1.Changchun Institute of Optics,Fine Mechanics and Physics,Chinese Academy of Sciences,Changchun 130033,China 2.Graduate School of the Chinese Academy of Sciences,Beijing 100039,China 3. Department of Physics, Changchun University of Science and Technology, Changchun 130022, China
Abstract:Highly oriented VO2 thin films were deposited on sapphire substrate and [C8H17O]8PcNi thin films were spin-coated onto VO2 thin films. The microstructure of VO2 thin films was studied with XRD. The phase transition was observed and the change in the optical properties of the PcNi/VO2 multilayer-films were investigated with infrared spectrometer. It was found that the mid-infrared transmittance of the complex films in the wavelength range 1.5 to 5.5 mm raised with PcNi coating. The thermochromism of PcNi/VO2 films did not changed compared with VO2 films and the transition temperature was the same as that of VO2. It can be anticipated that the optical limiting property of PcNi/VO2 films will be superior to that of VO2 thin films or PcNi thin films.
[1] Segaud J P, Dillemann B, Giraudo O. Nolinear Opt., 1999, 21: 175. [2] HE Chen-juan, LI De-hua, LU Zhen-zhong, et al(何琛娟, 李德华, 卢振中, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2003, 23(3): 417. [3] Granqvist C G. Thin Solid Films, 1990, 193/194: 730. [4] Rozgonyi G A, Polito W J. J. Electrochem. Soc., 1968, 1: 56. [5] Chain E E. Appl. Opt., 1991, 30: 2782. [6] Fan J C C, Fetterman H R, Bachner F J, et al. Appl. Phys. Lett., 1977, 30: 11. [7] Ballberb I, Trokman S. J. Appl. Phys., 1975, 46: 2111. [8] Razavi A, Hughes T. Antinovitch J, et al. J. Vac. Sci. Technol., 1989, A7: 1310. [9] Griffiths C H, Eastwood H K. J. Appl. Phys., 1974, 45: 2201. [10] Yin Dachuan, Xu Niankan. Materials Research Bulletin, 1996, 31(3): 335. [11] Perry J W, Mansour K, Lee L Y, et al. Science, 1996, 273: 1533.