et al. American Chemical Society, 2011, 5(2): 952.