Abstract：At present there are many methods to discuss the crystallinity of lignocellulose but scholars experts have different opinions about them. This study, with bamboo under the different pretreatment conditions, and with help of acid, alkali and glycerol uses X-ray diffraction and CP/MAS13NMR in order to make clear of the crystallinity of bamboo change characteristics, and measured the area length, spacing, crystal plane diffraction peak position, the crystallinity index and parameters and complete the comparison of crystalline cellulose and Gaussian function curve C - 4 area signal area. Results showed that crystalline overall increased significantly after pretreatment, 002 peak become sharp and offset to the direction of large angle for alkali pretreatment, 002 crystal width increases, crystalline spacing is smaller. CP/MAS13NMR is consisting with XRD, but calculated value is smaller. It proved that effective processing can effectively disrupted the recalcitrance of bamboo, and produce highly active cellulose in lignocelluloses’ biomass ethanol production, that provide guidance to realize the lignocellulose bioconversion and effective utilization.
楚 杰，张军华*，马 莉，路海东* . XRD与NMR的热处理竹材结晶性能研究 [J]. 光谱学与光谱分析, 2017, 37(01): 256-261.
CHU Jie, ZHANG Jun-hua*, MA Li, LU Hai-dong* . Study of Crystallinity Performance of Pretreated Bamboo Fibers Based on X-Ray Diffraction and NMR . SPECTROSCOPY AND SPECTRAL ANALYSIS, 2017, 37(01): 256-261.
[1] Xin Donglin，Yang Zhong，Zhang Junhua，et al. Bioresource Technology，2015，175：529. [2] Chundawat Shishir P S, Beckham Gregg T, Himmel Michael E, et al. Annu. Rev. Chem. Biomol. Eng.，2011，2: 121. [3] Liu Yanping, Hu Hong. Fibers and Polymers，2008，9(6):735. [4] Yue Y, Han J, Han G，et al. Carbohydr. Polym.，2015，133(20): 438. [5] Li M F, Fan Y M, Xu F, et al. Ind. Crop. Prod，2010，32 : 551. [6] Wang Yueping, Wang Ge, Cheng Haitao, et al. Textile Research Journal，2010，80(4)：334. [7] Oh S Y, Yoo D I，Shin Y，et al. Carbohydr. Res.，2005，340：2376. [8]Ben Sghaier A E, Chaabouni Y, Msahli S, et al. Ind. Crops Prod.，2012，36: 257. [9]Yang Zhanping，Xu Songwei，Ma Xiaolong，et al. Wood Science and Technology，2008，42(8)：621. [10] LI Jian(李 坚). Wood Spectroscopy(木材波谱学). Beijing: Science Press(北京: 科学出版社)，2003. 104. [11] Segal L，Creely J J, Martin A E, et al. Textile Research Journal，1959，29: 786. [12] Nishimiya Koei，Hata Toshimitsu，Imamura Yuji，et al. Journal of Wood Science，1998，44(1): 56. [13] Tamura N, MacDowell A A，Spolenak B C，et al. J. Synchrotron Rad.，2003，10：137. [14] Siroky J，Blackburn R S，Bechtold T, et al. Cellulose，2010，17: 103. [15] Locci E，Laconi S，Pompei R，et al. Bioresour. Technol.，2008，99：4279. [16] Zuckerstatter G, Schild G, Wollboldt P，et al. Lenzinger Berichte，2009，87：38. [17] Teeaar R, Serimaa R, Paakkari T. Polym. Bull.，1987，17：231.